Preparation method of evenly film-formed color liquid crystal light adjusting film

A liquid crystal dimming film and color technology, which is applied in the field of dimming films, can solve the problems of unsatisfactory film formation uniformity and compactness, poor color satisfaction of color liquid crystal dimming films, and high preparation cost, and achieves the solution of film formation. Unsatisfactory uniformity and compactness, improved satisfaction, improved uniformity

Inactive Publication Date: 2019-09-10
TIANJIN BAOXINGWEI TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the ordinary color liquid crystal dimming film has the problems of high preparation cost, unsatisfactory film uniformity and compactness in the preparation process, and the user's satisfaction with the color of the color liquid crystal dimming film is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0016] A method for preparing a uniform film-forming color liquid crystal dimming film, characterized in that the steps are:

[0017] (1) take respectively the monomer cholesteryl pelargonate of 40-60 parts by weight, the vinyl ether of 38-45 parts by weight, the polychloride of 22-28 parts by weight, the polyurethane acrylic acid of 4-6 parts by weight, Add 7-10 parts by weight of color filler and 1-3 parts by weight of photoinitiator into the mixer and mix at 40-50°C for 30-45min. After mixing, add to the mixer and stir at 20-30°C for 15-20min. Mixture 1 is prepared for subsequent use;

[0018] (2) Weighing 10-30 parts by weight of the spacer is added to the mixture 1 obtained in step (1), and the stirrer continues to stir at 40-60°C for 30-45min to obtain a colored liquid crystal mixture;

[0019] (3) Add the colored liquid crystal mixture in the step (2) to the coating pressing machine, and the feeding tank on the coating pressing machine squeezes the colored liquid cryst...

Embodiment 1

[0026] A method for preparing a uniform film-forming color liquid crystal dimming film, the steps of which are:

[0027] (1) take respectively the monomer cholesteryl pelargonate of 40 parts by weight, the vinyl ether of 38 parts by weight, the polypropylene chloride of 22 parts by weight, the polyurethane acrylic acid of 4 parts by weight, the color essence of 7 parts by weight and 1 The photoinitiator 184 in parts by weight was added to the mixer and mixed at 40°C for 45 minutes. After the mixing was completed, it was added to the mixer and stirred at 20°C for 20 minutes to prepare mixture 1 and set aside;

[0028] (2) Weigh 10 parts by weight of spacers of rigid microbeads with a particle size of 6 μm and add them to the mixture 1 obtained in step (1), and continue stirring at 40° C. for 45 minutes to obtain a colored liquid crystal mixture;

[0029] (3) Add the colored liquid crystal mixture in the step (2) to the coating pressing machine, and the feeding tank on the coati...

Embodiment 2

[0032] A method for preparing a uniform film-forming color liquid crystal dimming film, the steps of which are:

[0033] (1) take respectively the monomer cholesteryl pelargonate of 60 parts by weight, the vinyl ether of 45 parts by weight, the polypropylene chloride of 28 parts by weight, the polyurethane acrylic acid of 6 parts by weight, the sulfur dye of 10 parts by weight and 3 parts by weight The photoinitiator 1173 in parts by weight was added to the mixer and mixed for 30 minutes at 50°C. After the mixing was completed, it was added to the mixer and stirred at 30°C for 15 minutes to prepare mixture 1 and set aside;

[0034] (2) Weigh 30 parts by weight of spacers of rigid microbeads with a particle size of 9 μm and add them to the mixture 1 obtained in step (1), and continue stirring at 60° C. for 30 minutes to obtain a colored liquid crystal mixture;

[0035] (3) Add the colored liquid crystal mixture in the step (2) to the coating pressing machine, and the feeding ta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The present invention provides a preparation method of an evenly film-formed color liquid crystal light adjusting film, comprising the steps of preparing a mixture I for standby application; weighing10 to 30 parts by weight of spacers and adding them to the mixture I, thereby obtaining a color liquid crystal mixture; adding the color liquid crystal mixture to a coating lamination machine, by laminating an upper film and a lower film tightly through a laminating roller and pulling the films out through a pull roll, thereby obtaining a laminated film; and performing staged curing, thereby making the color liquid crystal light adjusting film via UV curing. The preparation process of the present invention is simple and reasonable. As compared with the prior art, by adjusting a laminating space and staged curing, the preparation method solves the problem of not ideal film-forming evenness and compactness of the color liquid crystal light adjusting film in the preparation process. By addingcolor fillers and spacers, the preparation method improves evenness of color distribution of the light adjusting film, thus further enhancing satisfaction with color of the color liquid crystal lightadjusting film.

Description

technical field [0001] The invention relates to the technical field of dimming films, in particular to a method for preparing a uniformly formed color liquid crystal dimming film. Background technique [0002] Liquid crystal dimming film is a new type of electronic light control product, which injects a liquid crystal / polymer hybrid material between two transparent conductive films. In the absence of an electric field, the liquid crystal dimming film is in an opaque state; At this time, the liquid crystal molecules are arranged in an orderly manner. At this time, the dimming film is converted from the opaque state, that is, the OFF state, to the transparent state, that is, the ON state. Quick conversion. Liquid crystal dimming film has broad application prospects in many aspects such as commerce, retail, medical and health, government agencies, and security. However, the ordinary color liquid crystal dimming film has the problems of high preparation cost, unsatisfactory fi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G02F1/137C09K19/54
CPCC09K19/542G02F1/13718
Inventor 潘中海司荣美
Owner TIANJIN BAOXINGWEI TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com