Method for improving cold strength of coke

A cold-strength, high-strength technology, applied in the coking oven, petroleum industry, etc., can solve the problems of high coal quality index requirements for fat coal, poor practicability, complicated methods, etc., achieve good environmental and economic benefits, and reduce the use of efficiency and reduce production costs

Inactive Publication Date: 2019-12-24
BAOSHAN IRON & STEEL CO LTD
View PDF11 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The Chinese patent application whose publication number is CN103184058A proposes a method that is beneficial to the cold strength of coke. This method requires that the Aurora expansion degree of fat coal is greater than 150%, the proportion of fat coal is 10-20%, and the gas fat coal is required. The percentage of fat coal with a volatile content greater than 34% should be less than 10% to obtain coke with better cold strength, but this method is more complicated and has high requirements on the coal quality index of fat coal, and gas fat coal in coal blending It is difficult to control the percentage of the sum of fat coal with volatile content greater than 34% is less than 10%
This makes the method less practical

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for improving cold strength of coke

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The gas coal with a particle size of less than 6mm from the production plant is added to the crusher for crushing. After crushing, the particle size of the gas coal is screened and analyzed. After crushing, the proportion of the particle size of the gas coal smaller than 3mm is 48%. The processed gas coal is blended with other types of coal. The proportion of gas coal in the entire blended coal is 25.5%, and the ash content of the blended coal after blending is A d =8%, the volatile matter is VM d = 28%. Add the blended coal into the crusher for repeated crushing. The groove spacing of the crusher is 3mm, and the proportion of the crushed blended coal with particle size less than 3mm is 86%. Use a spraying device to mix a certain amount of water into the crushed blended coal to facilitate even moisture blending and ensure that the moisture content of the blended coal is 4%. Finally, add the blended coal to 40kg of coke oven and heat it at a heating rate of 4°C / min. 10...

Embodiment 2

[0030] The gas coal with a particle size of less than 6mm from the production plant is added to the crusher for crushing. After crushing, the particle size of the gas coal is screened and analyzed. After crushing, the proportion of the particle size of the gas coal smaller than 3mm is 50%. The processed gas coal is blended with other types of coal. The proportion of gas coal in the entire blended coal is 26%, and the ash content of the blended coal after blending is A d =9%, the volatile matter is VM d = 27%. Add the blended coal into the crusher for repeated crushing. The groove spacing of the crusher is 3.5mm, and the proportion of the crushed blended coal with a particle size less than 3mm is 85%. Use a spraying device to mix a certain amount of water into the crushed blended coal to facilitate even moisture blending and ensure that the moisture content of the blended coal is 5%. Finally, add the blended coal to a 40kg coke oven and heat it at a heating rate of 4°C / min. 1...

Embodiment 3

[0033] The gas coal with a particle size of less than 6mm from the production plant is added to the crusher for crushing. After crushing, the particle size of the gas coal is screened and analyzed. After crushing, the proportion of the particle size of the gas coal smaller than 3mm is 51%. The processed gas coal is blended with other types of coal. The proportion of gas coal in the entire blended coal is 26.5%, and the ash content of the blended coal after blending is A d =9.5%, the volatile matter is VM d = 26.5%. Add the blended coal into the crusher for repeated crushing. The groove spacing of the crusher is 4mm, and the proportion of the crushed blended coal with particle size less than 3mm is 84%. Use a spraying device to mix a certain amount of water into the crushed blended coal to facilitate even moisture blending and ensure that the moisture content of the blended coal is 6%. Finally, add the blended coal to a 40kg coke oven and heat it at a heating rate of 4°C / min. ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for improving the cold strength of coke, which comprises the following steps: 1, gas coal crushing: gas coal with the granularity of less than 6 mm from a production plant is fed into a crusher for crushing, performing screening analysis on the granularity of the gas coal after crushing according to the requirement of the proportion of the granularity of less than3 mm in the crushed gas coal to be 48-53%; 2, blending of blended coal: the crushed gas coal is blended with 1 / 3 coking coal, fat coal and lean coal according to the requirements of coal blending, themass ratio of the gas coal in the whole blended coal is 25.5-27%, the ash content Ad of the blended coal is 8-10%, and the volatile matter VMd of the blended coal is 26-28%; 3, crushing and mixing ofthe blended coal: the blended coal is added into a crusher for repeated crushing, the groove spacing of the crusher is 3-4 mm, and the mass ratio of the blended coal with the particle size smaller than 3 mm after crushing is 84-86%; and 4, moisture adjustment and preparation of high-strength coke.

Description

technical field [0001] The invention belongs to the technical field of coke quality control for high-temperature pyrolysis of coal, and in particular relates to a method for improving the cold strength of coke. Background technique [0002] In recent years, the rapid expansion of coke production capacity has led to a tight supply of coking coal. In addition, due to the current large-scale blast furnaces in iron and steel enterprises, the requirements for coke quality and stability are getting higher and higher, and coking coal resources are strongly bonded. Natural coal is less and less, this contradiction is particularly prominent in our country. How to rationally utilize coal resources to meet the needs of coking production is a long-term task. With the slowdown of the national economic growth rate in 2016, the serious overcapacity of my country's coking industry is highlighted. Only by improving coal blending coking technology, increasing coke production and quality, and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10B57/04
CPCC10B57/04
Inventor 王玉明胡德生毛晓明钱晖徐万仁
Owner BAOSHAN IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products