Three-dimensional embossing printing process for flannelette

A printing process, flannelette technology, applied in the field of flannelette embossing printing, can solve the problems of high probability of cloth damage, weakening and disappearing of concave-convex effect, etc., and achieve the effect of small damage probability and unchanged concave-convex effect

Active Publication Date: 2021-04-06
ZHEJIANG MIZUDA TEXTILE PRINTING & DYEING TECH CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Therefore, the existing embossing process has the problems that the concave-convex effect of the finished product is weakened or even disappeared after washing, and the probability of fabric damage is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Example 1. The three-dimensional embossing printing process of flannelette comprises the following steps:

[0025] a. Prepare the semi-bleached fabric of flannelette, and add the padding and stiffening resin into the rolling groove on the primer machine;

[0026] b. Press the semi-bleached flannelette cloth with a steel rod, the pressure of the cloth pressing treatment is 0.4KPa, and the time of the cloth pressing treatment is 5s, and the A product is obtained;

[0027] c, printing the A product mucilage, the mucilage is the PU mucilage of polyurethane, counted by mass parts, including 40 parts of PU glue, 1 part of emulsifying thickener and 6 parts of kerosene, to get B product;

[0028] d. Carry out cloth pressing treatment on product B again, the pressure of cloth pressing treatment is 0.4KPa, the time of cloth pressing treatment is 5s, and C product is obtained;

[0029] e. Bake product C at a temperature of 150°C for 3 minutes to obtain product D;

[0030] f. Wa...

Embodiment 2

[0036] Example 2. The three-dimensional embossing printing process of flannelette comprises the following steps:

[0037] a. Prepare the semi-bleached fabric of flannelette, and add the padding and stiffening resin into the rolling groove on the primer machine;

[0038] b. Press the semi-bleached flannelette cloth with a steel rod, the pressure of the cloth pressing treatment is 0.5KPa, the time of the cloth pressing treatment is 3s, and the A product is obtained;

[0039] c, printing the product A mucilage, the mucilage is the PU mucilage of polyurethanes, counted by mass parts, including 60 parts of PU glue, 5 parts of emulsifying thickener and 12 parts of kerosene, to get B product;

[0040] d. Carry out cloth pressing treatment on product B again, the pressure of cloth pressing treatment is 0.5KPa, the time of cloth pressing treatment is 5s, and C product is obtained;

[0041] e. Bake product C at a temperature of 170°C for 2 minutes to obtain product D;

[0042] f. Was...

Embodiment 3

[0048] Example 3. The three-dimensional embossing printing process of flannelette comprises the following steps:

[0049] a. Prepare the semi-bleached fabric of flannelette, and add the padding and stiffening resin into the rolling groove on the primer machine;

[0050] b. Press the semi-bleached flannelette cloth with a steel rod, the pressure of the cloth pressing treatment is 0.45KPa, and the time of the cloth pressing treatment is 4s, and the A product is obtained;

[0051] c. Printing the A product mucilage, the mucilage is polyurethane PU mucilage, counted by mass parts, including 45 parts of PU glue, 2 parts of emulsifying thickener and 8 parts of kerosene, to obtain B product;

[0052] d. Carry out cloth pressing treatment on product B again, the pressure of cloth pressing treatment is 0.45KPa, the time of cloth pressing treatment is 6s, and C product is obtained;

[0053] e. Bake product C at a temperature of 160°C for 2.5 minutes to obtain product D;

[0054] f. W...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a three-dimensional embossing printing process for velvet cloth, which comprises the following steps: a. preparing a semi-bleached velvet cloth, adding padding and stiffening resin into rolling grooves on a primer; Press cloth to obtain product A; c, print product A with mucilage to obtain product B; d, press product B again to obtain product C; e, bake product C to obtain product D; f, Wash product D in a cylinder to obtain product E; g, finish finishing product E to obtain a finished product. The concave-convex effect of the finished product prepared by the invention remains unchanged after washing, and the probability of cloth damage during the cloth pressing process is reduced; the fabric prepared by the invention is fashionable and novel, and is very popular in the market and wins the favor of consumers.

Description

technical field [0001] The invention relates to the technical field of velvet embossing printing, in particular to a three-dimensional embossing printing process for velvet. Background technique [0002] The existing embossing printing process is usually to engrave a steel stick flower tube die roll, and then emboss on an embossing machine. This process uses a certain amount of external pressure on the fabric pattern to form a three-dimensional effect of unevenness. This embossing printing process has many disadvantages. First, the concave-convex effect of the finished product is weakened or even disappears after washing; second, once the steel mold has slight burrs and snaps, it will be damaged under the extrusion of a large external force. [0003] Therefore, the existing embossing process has the problems that the concave-convex effect of the finished product is weakened or even disappeared after washing, and the probability of cloth damage is high. Contents of the inv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06P1/52
CPCD06P1/5207D06P1/5285
Inventor 李祥波刘昌
Owner ZHEJIANG MIZUDA TEXTILE PRINTING & DYEING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com