Forming method for composite grating

A composite material and molding method technology, used in household appliances, other household appliances, household components, etc., can solve the problems of high technical difficulty in operation, warping strength and other problems, achieve simple production process, meet fire protection requirements, and be practical and popular. effect of value

Inactive Publication Date: 2019-05-03
HENGSHEN +1
View PDF5 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It solves the problems of high technical difficult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Forming method for composite grating
  • Forming method for composite grating
  • Forming method for composite grating

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0023] In order to make the technical problems, technical solutions and advantages to be solved by the present invention clearer, a detailed description will be given below in conjunction with the accompanying drawings and specific embodiments.

[0024] Such as figure 1 As shown, there are reinforced frames around the grille, and ribs are used in the middle to layer grids of different sizes.

[0025] The molding method of the composite grid includes the following steps:

[0026] Step 1: Mold preparation. Design the mold according to the grid structure. The grid mold includes a core mold, an upper mold and a lower mold, respectively. Figure 4 , image 3 with figure 2 , The core mold is made of aluminum alloy, and the upper and lower molds are made of carbon fiber composite materials.

[0027] Step 2: Lay up, design the blanking map according to the ply and the mold, and use a cutting machine to cut, and pave the cut grid reinforcement frame prepreg on figure 2 On the lower mold show...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a forming method for a composite grating. The forming method comprises the steps that grating reinforcing frame prepreg is laid on a lower mold; a grating rib prepreg is laid on a core mold; the core mold and the lower mold are combined, grating reinforcing frame prepreg continues to be laid on the lower mold, an upper mold and the lower mold are assembled, solidified and formed, and mold release is carried out. OOA closed mold integrated forming is adopted, forming is easy, the manufacturing cost is low, net forming can be achieved, and the product appearance is ensured. The vacuum bag pressing technology and the RTM technology are combined, the mold and equipment input cost is reduced, and the grating manufactured from Tg inflaming retarding prepreg meets fireproof requirements and is applicable to the field of rail traffic.

Description

technical field [0001] The invention belongs to the field of composite materials, and in particular relates to a forming method of a composite material grid, and is especially suitable for places requiring ventilation and heat dissipation in the rail transit field. Background technique [0002] Composite materials have many advantages such as high specific strength, high specific modulus, and strong designability, and are more and more widely used in the field of rail transportation. Grids are mainly used for ventilation and heat dissipation of rail transit equipment. With the requirement of lightweight vehicles, composite material grids have been widely used. At present, the molding methods of composite grids mainly include injection molding and RTM molding. Injection-molded grids are prone to warping and low strength, which cannot meet market requirements for grids. Although the RTM-formed grid can meet the strength requirements, the RTM process has high requirements for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C70/34B29L31/00
Inventor 贾朋军董晴晴石双
Owner HENGSHEN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap