A kind of transparent heat-resistant polycarbonate material and preparation method thereof

A polycarbonate, heat-resistant technology, used in the field of polycarbonate composites and their preparation, can solve the problems of poor solubility, poor processability, high melt viscosity, difficult to prepare, etc., and achieves improved light transmission performance, industrial Simple preparation and improved transparency

Active Publication Date: 2021-04-13
HANGZHOU NORMAL UNIVERSITY
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] It is worth noting that in the wide application of polycarbonate mentioned above, there are two aspects that need to be considered in the research and development of polycarbonate materials: first, the transparency of polycarbonate materials
Second, the heat resistance of polycarbonate
Although polyarylate has good heat resistance, it also has some disadvantages, such as high melt viscosity, poor fluidity, poor solubility and processability, especially thin-walled and large-scale products are difficult to produce

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of transparent heat-resistant polycarbonate material and preparation method thereof
  • A kind of transparent heat-resistant polycarbonate material and preparation method thereof
  • A kind of transparent heat-resistant polycarbonate material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 2-1

[0035] Step (1). Vacuum dry the polycarbonate and polyarylate at 120°C for 24 hours respectively (Li-TFSI does not need to be dried);

[0036] Step (2). Add 36g of dried polycarbonate, 24g of dried polyarylate and 0.3g of Li-TFSI into the internal mixer, melt and blend at 260°C, and melt and mix at 50rpm / min 10min.

[0037]Step (3). The mixture is discharged from the melting and kneading equipment and lowered to normal temperature to obtain a polycarbonate composite material.

[0038] The mass ratio of polycarbonate, polyarylate and Li-TFSI in the polycarbonate composite prepared in Example 2-1 is 60:40:0.5.

[0039] The materials prepared in Comparative Example 1 and Example 2-1 were tested for thermal performance.

[0040] The materials prepared in Comparative Example 1 and Example 2-1 were subjected to a light transmittance-haze test, and the test conditions were as follows: the samples should be pressed into 0.3 mm thin slices.

[0041] The glass transition temperature ...

Embodiment 2-2

[0050] Step (1). Vacuum dry the polycarbonate and polyarylate at 120°C for 24 hours respectively (Li-TFSI does not need to be dried);

[0051] Step (2). Add 42g of dried polycarbonate, 18g of dried polyarylate and 0.3g of Li-TFSI into the internal mixer, melt and blend at 260°C, and melt and mix at 50rpm / min 10min.

[0052] Step (3). The mixture is discharged from the melting and kneading equipment and lowered to normal temperature to obtain a polycarbonate compound with high transparency.

[0053] The mass ratio of polycarbonate, polyarylate and Li-TFSI in the polycarbonate compound prepared in Example 2-2 is 70:30:0.5.

Embodiment 2-3

[0055] Step (1). Vacuum dry the polycarbonate and polyarylate at 120°C for 24 hours respectively (Li-TFSI does not need to be dried);

[0056] Step (2). Add 48g of dried polycarbonate, 16g of dried polyarylate and 0.3g of Li-TFSI into the internal mixer, melt and blend at 250°C, and melt and mix at 40rpm / min 10min.

[0057] Step (3). The mixture is discharged from the melting and kneading equipment and lowered to normal temperature to obtain a polycarbonate compound with high transparency.

[0058] The mass ratio of polycarbonate, polyarylate and Li-TFSI in the polycarbonate composite prepared in Example 2-3 is 80:20:0.5.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a transparent heat-resistant polycarbonate material and a preparation method thereof. The polycarbonate material is a blend of polycarbonate, polyarylate and organic salt. The preparation method is to vacuum-dry polycarbonate and polyarylate at 80-120°C for 24-48 hours respectively; dry polycarbonate, polyarylate and organic salt according to the mass ratio of 60-90:40-10: 0.3-3, put into the melting and mixing equipment for melting and kneading at 250-300°C to obtain a mixture; discharge the mixture from the melting and mixing equipment, and lower it to normal temperature to obtain a polycarbonate material. The polycarbonate material in the invention has excellent light transmittance and good heat resistance, and its preparation method only needs to use common melting and mixing equipment, and the industrial preparation is simple.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and relates to a polycarbonate composite with high transparency and heat resistance and a preparation method thereof, in particular to a polycarbonate compound with heat resistance obtained by modifying polycarbonate with an organic salt. Polycarbonate compound with transparent properties and preparation method thereof. Background technique [0002] Polycarbonate (referred to as PC) is an amorphous, odorless, tasteless, non-toxic and transparent thermoplastic polymer. It is the only plastic variety with good transparency. It has good mechanical strength, heat resistance, and UV resistance. Radiation and electrical resistance comprehensive performance, high impact resistance, low creep, stable product size, easy to strengthen, non-toxic and hygienic, can be colored, has good cost performance and the potential of chemical modification and physical modification. It is an excellent comprehe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L69/00C08L67/03C08K5/435
CPCC08L69/00C08L2201/08C08L2201/10C08L67/03C08K5/435B29C48/022B29C48/16B29C48/397B29C48/92B29C2948/9259C08L67/00B29C2948/9258B29C2948/92885
Inventor 李勇进徐慧慧
Owner HANGZHOU NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap