A kind of high light transmission and weather resistance polycarbonate composite material for LED lampshade processing

A technology of LED lampshade and polycarbonate, which is applied in the field of polycarbonate composite materials with high light transmission and weather resistance for LED lampshade processing, and can solve the problems of reducing the impact resistance of polycarbonate, weakening weather resistance, and reducing light transmission.

Active Publication Date: 2021-04-09
JIANGSU SONGSHANG TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the addition of weather-resistant agents will reduce the impact resistance of polycarbonate, and at the same time reduce the light transmittance
Moreover, organic weather-resistant agents are often used in this field at present. Although this type of weather-resistant agent is added in a small amount, has good blending compatibility with polycarbonate, and has excellent weather resistance in a short period of time, the weather resistance stability is poor, and the weather resistance decreases with time. The extension of time gradually weakens or even disappears, thereby shortening the service life of polycarbonate products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] (1) Activation of molecular sieve raw powder: first place 4A molecular sieve raw powder in an oven at 100-105°C to dry to constant weight, and roast at 550°C for 2 hours to obtain activated molecular sieve raw powder;

[0031] (2) Preparation of carrier: Disperse 50g activated molecular sieve former powder in dehydrated alcohol, then add 8g allyl glycidyl ether, 10g magnesium dimethacrylate and 0.5g initiator azobisisobutyronitrile, then heat Insulate and stir the reaction in the reflux state. After the polymerization reaction, continue to reflux and stir for 30 minutes. The resulting mixture is concentrated under reduced pressure to recover ethanol. The concentrated residue is washed with water to remove unreacted monomers, and dried in an oven at 100-105°C until Weight, the obtained solid is made into fine powder by ultrafine pulverizer, and the carrier is obtained;

[0032] (3) Preparation of weather resistance agent: disperse 50g of the prepared carrier in absolute ...

Embodiment 2

[0035] (1) Activation of molecular sieve raw powder: first place 4A molecular sieve raw powder in an oven at 100-105 ° C to dry to constant weight, and roast at 550 ° C for 2 hours to obtain activated molecular sieve raw powder;

[0036](2) Preparation of carrier: Disperse 50g activated molecular sieve former powder in dehydrated alcohol, then add 8g allyl glycidyl ether, 15g magnesium dimethacrylate and 0.5g initiator azobisisobutyronitrile, then heat Insulate and stir the reaction in the reflux state. After the polymerization reaction, continue to reflux and stir for 30 minutes. The resulting mixture is concentrated under reduced pressure to recover ethanol. The concentrated residue is washed with water to remove unreacted monomers, and dried in an oven at 100-105°C until Weight, the obtained solid is made into fine powder by ultrafine pulverizer, and the carrier is obtained;

[0037] (3) Preparation of weathering agent: Disperse 50g of the prepared carrier in absolute ethan...

Embodiment 3

[0040] (1) Activation of molecular sieve raw powder: first place 4A molecular sieve raw powder in an oven at 100-105 ° C to dry to constant weight, and roast at 550 ° C for 2 hours to obtain activated molecular sieve raw powder;

[0041] (2) Preparation of carrier: Disperse 50g activated molecular sieve former powder in dehydrated alcohol, then add 8g allyl glycidyl ether, 15g magnesium dimethacrylate and 0.5g initiator azobisisobutyronitrile, then heat Insulate and stir the reaction in the reflux state. After the polymerization reaction, continue to reflux and stir for 30 minutes. The resulting mixture is concentrated under reduced pressure to recover ethanol. The concentrated residue is washed with water to remove unreacted monomers, and dried in an oven at 100-105°C until Weight, the obtained solid is made into fine powder by ultrafine pulverizer, and the carrier is obtained;

[0042] (3) Preparation of weathering agent: Disperse 50g of the prepared carrier in absolute etha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polycarbonate composite material with high light transmission and weather resistance for processing LED lampshades, relates to the technical field of polycarbonate composite materials, and is made of the following raw materials in parts by weight: polycarbonate 80‑100 parts, ethylene‑ 5-10 parts of methyl acrylate copolymer, 5-10 parts of polytetrafluoroethylene superfine powder, 1-5 parts of fumed silica, 1-5 parts of white polyaluminum chloride, 0.5-2 parts of weather resistance agent, antioxidant Dose 0.2‑1 part. The polycarbonate composite material prepared by the invention has high light transmittance, strong weather resistance and impact resistance, good processing and molding, the total light transmittance reaches more than 93%, the notched impact strength reaches more than 750J / m, and can withstand long-term use. Sunlight does not cause the LED lampshade to age and become brittle, thereby ensuring the quality of the LED lampshade and prolonging the service life of the LED lampshade.

Description

Technical field: [0001] The invention relates to the technical field of polycarbonate composite materials, in particular to a polycarbonate composite material with high light transmission and weather resistance for processing LED lampshades. Background technique: [0002] Polycarbonate, referred to as PC, is a widely used engineering plastic. It has the characteristics of high transparency, high toughness, high heat resistance, and high strength. It has great advantages in the LED lighting lampshade industry. However, when unmodified polycarbonate is used as a lampshade, its weather resistance is poor, and it is easy to cause the lampshade to age and become brittle under long-term sunlight. [0003] In order to improve the weather resistance of polycarbonate, the most convenient and effective method is to add weather resistance agent. However, the addition of weather-resistant agents will reduce the impact resistance of polycarbonate, and at the same time reduce the light t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L69/00C08L23/08C08L27/18C08L77/04C08K9/04C08K3/36C08K3/16C08K9/12C08K3/22
CPCC08K2003/2296C08K2201/011C08L69/00C08L2201/08C08L2203/20C08L2205/035C08L23/0869C08L27/18C08L77/04C08K9/04C08K3/36C08K3/16C08K9/12C08K3/22
Inventor 汪涛
Owner JIANGSU SONGSHANG TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap