A kind of preparation method of high absorption rate high emissivity coating

A technology with high emissivity and absorptivity, applied in anodizing and other directions, can solve problems such as unfavorable spacecraft application, poor coating adhesion, easy aging and falling off, etc. Effect

Active Publication Date: 2021-03-09
HARBIN INST OF TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem that the coating prepared by the existing magnesium-lithium alloy surface treatment technology has poor bonding force, instability, easy aging and falling off, low absorption rate and low emissivity, which are unfavorable for its application on spacecraft , and provide a method for preparing a coating with high absorptivity and high emissivity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of high absorption rate high emissivity coating
  • A kind of preparation method of high absorption rate high emissivity coating
  • A kind of preparation method of high absorption rate high emissivity coating

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0024] Specific Embodiment One: This embodiment is a method for preparing a high-absorption and high-emissivity coating, which is completed in the following steps:

[0025] 1. Pre-treatment of test pieces:

[0026] ①. Use 240#, 600# and 1000# water-grinding sandpaper in sequence to polish the test piece to obtain a bright surface test piece;

[0027] ②. Use distilled water to wash the bright surface of the test piece for 3 to 5 times, and then use absolute ethanol to wash the bright surface of the test piece for 3 to 5 times to obtain the treated test piece;

[0028] 2. Preparation of thermal control coating:

[0029] Pour the electrolyte solution into the stainless steel electrolytic tank, and then immerse the treated specimen in the electrolyte solution. The treated specimen is connected to the positive pole of the pulse power supply as the anode; the negative pole of the pulse power supply is connected to the stainless steel electrolytic tank as the cathode; turn on Stirr...

specific Embodiment approach 2

[0038] Embodiment 2: The difference between this embodiment and Embodiment 1 is that the test piece described in step 1 is a magnesium-lithium alloy. Other steps are the same as in the first embodiment.

specific Embodiment approach 3

[0039] Specific embodiment three: the difference between this embodiment and specific embodiment one or two is that in step two, the electrolyte is poured into the stainless steel electrolytic cell, and then the treated specimen is immersed in the electrolyte, and the processed The test piece is connected to the positive pole of the pulse power supply as the anode; the negative pole of the pulse power supply is connected to the stainless steel electrolytic cell as the cathode; the stirrer and the cooling water are turned on, and the stirring speed is 30r / min~80r / min, and the current density is 2A / dm 2 ~3A / dm 2 , The power frequency is 300Hz~600Hz, the duty ratio is 20%~30%, and the electrolyte temperature is 10℃~30℃, and the plasma electrolytic oxidation reaction is carried out for 5min~10min, and high absorption rate and high emissivity are obtained on the surface of the test piece. coating. Other steps are the same as those in Embodiment 1 or 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
emissivityaaaaaaaaaa
emissivityaaaaaaaaaa
emissivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a coating with high absorptivity and high emissivity, which relates to a method for preparing a coating. The purpose of the present invention is to solve the problem that the coating prepared by the existing magnesium-lithium alloy surface treatment technology has poor bonding force, instability, easy aging and falling off, low absorption rate and low emissivity, which are unfavorable for its application on spacecraft . Methods: 1. Pretreatment of specimens; 2. Preparation of thermal control coating with high absorption and high emissivity in silicate electrolyte system by micro-arc oxidation. The thermal control coating prepared by the invention has higher absorptivity and emissivity and good thermal control performance. The invention can obtain a coating with high absorptivity and high emissivity.

Description

technical field [0001] The invention relates to a method for preparing a coating. Background technique [0002] When a satellite is in low-Earth orbit, its external thermal environment will change drastically, and the temperature fluctuation range can reach -150-150°C. In order to maintain the normal operation of its carrying equipment, ensure that the structural components and instruments of the spacecraft are in a suitable temperature range in the space environment, and maximize the service life, the spacecraft needs to be equipped with a thermal control system, and thermal control materials are important. way of realization. Magnesium-lithium alloy is the lightest alloy among engineering materials and can be used as an alternative material for lightweight components. It has excellent properties such as high specific strength, good formability, excellent vibration damping performance, and strong resistance to electromagnetic interference. The research and production of m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C25D11/30
Inventor 姚忠平李响孙秋陈昌举夏琦兴李东琦姜兆华
Owner HARBIN INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com