Modified natural rubber waterproof emulsion and preparation method thereof

A natural rubber and waterproof emulsion technology, which is applied in natural rubber coatings, anti-corrosion coatings, coatings, etc., can solve the problems of high glass transition temperature, poor low-temperature film-forming property, water resistance, etc., and achieve excellent anti-aging performance, acid and alkali resistance Good performance and excellent waterproof performance

Inactive Publication Date: 2019-12-20
王廷龙
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the disadvantages of ethylene-vinyl acetate emulsion, such as high glass transition temperature, poor low-temperature film-forming property, water resistance, cold resistance and poor mechanical stability, greatly limit its application.
Moreover, the ethylene-vinyl acetate emulsion will turn white when it touches water, which cannot meet the fields that have high requirements for the waterproof performance of the emulsion.
[0004] Furthermore, since this type of coating is a curing mechanism in which cement and polymer emulsion cooperate with each other with the volatilization of water, the drying speed is obviously slowed down in a closed environment with a temperature of ≤10° and a humidity of ≥80% or in a more complicated environment. , to a certain extent affect the progress of construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified natural rubber waterproof emulsion and preparation method thereof
  • Modified natural rubber waterproof emulsion and preparation method thereof
  • Modified natural rubber waterproof emulsion and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Embodiment 1 A kind of modified natural rubber waterproof emulsion, comprises each component of following mass percent:

[0035]

[0036] The emulsifier is commercially available polyurethane-acrylate composite latex. The initiator is ammonium persulfate. The adhesive is selected from chloroprene phenolic adhesives.

[0037] Described auxiliary agent comprises each component accounting for the following mass percentages of described waterproof emulsion gross mass:

[0038] Defoamer: 1%;

[0039] Stabilizer: 0.5%;

[0040] Thickener: 0.5%;

[0041] Fungicide: 0.5%;

[0042] Multifunctional additive: 0.5%.

[0043] The defoamer is a polyether silicone oil defoamer. The stabilizer is gas phase titanium dioxide. The thickener is a polyacrylate thickener. The fungicide is benzisothiazolinone. The multifunctional auxiliary agent AMP-95.

[0044] The preparation method of described modified natural rubber waterproof emulsion, comprises the steps:

[0045] (1) Th...

Embodiment 2

[0048] Embodiment 2 A kind of modified natural rubber waterproof emulsion, comprises each component of following mass percentage content:

[0049]

[0050]

[0051] The emulsifier is commercially available polyurethane-acrylate composite latex. The initiator is potassium persulfate. The adhesive is selected from epoxy resin adhesives.

[0052] Described auxiliary agent comprises each component accounting for the following mass percentages of described waterproof emulsion gross mass:

[0053] Defoamer: 2%;

[0054] Stabilizer: 1%;

[0055] Thickener: 0.5%;

[0056] Fungicide: -0.5%;

[0057] Multifunctional Auxiliary: 1%.

[0058] The defoamer is a silicone oil emulsion defoamer. The stabilizer is nano ceria. The thickener is a polyacrylate thickener and a polyurethane thickener. The fungicide is isothiazolinone. The multifunctional auxiliary agent AMP-96.

[0059] The preparation method of described modified natural rubber waterproof emulsion, comprises the st...

Embodiment 3

[0063] Embodiment 3 A kind of modified natural rubber waterproof emulsion, comprises each component of following mass percentage content:

[0064]

[0065]

[0066] The emulsifier is commercially available polyurethane-acrylate composite latex.

[0067] The initiator is sodium persulfate. The adhesive is polyurethane adhesive.

[0068] Described auxiliary agent comprises each component accounting for the following mass percentages of described waterproof emulsion gross mass:

[0069] Defoamer: 0.5;

[0070] Stabilizer: 0.5;

[0071] Thickener: 0.25;

[0072] Fungicide: 0.25;

[0073] Multifunctional additive: 0.5.

[0074] The defoamer is a polyether silicone oil defoamer. The stabilizer is gas phase titanium dioxide. The thickener is a polyurethane thickener. The bactericide is a mixture of isothiazolinone and benzisothiazolinone. The multifunctional auxiliary agent AMP-95.

[0075] The preparation method of described modified natural rubber waterproof emulsi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical field of waterproofness and in particular to a modified natural rubber waterproof emulsion which comprises the following components in percentage by mass: 40-70%of natural rubber, 25-35% of a cation emulsion, 0.5-6% of an initiator, 0.5-6% of an emulsifier, 2-8% of an adhesive and 2-5% of aids. The modified natural rubber waterproof emulsion has excellent waterproof performance, is good in acid-alkali resistance, has properties of corrosion resistance and humidity resistance, can be rapidly formed as a film at a low temperature, is high in transparency after being dried, is free of color difference, gel or caking, and has a solid content up to 50% or greater.

Description

technical field [0001] The invention relates to the technical field of waterproofing, in particular to a modified natural rubber waterproof emulsion and a preparation method thereof. Background technique [0002] Polymer cement waterproof coating is made of modified polymer emulsion and cement as the main raw materials, adding various additives and inorganic fillers. The material has good film-forming properties and is suitable for waterproofing, Seepage-proof and moisture-proof. [0003] For example, Chinese patent document CN201810956051.X discloses a polymer cement waterproof coating, including liquid material and powder material. The liquid material includes the following components in parts by weight: 50-60 parts of ethylene-vinyl acetate emulsion, 0.3-60 parts of emulsifier 0.9 parts, 15-30 parts of plasticizing emulsion, 0.6-1.2 parts of dispersant and 10-15 parts of water; the powder includes the following components in parts by weight: 30-40 parts of cement, 20-30 ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D107/00C09D201/00C09D161/14C09D163/00C09D175/04C09D131/04C09D7/65C09D5/08
CPCC08L2205/035C09D5/08C09D107/00C09D7/65C08L101/00C08L61/14C08L51/08C08L63/00C08L75/04C08L31/04
Inventor 王廷龙
Owner 王廷龙
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap