Cementing-type well wall reinforcing agent and preparation method thereof

A technology of reinforcing agent and cementing agent, which is applied in the field of cemented well wall reinforcing agent and its preparation

Active Publication Date: 2019-03-05
CHINA PETROLEUM & CHEM CORP +1
View PDF12 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to fundamentally solve the problem of wellbore stability in fractured formations, especially non-water-sensitive hard and brittle formations, the present invention provides a cemented wellbore reinforcement and its preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cementing-type well wall reinforcing agent and preparation method thereof
  • Cementing-type well wall reinforcing agent and preparation method thereof
  • Cementing-type well wall reinforcing agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0077] 1# formula cement and its preparation method:

[0078] Formula: 300 parts of rheology regulator (AGE), 1000 parts of main agent (E44), 500 parts of curing agent (dicyandiamide), and 50 parts of accelerator (thiourea).

[0079] Preparation method: weigh the required parts by weight of each component in proportion. Under stirring (speed 350-500rmp), slowly add the main agent of the cementing agent to the 200 parts of the rheology regulator, and stir until the main agent is completely dissolved to obtain component A; Add curing agent and accelerator to the conditioner, and stir until the curing agent and accelerator are completely dissolved to obtain component B; the above components A and component B are stored separately, and components A and B are mixed evenly to obtain Formulation 1# cement that cures in water.

Embodiment 2

[0081] 2# formula cement and its preparation method:

[0082] Formula: 350 parts of rheology modifier (AGE), 1000 parts of main agent (E44), 300 parts of curing agent (dicyandiamide), 30 parts of accelerator (thiourea).

[0083] Preparation method: weigh the required parts by weight of each component in proportion. Under stirring (speed 350-500rmp), slowly add the main agent of the cementing agent to the 280 parts of the rheology regulator, and stir until the main agent is completely dissolved to obtain component A; Add curing agent and accelerator to the conditioner, and stir until the curing agent and accelerator are completely dissolved to obtain component B; the above components A and component B are stored separately, and components A and B are mixed evenly to obtain 2# formulation cement that cures in water.

Embodiment 3

[0085] 3# Formula cement and its preparation method:

[0086] Formula: rheology regulator (HK-66) 200 parts, main agent (E51) 1000 parts, curing agent (phenol formal hexamethylenediamine) 100 parts, accelerator (2-methylimidazole-salicylate) 10 parts share.

[0087] Preparation method: weigh the required parts by weight of each component in proportion. Under stirring (rotating speed 350-500rmp), slowly add the main agent of the cementing agent to 120 parts of the rheology regulator, and stir until the main agent is completely dissolved to obtain component A; Add curing agent and accelerator to the conditioner, and stir until the curing agent and accelerator are completely dissolved to obtain component B; the above components A and component B are stored separately, and components A and B are mixed evenly to obtain 3# formulation cement that cures in water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
shear viscosityaaaaaaaaaa
thermal resistanceaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a cementing-type well wall reinforcing agent and a preparation method thereof. The well wall reinforcing agent is prepared from the following raw materials in parts by weight:100 parts of water, 7-15 parts of a cementing agent, 15-25 parts of a temperature-resistant polymer adhesive, 2-6 parts of an inorganic bonding effect enhancer, 1.2-3 parts of a low-molecular-weight polymer binding effect enhancer and 0.5-2.4 parts of a solvation enhancer. After treatment is carried out by using the well wall reinforcing agent, broken rocks around a borehole are formed into a whole again. Meanwhile, due to the fact that the well wall reinforcing agent has an extremely strong bonding property, a generated artificial rock body cannot be broken again in a drilling environment; and even if crushing occurs, the broken rocks can be closed again to form a new whole in the working environment, so that the borehole located in a crushing-zone stratum in a drilling process can be kept stable all the time.

Description

technical field [0001] The invention relates to the technical field of drilling, and more particularly relates to a cemented well wall reinforcing agent and a preparation method thereof. Background technique [0002] In drilling engineering, the causes of wellbore instability are complex, in various forms, and difficult to deal with. Due to the inhomogeneity of rock composition and its strong anisotropic characteristics in mechanical properties, regardless of factors such as geological age, type, burial depth, and geological environment, rocks may lose stability and collapse after drilling. possible. In addition to the common wellbore collapse caused by damage to hydration stress and mechanical balance, another type of wellbore collapse that is extremely difficult to deal with in drilling engineering is the natural fracture zone or extremely sensitive hydration stress. weakly cemented strata. Modern drilling fluid technology deals with unstable formations mainly by compre...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K8/508
CPCC09K8/5086
Inventor 蔡利山王建宇宋兆辉林永学褚奇金军斌唐文泉杨枝张凤英杨帆
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap