A kind of ultrafine nano liquid dispersion color paste and preparation method thereof
A liquid dispersion, ultra-fine nanotechnology, applied in the field of disperse dye research, can solve the problems of high COD, short storage time, uneven distribution of dyeing residual liquid, etc., and achieve the goal of improving the stability of the color paste, excellent effect and improving stability Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0032] Embodiment 1 of the present invention discloses a kind of ultra-fine nano liquid dispersion color paste, and the adopted technical scheme is as follows:
[0033] S1: Weigh 40g of CI.B-79 disperse blue and dissolve it in 100mL of carbon tetrachloride solvent to obtain a disperse dye solution;
[0034] S2: Then weigh 5g of polyacrylate hyperdispersant and 1g of silanol nonionic wetting agent and dissolve them in 100mL of water, add grinding beads and stir and mix at a low speed of 100r / min for 10min to obtain a dispersed grinding system;
[0035] S3: Slowly add the prepared dye solution into the disperse grinding system, grind and stir, after the disperse dye solution is added, gradually increase the stirring speed to 1000r / min, and at the same time heat up to 80°C, condense and reflux to recover the organic solvent, and keep Stir and grind for 5 hours, peel off and recover the complete organic solvent to obtain a mixed dispersion system of disperse dye, dispersant, wetti...
Embodiment 2
[0040] Embodiment 2 of the present invention discloses a kind of ultra-fine nano liquid dispersion color paste, and the adopted technical scheme is as follows:
[0041] S1: Weigh 30g CI.R-54 disperse red and dissolve it in 100mL trichlorethylene solvent to obtain a disperse dye solution;
[0042] S2: Then weigh 4g of styrene-maleic anhydride polymer and 0.5g of alkylphenol polyoxyethylene ether and dissolve it in 100mL of water, add grinding beads and stir and mix at a low speed of 100r / min for 10min to obtain a dispersed grinding system;
[0043] S3: Slowly add the prepared dye solution into the disperse grinding system, grind and stir, after the disperse dye solution is added, gradually increase the stirring speed to 2000r / min, at the same time raise the temperature to 90°C, condense and reflux to recover the organic solvent, and keep Stir and grind for 3 hours, peel off and recover the complete organic solvent to obtain a mixed dispersion system of disperse dye, dispersant,...
Embodiment 3
[0048] Embodiment 3 of the present invention discloses a kind of ultra-fine nano liquid dispersion color paste, the adopted technical scheme is as follows:
[0049] S1: Weigh 50g CI.V-93 Disperse Violet and dissolve it in 100mL trichloroethane solvent to obtain a disperse dye solution;
[0050] S2: Then weigh 8g of styrene-maleic anhydride polymer and 5g of fatty alcohol polyoxyethylene ether and dissolve it in 200mL of water, add grinding beads and stir and mix at a low speed of 200r / min for 10min to obtain a dispersed grinding system;
[0051] S3: Slowly add the prepared dye solution into the disperse grinding system, grind and stir, after the disperse dye solution is added, gradually increase the stirring speed to 800r / min, and at the same time heat up to 80°C, condense and reflux to recover the organic solvent, and keep Stir and grind for 3 hours, strip off and recover the complete organic solvent to obtain a mixed dispersion system of disperse dye, dispersant, wetting age...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com