A plastic processing method for fine-grained magnesium alloy tube

A magnesium alloy tube and plastic processing technology, applied in the field of magnesium alloy tube manufacturing, can solve the problems of complex process, poor adaptability of process equipment and high production cost, and achieve the effects of good process flexibility, automatic operation and short processing flow.

Active Publication Date: 2020-10-30
JIANGSU UNIV OF TECH
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the existing problems in the prior art that mainly focus on the manufacture of fine-grained magnesium alloy plates and the complex process, poor adaptability of process equipment and high production costs, the present invention provides a plastic processing method for fine-grained magnesium alloy tubes, which adopts continuous Local plastic forming, at the same time through the rapid heating and rapid cooling of the laser, forms a local deformation zone with temperature gradient and strain gradient on the magnesium alloy tube billet, and promotes the dynamic recrystallization of the magnesium alloy to obtain a fine-grained magnesium alloy tube with uniform structure , to achieve the purpose of improving the strength and toughness of magnesium alloys

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A plastic processing method for fine-grained magnesium alloy tube
  • A plastic processing method for fine-grained magnesium alloy tube
  • A plastic processing method for fine-grained magnesium alloy tube

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0034] This embodiment is a plastic processing method for a ZK60 magnesium alloy pipe with a wall thickness of 1.5 mm and an inner diameter of 100 mm, comprising the following steps:

[0035] Step 1, selecting a bottomed ZK60 magnesium alloy extruded tube blank 31 with a grain size of 6-25 μm, an inner diameter of Φ100 mm, and a wall thickness of 6 mm;

[0036] Step 2, the AZ31 magnesium alloy extruded tube blank 31 is sleeved on the mold 2, and the bottom of the tube wall of the magnesium alloy extruded tube blank 31 is used for positioning, and then fixed on the mold 2 with the fixing device 5, and the mold 2 is fixed on the main shaft 1 on (such as figure 1 shown);

[0037] Step 3, setting the initial processing position of the working head 4, the working head 4 includes two working heads, and the two working heads are symmetrically arranged on both sides of the magnesium alloy extruded tube blank 31 in the circumferential direction, and the laser heating head 7 is adjuste...

example 2

[0047] This embodiment is a plastic processing method for an AZ31 magnesium alloy pipe with a wall thickness of 3 mm and an inner diameter of 100 mm, comprising the following steps:

[0048] Step 1: AZ31 magnesium alloy cast tube billet 32 ​​is selected, with an average grain size of 80 μm, an inner diameter of Φ100 mm, and a wall thickness of 30 mm;

[0049] Step 2, the AZ31 magnesium alloy cast tube blank 32 is sleeved on the mold 2 with an electric heating device inside, and one side of the magnesium alloy cast tube blank 32 is pushed against the chuck 9 for positioning, and the mold 2 is fixed on the spindle 1 (Such as figure 2 shown);

[0050] Step 3, setting the initial processing position of the working head 4, the working head 4 includes three working heads, the three working heads are evenly arranged in the circumferential direction of the magnesium alloy cast tube billet 32 ​​at 120°, and the laser spot B is set The initial irradiation position is to keep the pres...

example 3

[0064] This embodiment is a plastic processing method for an AZ61 magnesium alloy pipe with a wall thickness of 1.5mm and an inner diameter of 100mm, comprising the following steps:

[0065] Step 1: Select the pre-pressed AZ61 magnesium alloy slab, the pre-pressed amount is 6%, the wall thickness of the slab is 3.76mm, the grain size is 10-30μm, and cut it into a magnesium alloy disc with an outer diameter of Φ185mm Blank 33;

[0066] Step 2, 33 sets of magnesium alloy circular slabs are fixed to the bottom of the mold 2, and then fixed on the mold 2 with the fixture 5, and the mold 2 is fixed on the main shaft 1 (such as image 3 shown);

[0067] Step 3, setting the initial processing position of the working head 4, the working head 4 includes a working head, adjusting the laser heating head 7 so that the angle α formed between the output laser beam and the axial direction of the magnesium alloy circular slab 33 is 40°, Set the initial irradiation position of the laser spot...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a plastic processing method for a fine-grained magnesium alloy pipe, which belongs to the field of magnesium alloy pipe material manufacturing. It adopts the continuous local plastic forming process, and conducts local laser heating on the magnesium alloy tube billet during the deformation process; under the joint action of the strain gradient and temperature gradient, it promotes the dynamic recrystallization of the magnesium alloy, and realizes the refinement of the grain of the tube material. The mechanical properties of the pipe are improved. The invention has good process stability, simple process equipment, short process flow and low production cost.

Description

technical field [0001] The invention belongs to the field of manufacturing magnesium alloy pipes, in particular to a plastic processing method for fine-grained magnesium alloy pipes. Background technique [0002] As a structural material, in the case of the same unit volume, the mass of magnesium alloy is the smallest. At the same time, the material has high specific stiffness and specific strength, excellent electromagnetic shielding and damping properties, good thermal conductivity and dimensional stability, and It is known as "the green engineering metal of the 21st century" for its advantages of easy processing, forming and recycling. With the increasing application of magnesium alloys in industries such as transportation and electronic appliances, the research on magnesium alloys has entered a new stage. [0003] Although magnesium resources are very rich, the mechanical properties and deformability of magnesium alloys have become bottlenecks that limit their applicati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21C23/00B21C23/08B21C29/00
Inventor 孙凌燕程亮谢利
Owner JIANGSU UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com