A fiber modification, board technology, applied in the direction of fiber chemical characteristics, monocomponent polyester rayon, textiles and papermaking, etc., can solve problems such as low surface, scratch marks, etc.

Active Publication Date: 2021-10-22
GUIZHOU SENSUYU WOOD PLASTIC CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] As one of the widely used materials in construction, furniture and other fields, plastic sheet is not only low in cost but also convenient in production and molding, which makes it favored by merchants and consumers. With the increasing diversity of consumer demand, the performance of the sheet The requirements are becoming more and more stringent and targeted. Therefore, some plastic sheets currently on the market increase their toughness by adding toughening agents, and increase their weather resistance by adding light shielding agents. However, in terms of wear resistance It has always been a shortcoming of plastic boards. Since plastics are mostly resin components, the hardness of the surface is low. When it comes into contact with metal or stone and other materials, it is easy to have obvious scratch marks.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of fiber modified board and its application
  • A kind of fiber modified board and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] A kind of preparation method of fiber modified plate, it comprises the steps:

[0029] (1) Dry the polyester chips at 170°C for 4 hours. During the drying process, inert gas is continuously introduced, so that the polyester chips are dried in an inert gas atmosphere. The moisture content of the dried polyester chips is low at 300ppm;

[0030] (2) According to chemical composition (Pt 24 Al 34 Fe 37 P 24 ) Put Pt, Al, Fe and P raw materials into a vacuum melting furnace, melt at a temperature of 1000°C, fill in argon during the melting process and melt under an argon atmosphere, wherein the components are melted and mixed After that, keep the constant temperature for 1.5 hours, then cool it down to below 400°C with the furnace, then raise the temperature to 1000°C to continue the smelting process, repeat 3 times, cool the smelted product to room temperature with the furnace, and then grind it into a particle size less than 0.1 mm to obtain alloy powder, wherein the ...

Embodiment 2

[0035] A kind of preparation method of fiber modified plate, it comprises the steps:

[0036] (1) Dry the polyester chips at 160°C for 4.5 hours. During the drying process, inert gas is continuously introduced to dry the polyester chips in an inert gas atmosphere. The moisture content of the dried polyester chips is less than 300ppm;

[0037] (2) According to chemical composition (Pt 23 Al 37 Fe 42 P 26 ) Put Pt, Al, Fe and P raw materials into a vacuum melting furnace, melt at a temperature of 1100°C, fill in argon during the melting process and melt under an argon atmosphere, wherein the components are melted and mixed After that, keep the constant temperature for 1.5 hours, then cool it down to below 400°C with the furnace, then raise the temperature to 1100°C to continue the smelting process, repeat 2 times, cool the smelted product to room temperature with the furnace, and then grind it into a particle size less than 0.1 mm to obtain alloy powder, wherein the purity ...

Embodiment 3

[0042] A kind of preparation method of fiber modified plate, it comprises the steps:

[0043] (1) Dry the polyester chips at 150°C for 5 hours. During the drying process, inert gas is continuously introduced to make the polyester chips dry in an inert gas atmosphere. The moisture content of the dried polyester chips is low at 300ppm;

[0044] (2) According to chemical composition (Pt 27 al 32 Fe 34 P 23 ) Put Pt, Al, Fe and P raw materials into a vacuum melting furnace, melt at a temperature of 900°C, fill in argon during the melting process and melt under an argon atmosphere, wherein the components are melted and mixed After that, keep the constant temperature for 1.5 hours, then cool it down to below 400°C with the furnace, then raise the temperature to 900°C to continue the smelting process, repeat 4 times, cool the smelted product to room temperature with the furnace, and then grind it into a particle size less than 0.1 mm to obtain alloy powder, wherein the purity of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a fiber modified plate and its application, which comprises a first layer formed by plastic and modified fiber doped in the first layer, and the modified fiber is made of polyester chip and alloy After the powders are mixed, the polyester chips in the mixing system are heated to a molten state, further mixed by a twin-screw extruder, and then sent to a spinning device to make modified fibers; the chemical composition of the alloy powder for Pt x Al y Fe m P n , among them, 23≤x≤27, 32≤y≤37, 34≤m≤42, 23≤n≤26, the plate of this scheme has good wear resistance, reliable and convenient processing and stable performance.

Description

technical field [0001] The invention relates to the field of plates and fiber composite materials, in particular to a fiber modified plate and its application. Background technique [0002] As one of the widely used materials in construction, furniture and other fields, plastic sheet is not only low in cost but also convenient in production and molding, which makes it favored by merchants and consumers. With the increasing diversity of consumer demand, the performance of the sheet The requirements are becoming more and more stringent and targeted. Therefore, some plastic sheets currently on the market increase their toughness by adding toughening agents, and increase their weather resistance by adding light shielding agents. However, in terms of wear resistance It has always been a shortcoming of plastic boards. Since plastics are mostly resin components, their surface hardness is low. When they come into contact with materials such as metal or stone, obvious scratch marks a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/12C08L23/06C08L67/00C08K3/08C08K5/20D01F6/92D01F1/10
CPCC08L23/06C08L23/12C08L2205/16D01F1/10D01F6/92C08L67/00C08K3/08C08K5/20
Inventor 敖显鸿陆欢
Owner GUIZHOU SENSUYU WOOD PLASTIC CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap