A kind of PVC furniture film/asa plastic film water-based composite ink and preparation method thereof

A technology for plastic film and furniture, which is applied in ink, household utensils, applications, etc. It can solve the problems of inability to print in color and restrict the application of ASA film, and achieve good anti-plasticizer migration, high cost performance, and good printing effects

Active Publication Date: 2021-10-08
HANGZHOU HIWETECH CHEM TECH CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, due to the similar structural characteristics of ASA and ABS (micron-sized rubber "sea islands" dispersed in the plastic continuous phase), the unprocessed ASA films currently on the market are all opaque films, which can only use plastic toner Single coloring, can not be printed in color like PVC film, which undoubtedly restricts the application of ASA film in the field of decoration to a large extent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of PVC furniture film/asa plastic film water-based composite ink and preparation method thereof
  • A kind of PVC furniture film/asa plastic film water-based composite ink and preparation method thereof
  • A kind of PVC furniture film/asa plastic film water-based composite ink and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0076] (1) Preparation of monomer dropping phase: at room temperature, 23.012 kg of methyl methacrylate monomer (Guangzhou Zhongye Chemical Co., Ltd.), 20.548 kg of methyl acrylate monomer (Shanghai Merrill Chemical Technology Co., Ltd. company), 0.44kg of glycidyl methacrylate monomer (Jiangxi Ruixiang Chemical Co., Ltd.), 0.00368 kg of isooctyl 3-mercaptopropionate (Sinopharm Chemical Reagent Co., Ltd.) chain transfer reagent and 2kg of ER- 40 (ADEKA company) nonionic emulsifier is stirred and dissolved 40min with the speed of 500rpm, obtains the monomer dropwise addition phase;

[0077] (2) Preparation of the primer phase: 1.3kg of DowFax TM 8390 (DOW company) anionic emulsifier, 0.7kg of ER-40 (ADEKA company) nonionic emulsifier, 0.11kg of AMP-95 (Dow company) pH buffer, 0.08kg of potassium persulfate (Wujiang Sanyuan fine Chemical Co., Ltd.) initiator joins the deionized water of 39kg, stirs and dissolves with the speed of 400rpm, obtains the base phase;

[0078] (3) P...

Embodiment 1

[0081] At room temperature, mix 30kg of purified water, 2kg of ethanol (Suzhou Outer Chemical Co., Ltd.), 4kg of dispersant ADISPERBYK-190 (BYK company), 0.8kg of dispersant B cellulose acetate butyrate (such as Eastman CAB 553-0.4 , Eastman Company) and 0.6kg of co-solvent 3-methoxy-3-methyl butyl acetate (Hubei Ferry Chemical Co., Ltd.) were sequentially added to the dispersion kettle, stirred and mixed evenly at a speed of 100rpm, and then added 8kg of Pigment Red 177 (P.R.177, Zhejiang Lily Group Co., Ltd.), 0.5kg of nano-calcium carbonate (below particle size 40nm, Henan Keli New Materials Co., Ltd.) filler, after stirring and mixing at a speed of 400rpm, and then sequentially Add 9kg of film-forming resin A and 6kg of film-forming resin B, then transfer to a horizontal sand mill (TBM-50, Taiyi (Shanghai) Industrial Co., Ltd.) and grind for 2 passes until the particle size of the color paste reaches 300nm After the following steps, the material is filtered and discharged ...

Embodiment 2

[0098] At room temperature, 29kg of purified water, 3kg of ethanol (Suzhou Outer Chemical Co., Ltd.), 3kg of dispersant ADISPERBYK-190 (BYK company), 1kg of dispersant B cellulose acetate butyrate (such as Eastman CAB 553-0.4, Eastman Company) and 0.8kg of co-solvent 3-methoxyl-3-methyl butyl acetate (Hubei Ferry Chemical Co., Ltd.) were sequentially added to the dispersion kettle, stirred and mixed evenly at a speed of 200rpm, and then added 5kg of pigment Yellow Yellow2154C (P.Y.154, Zhejiang Lily Group Co., Ltd.), 0.3kg of nano-calcium carbonate (below 40nm in particle size, Henan Keli New Material Co., Ltd.) filler, stir and mix evenly at a speed of 200rpm, and then add 6kg of film-forming resin A and 4kg of film-forming resin B are then transferred to a horizontal sand mill (TBM-50, Taiyi (Shanghai) Industrial Co., Ltd.) and ground for 2 passes until the particle size of the color paste reaches below 300nm Afterwards, the material is filtered and discharged to obtain wate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a PVC furniture film / ASA plastic film water-based composite ink and a preparation method thereof. The PVC furniture film / ASA plastic film water-based composite ink of the present invention has good plasticizer migration resistance to PVC furniture films, and can be used on ASA plastic films. Good printing can be achieved on PVC furniture film or PVC furniture film, and it has good bonding strength to PVC furniture film / ASA plastic film system, and the peel strength of blank composite film system can be promoted to a level close to 2 times. The present invention also proposes A new combination of outdoor composite film, which uses cheaper PVC furniture film as the printing base film, and the nearly transparent ASA plastic film developed in recent years as the protective mask. This combination is cost-effective and has good weather resistance. Compared with The combination of traditional PVC furniture film / PVC wear-resistant sheet is more suitable for the field of outdoor color decorative film.

Description

technical field [0001] The present invention relates to a water-based ink and a preparation method thereof, in particular to a water-based ink that can be applied to ASA plastic film gravure printing and a preparation method thereof. The water-based ink of the present invention can be applied to ASA plastic film gravure printing, and can also be applied to PVC furniture film Gravure printing. Background technique [0002] With the rapid development of the industrial economy, the contradictions between the world's population, resources and the environment have further increased, the discharge of environmental pollutants and the destruction of natural ecology have continued to increase, and the pressure on global environmental protection has become increasingly serious. At present, the printing of domestic PVC plastic decorative films (mainly PVC floor films and PVC furniture films) is still dominated by solvent-based inks. Solvent-based inks contain a large amount (generally ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D11/107C09D11/106C09D11/03
CPCC09D11/03C09D11/106C09D11/107
Inventor 许少宏许华君罗英武
Owner HANGZHOU HIWETECH CHEM TECH CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com