Sports knitted fabric and preparation method thereof

A kind of knitted fabric, sports technology, applied in knitting, warp knitting, weft knitting and other directions, can solve the problem of uneven female shape, and achieve the effect of good moisture absorption and sweat wicking performance and wide application range.

Active Publication Date: 2021-08-13
JIANGSU HENGLI CHEM FIBER
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention provides a sports knitted fabric and its preparation method, aiming to solve the problem of random "strip-like unevenness" in the prior art when two-component side-by-side fibers are applied to sports knitted fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sports knitted fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The preparation method of sports knitted fabric, its process is as follows:

[0045] (1) Preparation of self-curling elastic fibers:

[0046] (1.1) Self-curling elastic fibers are extruded on the same spinneret, specifically:

[0047] Divide CDP melt (intrinsic viscosity 0.6dL / g) into two paths: one path is directly extruded after distribution; the other path is distributed with PTT melt (intrinsic viscosity 1.1dL / g) in parallel composite spinning squeeze out

[0048] The ratio between the number of spinneret holes m (four-lobed spinneret holes) that are directly extruded and flowed through and the number of spinneret holes n (circular spinneret holes) that are extruded and flowed through after distribution according to the parallel composite spinning method The ratio is 1:7; the mass ratio of the mass of the CDP melt passing through the spinneret n to the mass of the PTT melt is 50:50, and the ratio of the equivalent diameter of the spinneret m to the spinneret n is ...

Embodiment 2

[0061] The preparation method of sports knitted fabric, its process is as follows:

[0062] (1) Preparation of self-curling elastic fibers:

[0063] (1.1) Self-curling elastic fibers are extruded on the same spinneret, specifically:

[0064] Divide CDP melt (intrinsic viscosity 0.57dL / g) into two paths: one path is directly extruded after distribution; the other path is distributed with PTT melt (intrinsic viscosity 1.16dL / g) in parallel composite spinning squeeze out

[0065] The ratio between the number of spinneret holes m (four-lobed spinneret holes) that are directly extruded and flowed through and the number of spinneret holes n (circular spinneret holes) that are extruded and flowed through after distribution according to the parallel composite spinning method The ratio is 1:6; the mass ratio of the mass of the CDP melt passing through the spinneret n to the mass of the PTT melt is 50:50, and the ratio of the equivalent diameter of the spinneret m to the spinneret n i...

Embodiment 3

[0075] The preparation method of sports knitted fabric, its process is as follows:

[0076] (1) Preparation of self-curling elastic fibers:

[0077] (1.1) Self-curling elastic fibers are extruded on the same spinneret, specifically:

[0078] Divide the CDP melt (intrinsic viscosity 0.58dL / g) into two paths: one path is directly extruded after distribution; the other path is distributed with PTT melt (intrinsic viscosity 1.18dL / g) in parallel composite spinning squeeze out

[0079] The ratio between the number of spinneret holes m (four-lobed spinneret holes) that are directly extruded and flowed through and the number of spinneret holes n (circular spinneret holes) that are extruded and flowed through after distribution according to the parallel composite spinning method The ratio is 1:7; the mass ratio of the mass of the CDP melt passing through the spinneret n to the mass of the PTT melt is 50:50, and the ratio of the equivalent diameter of the spinneret m to the spinneret...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Basis weightaaaaaaaaaa
heightaaaaaaaaaa
Evaporation rateaaaaaaaaaa
Login to View More

Abstract

The invention relates to a sporty knitted fabric and a preparation method thereof. Cotton fibers are used as the raw material of the veil, self-curling elastic fibers are used as the raw material of the middle yarn, and fine denier cross-shaped PET fibers are used as the raw material of the ground yarn. The sports knitted fabric is obtained by finishing; the self-curling elastic fiber is obtained according to the FDY process. The CDP melt is divided into two paths: one path is directly extruded after distribution, and the other path is distributed and extruded together with the PTT melt in a parallel composite spinning method. out. The sports knitted fabric prepared by the present invention does not have the problem of "uneven stripes"; the weight of the sports knitted fabric is 120-160g / m 2 , the washing dimensional change rate in both warp and weft directions is between ‑1.0%~1.0%, the water absorption rate of sports knitted fabrics is ≥275%, the drip diffusion time is ≤2.2 seconds, the wicking height is ≥142mm, and the evaporation rate is ≥0.33 g / h, moisture permeability ≥128000g / (m 2 d).

Description

technical field [0001] The invention belongs to the technical field of textile fabrics, and relates to a sports knitted fabric and a preparation method thereof. Background technique [0002] Today's consumers place ever higher demands on the comfort and functionality of textiles. For spring and summer clothes, it is desired to be light, breathable and comfortable; for autumn and winter clothes, it is required to have good warmth retention. For sporty clothes, it is hoped that it only has a good moisture absorption and perspiration function, while traditional fabrics cannot meet the needs of consumers. Thereby developing sports fabric is of great practical significance. Sports moisture-wicking fabrics are mainly suitable for use in environments with a lot of exercise, sweating and hot weather. Generally, the sweat on the surface of the human body is conducted outward through close-fitting sportswear to keep the skin dry and comfortable. [0003] In the big family of two-co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D04B1/10D04B1/12D04B1/16D04B1/18D04B21/08D01D5/22D01D5/253D01D5/32D01D10/02D06H3/08
CPCD01D5/22D01D5/253D01D5/32D01D10/02D04B1/102D04B1/12D04B1/16D04B1/18D04B21/08D06H3/08D10B2331/04
Inventor 王丽丽王山水范红卫任怀林汤方明
Owner JIANGSU HENGLI CHEM FIBER