Novel interlayer bonding adhesive, preparation method and application thereof in papermaking interlayer spraying

A technology of interlayer bonding and interlayer spraying, which is used in textiles and papermaking, papermaking, papermaking and other directions. simple effect

Active Publication Date: 2019-04-26
JINING MING SHENG NEW MATERIALS CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Cardboard paper, recycled kraft cardboard, bobbin paper and other paper types are generally produced by recycling ordinary waste paper or adding a small amount of other pulp, so the improvement of its quality is subject to certain restrictions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel interlayer bonding adhesive, preparation method and application thereof in papermaking interlayer spraying
  • Novel interlayer bonding adhesive, preparation method and application thereof in papermaking interlayer spraying
  • Novel interlayer bonding adhesive, preparation method and application thereof in papermaking interlayer spraying

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] (1) Preparation of new interlayer adhesive:

[0032] (1) 60 parts of papermaking waste containing phenolic substrates, 20 parts of formaldehyde and 10 parts of sodium hydroxide mixed solution were reacted at 70° C. for 300 minutes;

[0033] (2) Then add 10 parts of cationic etherification agent 2,3-epoxypropyl tertiary amine compound, 3-chloro-2-hydroxypropyl tertiary amine compound in (1) reaction product, react for 300 minutes at 70 ℃, After cooling and filtering, a new type of interlayer bonding glue was prepared. The prepared novel interlayer bonding glue has a solid content of 12%, a viscosity of 250 cps, and a pH of 4.05.

[0034] (2) The novel interlayer bonding glue prepared in this example is applied on a machine in a bobbin paper factory in Shandong

[0035] (1) Experimental production conditions:

[0036] Paper machine type: stacked net paper machine;

[0037] Production speed: about 270m / min;

[0038] Papermaking width: 2650mm;

[0039] Production pape...

Embodiment 2

[0050] (1) Preparation of new interlayer adhesive:

[0051] (1) 80 parts of papermaking waste containing phenolic substrates, 5 parts of paraformaldehyde and 5 parts of potassium hydroxide mixed solution were reacted at 80° C. for 200 minutes;

[0052] (2) Then add 10 parts of cationic etherification agent β-haloalkyl tertiary amine compound and 2,3-epoxypropyl tertiary amine compound to the reaction product of (1), react at 80°C for 200 minutes, after cooling and filtering A new type of interlayer adhesive was prepared. The solid content of the novel interlayer bonding glue prepared in this example is 15%, the viscosity is 348 cps, and the pH is 4.18.

[0053] (2) The new type of interlayer bonding glue prepared in this example is applied on a machine in a bobbin paper factory in Zhejiang

[0054] (1) Experimental production conditions:

[0055] Paper machine type: 3200mm multi-cylinder paper machine;

[0056] Paper machine speed: 117m / min;

[0057] Production paper type...

Embodiment 3

[0069] (1) Preparation of new interlayer adhesive

[0070] (1) 100 parts of papermaking waste containing phenolic substrates, 5 parts of paraformaldehyde and sodium hydroxide, and 15 parts of ammonia water mixed solution were reacted at 85°C for 60 minutes;

[0071] (2) Then add 20 parts of cationic etherification agent 2,3-epoxypropyl quaternary ammonium compound, 3-chloro-2-hydroxypropyl quaternary ammonium in (1) reaction product again, 90 ℃ of reaction 120 minutes, through After cooling and filtering, a new type of interlayer bonding glue was prepared. The new interlayer bonding glue prepared in this example has a solid content of 18%, a viscosity of 483 cps, and a pH of 5.63.

[0072] (2) The new type of interlayer bonding glue prepared in this example is applied on the recycled kraft cardboard of a factory in Shandong

[0073] (1) Experimental production conditions:

[0074] Paper machine type: 6600mm stacked net paper machine;

[0075] Paper machine speed: 970m / min;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a novel interlayer bonding adhesive, a preparation method and an application thereof in papermaking interlayer spraying. The preparation method of the novel interlayer bondingadhesive comprises the following steps: (1), a mixed aqueous solution containing phenol papermaking waste, formaldehyde monomers and strong alkaline substances is subjected to reaction at 65-85 DEG Cfor 60-300 minutes; (2), then a cationic etherifying agent is added to the reaction product in the step (1), reaction is performed at 70-90 DEG C for 120-300 minutes, and cooling and filtering are performed, and the novel interlayer bonding adhesive is obtained. The novel interlayer bonding adhesive prepared with the method is applied to the production process of paper types such as bobbin paper,box board paper and regenerated cowhide cards, can partially or completely replace interlayer spraying starch, can effectively improve strength indexes such as interlayer bonding strength, ring compression strength, folding strength and breaking strength of finished paper, has wide raw materials and is affordable; discharge of papermaking waste is effectively reduced, pollution is reduced, and the environment is protected. Therefore, the development prospect is very promising.

Description

technical field [0001] The invention relates to the technical field of papermaking, in particular to a novel interlayer bonding glue and a preparation method thereof and its application in interlayer spraying of container board paper, recycled kraft card and bobbin paper. Background technique [0002] With the continuous improvement of people's living standards, online shopping has become the main way of people's daily shopping; the logistics and packaging industries have also developed rapidly; the market demand for cardboard paper, recycled kraft cards, bobbin paper and other paper is very large; and there is a great demand for packaging Paper quality requirements are getting higher and higher. Cardboard, recycled kraft cardboard, bobbin paper and other paper types are generally produced by recycling ordinary waste paper or adding a small amount of other pulp, so the improvement of its quality is limited to a certain extent. Generally speaking, when the equipment meets th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D21F11/04C08G8/36C09J161/14
CPCC08G8/36C09J161/14D21F11/04
Inventor 施晓旦刘体霞杨迪廖秀驰
Owner JINING MING SHENG NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com