A kind of low elastic modulus ti6al4v alloy and its preparation method and application

A low elastic modulus, alloy technology, applied in the field of titanium alloy material preparation, can solve the problem of low elastic modulus

Active Publication Date: 2021-08-31
HUNAN HANDLIKE MINIMALLY INVASIVE SURGERY CO LTD
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Therefore, preparing a Ti6Al4V alloy for medical ultrasonic scalpels with mechanical properties that meet the needs of ultrasonic scalpels and a low elastic modulus has become an urgent problem to be solved in the field of Ti6Al4V alloys for medical ultrasonic scalpels.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] The Ti6Al4V alloy was smelted with pure aluminum with a purity above 99.9wt.%, Al-V mesophase, pure Fe, pure Y and high-purity sponge titanium as raw materials, and the alloy with uniform composition was obtained by repeated smelting for 5 times. Al: 5.54wt.%; V: 4.44wt.%; Fe: 0.16wt.%; Y: 0.08wt.%; Ti: balance; other impurity elements meet relevant national standards. The obtained titanium ingot was heated to 950° C. and then hot-forged into a bar with a total deformation of 76%, and then air-cooled to room temperature. The obtained rod is heated to 930° C. and then hot-drawn into a wire. The total deformation of hot-drawing is 70%, and then air-cooled to room temperature. Annealing treatment in an annealing furnace, the first annealing temperature is 920°C, the annealing time is 1h, air-cooled to room temperature after the heat preservation is completed, the second annealing temperature is 780°C, the annealing time is 1.5h, and air-cooled to room temperature after the...

Embodiment 2

[0054] The Ti6Al4V alloy was smelted with pure aluminum with a purity above 99.9wt.%, Al-V mesophase, pure Fe, pure Y and high-purity sponge titanium as raw materials, and the alloy with uniform composition was obtained by repeated smelting for 5 times. Al: 5.64wt.%; V: 4.48wt.%; Fe: 0.18wt.%; Y: 0.04wt.%; Ti: balance; other impurity elements meet relevant national standards. The obtained titanium ingot was heated to 950° C. and then hot-forged into a bar with a total deformation of 77%, and then air-cooled to room temperature. The obtained rod is heated to 900° C. and then hot-drawn into a wire. The total deformation of hot-drawing is 75%, and then air-cooled to room temperature. Annealing in an annealing furnace, the first annealing temperature is 935°C, the annealing time is 1h, air-cooled to room temperature after the heat preservation is completed, the second annealing temperature is 770°C, the annealing time is 1.5h, air-cooled to room temperature after the heat preserva...

Embodiment 3

[0056] The Ti6Al4V alloy was smelted with pure aluminum with a purity above 99.9wt.%, Al-V mesophase, pure Fe, pure Y and high-purity sponge titanium as raw materials, and the alloy with uniform composition was obtained by repeated smelting for 5 times. Al: 6.2wt.%; V: 4.47wt.%; Fe: 0.18wt.%; Y: 0.01wt.%; Ti: balance; other impurity elements meet relevant national standards. The obtained titanium ingot was heated to 950° C. and hot-forged into a rod with a total deformation of 73%, and then air-cooled to room temperature. The obtained rods were heated to 930° C. and then hot-drawn into filaments. The total deformation of hot-drawing was 71%, and then air-cooled to room temperature. Annealing treatment in an annealing furnace, the first annealing temperature is 960°C, the annealing time is 2h, and air-cooled to room temperature after the heat preservation is completed, the second annealing temperature is 710°C, the annealing time is 1.5h, and air-cooled to room temperature afte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elastic modulusaaaaaaaaaa
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low elastic modulus Ti6Al4V alloy and its preparation method and application. The Ti6Al4V alloy has the following composition in terms of mass percentage: Al: 5.5-6.2wt.%; V: 3.8-4.5wt.%; Fe : 0.16-0.22wt.%; Y: 0.01-0.1wt.%; Ti is the balance. The preparation method is as follows: hot calcining, hot drawing, double annealing heat treatment and machining of Ti6Al4V titanium alloy ingot to obtain Ti6Al4V alloy with low elastic modulus. The elastic modulus of the Ti6Al4V alloy is 80-90GPa. The present invention increases the content of β phase by synergizing the alloy composition and process, thereby reducing the modulus of elasticity of the Ti6Al4V alloy.

Description

technical field [0001] The invention discloses a low elastic modulus Ti6Al4V alloy and a preparation method thereof and is applied to a medical ultrasonic knife, belonging to the field of preparation of titanium alloy materials. Background technique [0002] With the continuous improvement of medical technology, less surgical trauma, less pain, and faster postoperative recovery have become the development trend of surgical operations. Minimally invasive surgery uses laparoscopy, thoracoscopic and other modern medical equipment and related equipment to perform surgery. It is considerate to the patient to the greatest extent on the existing technical level, and achieves the purpose of small surgical trauma, light pain and fast postoperative recovery. It reduces the inconvenience and pain that the disease brings to patients and their families. [0003] As a commonly used instrument for minimally invasive surgery, the ultrasonic scalpel has the characteristics of high precision...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C14/00C22C1/03C22F1/18
CPCC22C1/03C22C14/00C22F1/183
Inventor 李益民赵志刚鄢家杰彭淀
Owner HUNAN HANDLIKE MINIMALLY INVASIVE SURGERY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com