Glass fiber production and processing technology

A technology of glass fiber and processing technology, applied in the field of glass fiber production and processing technology, can solve the problems of insufficient infiltration of glass fiber and poor infiltration effect of glass fiber, and achieve the effect of good infiltration effect and guaranteed infiltration effect.

Active Publication Date: 2020-03-24
五河县维佳复合材料有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, wetting liquid is usually applied on the surface of glass fiber to ensure the performance and storage time of glass fiber, but the existing glass fiber has poor wetting effect, and glass fiber cannot fully infiltrate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass fiber production and processing technology
  • Glass fiber production and processing technology
  • Glass fiber production and processing technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Such as figure 1 , figure 2 , image 3 As shown, the present invention provides a kind of glass fiber production and processing technology, comprises the following steps:

[0031] (1), the raw materials are put into the crucible kiln and melted to form liquid glass;

[0032] (2), the molten glass in (1) is put into the fiber forming equipment to form filiform glass fibers;

[0033] (3), adopting the fiber forming equipment in (2) to cool and wind the fiberglass fiber into bundles;

[0034] (4), the glass fiber after winding in (3) is placed on the soaking equipment and carries out soaking treatment;

[0035] (5), the glass fiber after soaking in (4) is put into warehouse;

[0036] The impregnation equipment used in this process includes:

[0037] A box body 10, the box body 10 is provided with a wetting liquid, and the top of the box body 10 is embedded with a casing 11. In order to facilitate discharging or observation, a transparent window can be set on the sid...

Embodiment 2

[0045] Such as figure 1 , figure 2 , image 3 As shown, the present invention provides a kind of glass fiber production and processing technology, comprises the following steps:

[0046] (1), the raw materials are put into the crucible kiln and melted to form liquid glass;

[0047] (2), the molten glass in (1) is put into the fiber forming equipment to form filiform glass fibers;

[0048] (3), adopting the fiber forming equipment in (2) to cool and wind the glass fibers in filamentary form into bundles;

[0049] (4), the glass fiber after winding in (3) is placed on the infiltration equipment and carries out infiltration treatment;

[0050] (5), the glass fiber after soaking in (4) is put into warehouse;

[0051] The impregnation equipment used in this process includes:

[0052] A box body 10, the box body 10 is provided with a wetting liquid, and the top of the box body 10 is embedded with a casing 11. In order to facilitate discharging or observation, a transparent wi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a glass fiber production and processing technology which comprises the following steps:(1)melting raw materials in a crucible kiln to form liquid glass;(2)putting the molten liquid glass in the step(1)into fiber forming equipment to form filamentous glass fibers;(3)cooling and winding the filamentous glass fibers into bundles by adopting the fiber forming equipment in the step(2);(4)putting the winded glass fibers in the step(3)on infiltration equipment for infiltration treatment;(5)putting the soaked glass fibers in the step(4)into a warehouse; the bundle-shaped glassfibers can enter the infiltration solution in a rotating state, so that the bundle-shaped glass fibers are sufficiently infiltrated, the infiltration effect is good, and the quality of the glass fibers is guaranteed.

Description

Technical field: [0001] The invention relates to the field of glass fiber production and processing, in particular to a glass fiber production and processing process. Background technique: [0002] Glass fiber is a kind of reticular fiber material obtained from glass after high-temperature melting, drawing and other steps, and then winding. Glass fiber has many advantages of super corrosion resistance and light weight. , After the production of glass fiber products is completed, they will be stored in the warehouse or directly sent to the customer by means of transportation. Whether it is warehouse or transportation, it will be placed for a period of time. Generally speaking, the longer the storage time, the greater the impact on the performance of the glass fiber. There are many reasons for this situation, one of which is the erosion of the glass fiber by moisture in the air; on the other hand, the surface of the glass fiber product is a polymer product, and the polymer i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C25/007C03B37/022
CPCC03B37/022C03C25/007Y02P40/57
Inventor 卢克香
Owner 五河县维佳复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products