Reactive single-component polyurethane root-puncture-resistant waterproof coating material and preparation method thereof

A waterproof coating, root puncture-resistant technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., to ensure the uniformity of dispersion, improve stability and durability, and easy to use.

Active Publication Date: 2020-03-24
KESHUN WATERPROOF TECH CO LTD
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

A similar reactive root puncture resistant waterproof material has not yet appeared

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reactive single-component polyurethane root-puncture-resistant waterproof coating material and preparation method thereof
  • Reactive single-component polyurethane root-puncture-resistant waterproof coating material and preparation method thereof
  • Reactive single-component polyurethane root-puncture-resistant waterproof coating material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A reactive single-component polyurethane root puncture-resistant waterproof coating, including the following raw material components: 12 parts of amino-terminated polyether (D2000), 12 parts of polyether trihydric alcohol (330N), 5 parts of isocyanate (TDI), chlorinated 20 parts of paraffin, 47 parts of pigments and fillers (heavy calcium, talcum powder), 0.1 parts of organic tin catalyst (CT-11), 1.8 parts of latent curing agent (JW505), chemical root inhibitor ((R)-2-(4- Chloro-2-methylphenoxy) propionate-2-hydroxypropyl) 0.5 parts, silicone defoamer (AP001) 0.2 parts, dispersant 0.05 parts, mineral spirits 3 parts.

[0036] Specific preparation steps: add 12 parts of amino-terminated polyether (D2000), 12 parts of polyether trihydric alcohol (330N), 20 parts of chlorinated paraffin, 0.2 parts of silicone defoamer (AP001), and Filler (heavy calcium, talcum powder) 47 parts, after high-speed dispersion evenly, heat up to 100-110°C under stirring, and dehydrate for abou...

Embodiment 2

[0038] A reactive single-component polyurethane root puncture-resistant waterproof coating, including the following raw material components: 12 parts of amino-terminated polyether (D2000), 12 parts of polyether trihydric alcohol (330N), 5 parts of isocyanate (TDI), chlorinated 20 parts of paraffin, 47 parts of pigments and fillers (heavy calcium, talcum powder), 0.1 parts of organic tin catalyst (CT-11), 1.8 parts of latent curing agent (JW505), chemical root inhibitor ((R)-2-(4- Chloro-2-methylphenoxy)propionic acid-2-hydroxypropyl ester) 1 part, silicone defoamer (AP001) 0.2 part, dispersant 0.05 part, mineral spirits 3 parts.

[0039] The specific preparation steps are: add 12 parts of amino-terminated polyether (D2000), 12 parts of polyether trihydric alcohol (330N), 20 parts of chlorinated paraffin, 0.2 part of silicone defoamer (AP001) into the reaction vessel, 47 parts of pigments and fillers (heavy calcium, talcum powder), after high-speed dispersion, heat up to 100-11...

Embodiment 3

[0041] A reactive single-component polyurethane root puncture-resistant waterproof coating, including the following raw materials: 12 parts of amino-terminated polyether (D2000), 12 parts of polyether trihydric alcohol (330N), 4 parts of isocyanate (TDI), chlorinated 20 parts of paraffin, 47 parts of pigments and fillers (heavy calcium, talcum powder), 0.1 parts of organic tin catalyst (CT-11), 1.8 parts of latent curing agent (JW505), chemical root inhibitor ((R)-2-(4- Mixture of 2,3-dihydroxypropyl chloro-2-methylphenoxy)propionate and 1,3-bis(R)-2-(4-chloro-2-methylphenoxy)propionate) 0.5 parts, silicone defoamer (AP001) 0.2 parts, dispersant 0.05 parts, mineral spirits 3 parts.

[0042] The specific preparation steps are: add 12 parts of amino-terminated polyether (D2000), 12 parts of polyether trihydric alcohol (330N), 20 parts of chlorinated paraffin, 0.2 part of silicone defoamer (AP001) into the reaction vessel, 47 parts of pigments and fillers (heavy calcium, talcum ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of waterproof coating materials, and discloses a reactive single-component polyurethane root-puncture-resistant waterproof coating material and a preparation methodthereof, wherein the waterproof coating is added with a chemical root-retardant agent capable of carrying out a chemical reaction with isocyanate in a coating material, and the molecular structure ofthe chemical root-retardant agent contains a root-retardant active group and one or two hydroxyl groups capable of carrying out a chemical reaction with the main component isocyanate in a polyurethanecoating material. According to the invention, the root-puncture-resistant waterproof coating material has excellent physical properties; the root-retardant agent of the root-puncture-resistant waterproof coating material directly participates in a chemical reaction, so that the root-puncture-resistant waterproof coating material has reliable and durable root-puncture-resistant effect compared with traditional physical addition, and is a real reactive single-component polyurethane root-puncture-resistant waterproof coating material; and the root-puncture-resistant waterproof coating material is suitable for planting roofs in various environments.

Description

technical field [0001] The invention relates to the field of waterproof materials, more specifically, to a reactive single-component polyurethane root puncture-resistant waterproof coating and a preparation method thereof. Background technique [0002] The one-component polyurethane waterproof coating is composed of isocyanate and polyether as the main raw materials, and isocyanate group-containing prepolymer formed by addition polymerization reaction under the action of a catalyst, together with additives, fillers, solvents, etc., after mixing and other processes Processed. This type of coating is a reaction-curing coating, which solidifies after contacting with moisture in the air, and forms a dense and tough seamless overall protective film on the surface of the base layer. It has the characteristics of high strength, high elongation, and good water resistance. In the actual application process, it has strong adaptability to the deformation of the base layer, and is suit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/08
CPCC09D175/08
Inventor 朱月泉梁水清陈立义龚兴宇
Owner KESHUN WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap