A kind of preparation method of titanium-aluminum alloy target

A titanium-aluminum alloy and target material technology, which is applied in metal processing equipment, metal material coating process, transportation and packaging, etc., can solve the problems of cumbersome process, high process cost and high energy consumption

Active Publication Date: 2020-10-27
东莞市欧莱溅射靶材有限公司
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since the melting point of the titanium-aluminum alloy phase reaches above 1500°C, different molding processes require a minimum molding temperature of above 1100°C, the process is cumbersome, the process is long, the process cost is high, and the energy consumption is high.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of titanium-aluminum alloy target
  • A kind of preparation method of titanium-aluminum alloy target
  • A kind of preparation method of titanium-aluminum alloy target

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] The following are only preferred embodiments of the present invention, and therefore do not limit the protection scope of the present invention.

[0032] A method for preparing a titanium-aluminum alloy target, comprising a powder mixing step, a filling step, a cold isostatic pressing step, a welding sheath degassing step, a hot isostatic pressing step, a cutting step, an alloying diffusion heat treatment step and a machine Machining and trimming steps.

[0033] Titanium aluminum targets are widely used in the fields of tools and decorative coatings. Titanium-aluminum alloy has low density, high strength and hardness, and has good wear resistance. Coating a layer of titanium-aluminum alloy on the surface of ordinary knives can enhance the surface hardness of the knives, make the knives sharper, and effectively extend the use time of the knives . Under different atmospheres, titanium-aluminum alloy targets can form decorative films of different colors such as yellow, b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a titanium-aluminum alloy target, which comprises a powder mixing step, a filling step, a cold isostatic pressing step, a welding sheath degassing step, a hot isostatic pressing step, a cutting step, and alloying diffusion A heat treatment step and a machining finishing step. The preparation method of the invention has the advantages of simple control, low processing cost and high processing efficiency.

Description

technical field [0001] The invention relates to the technical field of a titanium-aluminum alloy target, in particular to a preparation method of a titanium-aluminum alloy target. Background technique [0002] At present, the production process of titanium aluminum alloy target mainly includes smelting casting and powder alloying and sintering. [0003] When the smelting process is used to manufacture titanium-aluminum targets, air bubbles, porosity and segregation are prone to occur during the pouring process; titanium-aluminum alloys are difficult to heat process, casting defects are difficult to remove, density is difficult to increase, and the yield is low. At the same time, it is difficult to ensure the uniformity of the composition and structure in the titanium-aluminum alloy, which leads to the inability to guarantee the stability of the quality of the titanium-aluminum target. [0004] Powder alloying and then sintering, firstly mix aluminum powder and titanium powd...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C14/35B22F1/00B22F9/04B22F3/04B22F3/15B22F3/24B22F5/00C22C21/00
CPCC23C14/35C23C14/3414B22F9/04B22F3/04B22F3/15B22F3/24B22F5/00C22C21/003B22F2009/043B22F2003/248B22F1/052
Inventor 张中美
Owner 东莞市欧莱溅射靶材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com