Annealing technology for 8006-alloy double zero aluminum foil

A technology of double-zero aluminum foil and annealing process, applied in the field of double-zero aluminum foil annealing, can solve the problems that cannot be flattened, affect the surface quality of composite materials and user experience, and achieve the goal of reducing scrap, reducing the depth of hot drums, and reducing production costs. Effect

Inactive Publication Date: 2019-10-29
安徽中基电池箔科技有限公司
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the deficiencies of the prior art, the present invention provides an annealing process for 8006 alloy double-zero aluminum foil, which has the advantages of reducing the number and depth of hot drum rolls, reducing the amount of scrap generated by hot drums, and reducing production costs. It solves the problem that the aluminum foil currently used in the market cannot be flattened due to the double-zero aluminum foil roll formed by the hot drum during the user's compound use, and there are still traces of the hot drum after compounding, which affects the surface quality of the composite material and the user's experience.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Annealing technology for 8006-alloy double zero aluminum foil
  • Annealing technology for 8006-alloy double zero aluminum foil
  • Annealing technology for 8006-alloy double zero aluminum foil

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] The invention discloses an annealing process of an 8006 alloy double-zero aluminum foil. Those skilled in the art can refer to the content of this article and appropriately improve the process parameters to realize it. It should be pointed out that all similar replacements and modifications are obvious to those skilled in the art, and they are all considered to be included in the present invention. The annealing process of the present invention has been described through preferred embodiments, and relevant personnel can obviously make changes or appropriate changes and combinations to the annealing process described herein without departing from the content, spirit and scope of the present invention to realize and apply the present invention Invent technology. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention. B...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of double zero aluminum foil annealing and discloses an annealing technology for 8006-alloy double zero aluminum foil. The annealing technology for the 8006-alloy double zero aluminum foil comprises the following specific steps that firstly, outside-furnace standing is conducted; secondly, inside-furnace pretreatment is conducted; thirdly, uniform annealing is conducted; fourthly, intermediate temperature annealing is conducted; fifthly, low temperature annealing is conducted; sixthly, inside-furnace cooling is conducted; and seventhly, the aluminumfoil is discharged from the furnace. By means of the annealing technology for the 8006-alloy double zero aluminum foil, the number of hot-bulged rolls and the hot bulging depth can be lowered; the scrapping amount generated by hot bulging is lowered; and the production cost is lowered.

Description

technical field [0001] The invention relates to the technical field of double-zero aluminum foil annealing, in particular to an annealing process of 8006 alloy double-zero aluminum foil. Background technique [0002] At present, domestic production of 8006 alloy double-zero foil products is less, and foreign demand is gradually increasing. Using 8006 alloy to produce double-zero foil has very good advantages, specifically: 1) 8006 alloy contains Mn element, which is especially beneficial to the corrosion resistance of aluminum foil performance. 2) According to the test results of air-conditioning aluminum foil and thinned beer label aluminum foil, 8006 alloy has better mechanical properties than 8011, 8079, and 1235 alloys. 3) The research results show that 8006 alloy has good surface quality and extremely low number of pinholes. 4) The rolling process performance of 8006 alloy is good, and it is not easy to produce edge cracking defects. [0003] At present, more and mor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22F1/04C21D9/00C21D1/26
CPCC21D1/26C21D9/0068C22F1/04Y02P10/20
Inventor 马文宏赵世云崔志刚刘学武陈克飞孟祥武梁辰尹并贤孙辉赵曼丽
Owner 安徽中基电池箔科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products