Photosensitive elastomer composition having excellent ink affinity and flexographic resin plate containing photosensitive elastomer composition

An elastomer and composition technology, applied in the field of letterpress printing, can solve problems such as poor inking and affect the quality of printed products, and achieve the effect of improving the quality of printed products and excellent ink-friendly performance.

Pending Publication Date: 2020-05-05
LUCKY HUAGUANG GRAPHICS
7 Cites 0 Cited by

AI-Extracted Technical Summary

Problems solved by technology

When printing rough carton substrates, ordinary flexible resin plates can easily meet the requirements; however, when printing flexible packaging materi...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Abstract

The invention discloses a photosensitive elastomer composition with excellent ink affinity. The photosensitive elastomer composition comprises (A) a thermoplastic elastomer; (B) a liquid polyolefin plasticizer; (C) liquid polybutadiene of which the tail end is grafted with a hydrophilic group; (D) a monomer containing at least one unsaturated double bond functional group; (E) a photoinitiator or aphotoinitiation system; (F) auxiliaries. According to the flexographic resin plate containing the photosensitive elastomer composition having excellent ink affinity, the polymer liquid polybutadienecontaining hydrophilic groups is introduced into a photosensitive elastomer, so that the flexographic resin plate has excellent ink affinity; and the flexographic printing ink on an ink transfer roller is more easily accepted when the embossment image-text part using the flexographic resin plate is printed, so that the purpose of improving the quality of printed products is achieved.

Application Domain

Technology Topic

Image

  • Photosensitive elastomer composition having excellent ink affinity and flexographic resin plate containing photosensitive elastomer composition
  • Photosensitive elastomer composition having excellent ink affinity and flexographic resin plate containing photosensitive elastomer composition
  • Photosensitive elastomer composition having excellent ink affinity and flexographic resin plate containing photosensitive elastomer composition

Examples

  • Experimental program(12)
  • Comparison scheme(3)

Example Embodiment

[0044] Example 1:
[0045] The invention discloses a flexible resin plate with excellent ink affinity, including a top-down protective layer, an anti-sticking composite film or a laser ablated black film, a photosensitive elastomer, an adhesive film, and a support.
[0046] (1) Photosensitive elastomer composition:
[0047] The thermoplastic elastomer (A) is styrene-butadiene-styrene triblock copolymer D1102 (SBS), Kraton Company, 500 parts.
[0048] Polyolefin plasticizer (B) is liquid polybutadiene L-PB, Yanshan Jilian Petrochemical Company, 130 parts.
[0049] The liquid polybutadiene grafted with a hydrophilic group (C) is liquid hydroxyl-terminated polybutadiene HTPB I, Shandong Qilong Chemical Company, 40 parts.
[0050] Unsaturated double bond monomer (D) is 1,6-hexanediol dimethacrylate (HDDA), Tianjin Tianjiao Chemical Co., Ltd., 60 parts; Tripropylene glycol diacrylate (TPGDA), Hubei Jusheng Technology Limited company, 30 copies.
[0051] The photoinitiator (E) is 1-hydroxycyclohexyl phenyl ketone (IRGACURE 184), BASF, 10 parts; benzophenone, Nantong Yike Chemical Company, 5 parts.
[0052] Auxiliary (F) is anti-aging agent 2,6-di-tert-butyl-p-cresol (commonly known as 264), Nanjing Hualiming Technology Industry and Trade Co., Ltd., 1 copy.
[0053] (2) Plate production:
[0054] The elastomer composition is added to a high-speed mixing extruder in proportion, and heated and melted at a high temperature. The photosensitive elastomer is hot-pressed at 100°C using a twin-screw extruder on the adhesive film coated 175 Micron or 100 microns thick PET support layer (produced by Lucky Group), while the other side is covered with a PET peelable protective layer with anti-sticking composite film (produced by Lucky Group) to produce conventional flexible resin plates. Or covered with a PET peelable protective layer with laser ablation black film (produced by Lucky Group) to make a digital flexible resin plate.

Example Embodiment

[0055] Example 2:
[0056] The invention discloses a flexible resin plate with excellent ink affinity, including a top-down protective layer, an anti-sticking composite film or a laser ablated black film, a photosensitive elastomer, an adhesive film, and a support.
[0057] (1) Components of photosensitive elastomer:
[0058] The thermoplastic elastomer (A) is styrene-butadiene-styrene triblock copolymer D1102 (SBS), Kraton Company, 500 parts.
[0059] Polyolefin plasticizer (B) is liquid polybutadiene L-PB, Yanshan Jilian Petrochemical Company, 130 parts.
[0060] The liquid polybutadiene grafted with hydrophilic groups (C) is liquid carboxyl-terminated polybutadiene CTPB I, Shandong Qilong Chemical Co., Ltd., 40 parts.
[0061] Unsaturated double bond monomer (D) is 1,6-hexanediol dimethacrylate (HDDA), Tianjin Tianjiao Chemical Co., Ltd., 60 parts; Tripropylene glycol diacrylate (TPGDA), Hubei Jusheng Technology Limited company, 30 copies.
[0062] The photoinitiator (E) is 1-hydroxycyclohexyl phenyl ketone (IRGACURE 184), BASF, 10 parts; benzophenone, Nantong Yike Chemical Company, 5 parts.
[0063] Auxiliary (F) is anti-aging agent 2,6-di-tert-butyl-p-cresol (commonly known as 264), Nanjing Hualiming Technology Industry and Trade Co., Ltd., 1 copy.
[0064] (2) Plate production:
[0065] The elastomer composition is added to a high-speed mixing extruder in proportion, and heated and melted at a high temperature. The photosensitive elastomer is hot-pressed at 100°C using a twin-screw extruder on the adhesive film coated 175 Micron or 100 microns thick PET support layer (produced by Lucky Group), while the other side is covered with a PET peelable protective layer with anti-sticking composite film (produced by Lucky Group) to produce conventional flexible resin plates. Or covered with a PET peelable protective layer with laser ablation black film (produced by Lucky Group) to make a digital flexible resin plate.

Example Embodiment

[0066] Example 3:
[0067] The invention discloses a flexible resin plate with excellent ink affinity, including a top-down protective layer, an anti-sticking composite film or a laser ablated black film, a photosensitive elastomer, an adhesive film, and a support.
[0068] (1) Components of photosensitive elastomer:
[0069] The thermoplastic elastomer (A) is styrene-butadiene-styrene triblock copolymer D1102 (SBS), Kraton Company, 500 parts.
[0070] Polyolefin plasticizer (B) is liquid polybutadiene L-PB, Yanshan Jilian Petrochemical Company, 130 parts.
[0071] Liquid polybutadiene grafted with hydrophilic groups (C) is liquid amino-terminated polybutadiene, Lucky Group, 40 parts.
[0072] Unsaturated double bond monomer (D) is 1,6-hexanediol dimethacrylate (HDDA), Tianjin Tianjiao Chemical Co., Ltd., 60 parts; Tripropylene glycol diacrylate (TPGDA), Hubei Jusheng Technology Limited company, 30 copies.
[0073] The photoinitiator (E) is 1-hydroxycyclohexyl phenyl ketone (IRGACURE 184), BASF, 10 parts; benzophenone, Nantong Yike Chemical Company, 5 parts.
[0074] Auxiliary (F) is anti-aging agent 2,6-di-tert-butyl-p-cresol (commonly known as 264), Nanjing Hualiming Technology Industry and Trade Co., Ltd., 1 copy.
[0075] (2) Plate production:
[0076] The elastomer composition is added to a high-speed mixing extruder in proportion, and heated and melted at a high temperature. The photosensitive elastomer is hot-pressed at 100°C using a twin-screw extruder on the adhesive film coated 175 Micron or 100 microns thick PET support layer (produced by Lucky Group), while the other side is covered with a PET peelable protective layer with anti-sticking composite film (produced by Lucky Group) to produce conventional flexible resin plates. Or covered with a PET peelable protective layer with laser ablation black film (produced by Lucky Group) to make a digital flexible resin plate.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

no PUM

Description & Claims & Application Information

We can also present the details of the Description, Claims and Application information to help users get a comprehensive understanding of the technical details of the patent, such as background art, summary of invention, brief description of drawings, description of embodiments, and other original content. On the other hand, users can also determine the specific scope of protection of the technology through the list of claims; as well as understand the changes in the life cycle of the technology with the presentation of the patent timeline. Login to view more.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Similar technology patents

Classification and recommendation of technical efficacy words

Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products