A kind of room temperature superplasticity zinc-based alloy rod/plate and preparation method thereof

A technology of alloy rods and alloy plates, which is applied in the field of materials, can solve the problems of small alloy size range and difficulty in meeting practical application requirements, and achieve the effect of large product size, high surface quality, simple process and equipment

Active Publication Date: 2020-05-26
NORTHEASTERN UNIV LIAONING
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the size range of the alloy prepared by the large plastic deformation process is small, which is difficult to meet the needs of practical applications.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of room temperature superplasticity zinc-based alloy rod/plate and preparation method thereof
  • A kind of room temperature superplasticity zinc-based alloy rod/plate and preparation method thereof
  • A kind of room temperature superplasticity zinc-based alloy rod/plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0059] A zinc-based alloy bar with room temperature superplasticity, including components and mass percentages: 0.1% Cu, 1.5% Fe, 0.1% Mn, the total amount of other impurities is not more than 0.2%, and the balance is Zn; metal zinc , Metal copper, Zn-Fe master alloy, Zn-Mn master alloy as raw materials.

[0060] The preparation method of the zinc-based alloy bar with room temperature superplasticity comprises the following steps:

[0061] First, heat pure Zn in a graphite crucible to 580°C, and after melting, add metal copper, Zn-Fe master alloy, and Zn-Mn master alloy in turn, and stir until they are all melted and mixed evenly to obtain a zinc alloy melt. When the temperature of the melt is reduced to 520°C, use a graphite bell jar to add hexachloroethane to the melt in an amount of 0.5% of the mass of the melt, and then keep it for 15 minutes; During the process, the mold is cooled by water to obtain a cylindrical ingot with a diameter of 60 mm.

[0062] The ingot was ke...

Embodiment 2

[0064] A zinc-based alloy bar with room temperature superplasticity, including components and mass percentages: Cu 4%, Fe 0.05%, Mn 0.2%, the total amount of other impurities is not more than 0.2%, and the balance is Zn; metal zinc , Metal copper, Zn-Fe master alloy, Zn-Mn master alloy as raw materials.

[0065] The preparation method of the zinc-based alloy bar with room temperature superplasticity comprises the following steps:

[0066] First, heat pure Zn in a graphite crucible to 600°C, and after melting, add metal copper, Zn-Fe master alloy, and Zn-Mn master alloy in turn, and stir until they are all melted and mixed evenly to obtain a zinc alloy melt. When the temperature of the melt is reduced to 540°C, add hexachloroethane into the melt using a graphite bell jar in an amount of 0.8% of the mass of the melt, and then keep it for 20 minutes; before casting, the temperature of the melt is reduced to 500°C, During the process, the mold is cooled by water to obtain a cylin...

Embodiment 3

[0069] A zinc-based alloy bar with room temperature superplasticity, including components and mass percentages: Cu 0.5%, Fe2%, Mn0.5%, the total amount of other impurities is not more than 0.2%, and the balance is Zn; metal zinc, metal Copper, Zn-Fe master alloy, and Zn-Mn master alloy are used as raw materials.

[0070] The preparation method of the zinc-based alloy bar with room temperature superplasticity comprises the following steps:

[0071] First, heat pure Zn in a graphite crucible to 620°C. After melting, add metal copper, Zn-Fe master alloy, and Zn-Mn master alloy in turn. After all are melted, stir until they are evenly mixed to obtain a zinc alloy melt. When the temperature of the melt is reduced to 520°C, use a graphite bell jar to add hexachloroethane to the melt in an amount of 0.7% of the mass of the melt, and then keep it for 15 minutes; During the process, the mold is cooled by water to obtain a cylindrical ingot with a diameter of 60 mm.

[0072] The ingot...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile yield strengthaaaaaaaaaa
Login to View More

Abstract

A zinc-based alloy rod / plate with room temperature superplasticity and a preparation method thereof. The components in weight percentage are: Cu: 0.1~4%, Fe: 0.05~2%, Mn: 0.05~0.5%, unavoidable impurities ≤0.2%, the balance is Zn. The preparation method is: according to the proportion, heat and melt the pure metal zinc and then add the metal Cu and the intermediate alloy in sequence. After all the metals are melted, mix them to obtain a zinc alloy melt. After cooling, add hexachloroethane, keep it warm and let it stand, and then cast it after cooling. It is formed into ingots, undergoes two-stage homogenization treatment, heat treatment, and controls relevant parameters to obtain zinc-based alloy rods / plates with room temperature superplasticity. The preparation process of the method of the present invention is simple. By controlling the dynamic recrystallization process of the alloy, and using second phase particles to pinning the grain boundaries to hinder the growth of the grains, the matrix grains are significantly refined, and the zinc-based alloy rods / plates are produced with high performance. Strength, high plasticity and good creep resistance can meet the application needs in different fields.

Description

Technical field: [0001] The invention belongs to the technical field of materials, and in particular relates to a zinc-based alloy bar / plate with room temperature superplasticity and a preparation method thereof. Background technique: [0002] For some pure metals or alloys, when the grain size remains uniform and equiaxed below 10 μm; the deformation temperature is between 0.5 and 0.7 Tm (Tm melting point / K); the strain rate is generally 10 -3 ~10 -5 the s -1 Between the microstructure characteristics and deformation conditions, the material will exhibit high plasticity. If it is measured by tensile elongation at break, it can reach more than 100%, and this plastic deformation characteristic is called superplastic deformation. At the same time, superplastic deformation also has the characteristics of very small deformation resistance and uniform deformation without necking. Many superplastic metal materials have been discovered so far, which can be roughly divided into ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C18/02C22C18/00C22C1/03C22F1/16
Inventor 任玉平李洪晓李松秦高梧
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com