A kind of anti-HIC pipeline steel and its preparation method based on tissue regulation
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A pipeline and tissue technology, applied in the field of anti-HIC pipeline steel and its preparation based on tissue regulation, can solve the problems of increased wall thickness of steel pipelines, low alloy strength, and increased difficulty in manufacturing hydrogen pipelines, achieving refinement Effects of crystal grains, high-strength comprehensive performance, and high HIC resistance
Active Publication Date: 2021-06-29
FOSHAN UNIVERSITY +3
View PDF9 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
CN102839326B provides a kind of alloy with low carbon content, through controlled rolling and air-cooling process, relatively fine ferrite structure is obtained, HIC resistance performance is improved, but the alloy strength is low, the resistance strength is 437MPa, it is difficult to meet the requirements of high strength, good toughness, Comprehensive properties such as hydrogen-induced cracking resistance
The increasingly large and high-pressure requirements of hydrogen pipelines make the wall thickness of steel pipelines continue to increase, which further increases the difficulty of manufacturing such hydrogen pipelines.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0055]This example provides a kind of anti-HIC pipeline steel based on tissue regulation, including the following components in mass percentage:
[0056] C: 0.01-0.1%, Mn: 0.50-1.00%, Nb: 0.01-0.10%, Cr: 1.0-1.5%, Mo: 0.5-1.5%, V: 0.05-0.20%, B: 0.05-0.10%, N : 0.01 to 0.02%, Zr: 0.01 to 0.2%, and the balance is Fe.
[0057] Wherein, the S content is less than 0.01%, and the P content is less than 0.01%.
Embodiment 2
[0059] This example provides a method for preparing steel for anti-HIC pipelines based on tissue regulation, including the following steps:
[0060] S1: Weighing the C, Mn, Nb, Cr, Mo, V, B, N, Zr and Fe according to the proportion, and continuous casting after melting to obtain a billet;
[0061] S2: subjecting the billet obtained in step S1 to controlled rolling and controlled cooling treatment to obtain the HIC-resistant pipeline steel based on microstructure control.
[0062] Among them, controlled rolling and controlled cooling include rough rolling, finishing rolling and water cooling in sequence. The starting temperature of rough rolling is 1070°C, and the reduction ratio of a single pass is greater than 15%. The thickness of the intermediate slab for finishing rolling is 60mm. The start rolling temperature of finish rolling is 900°C. The water inlet temperature of the water cooling process is 780°C, the cooling rate is 13°C / s, and the final cooling temperature is 62...
Embodiment 3
[0064] In this example, using the preparation method of Example 2, referring to the formula of Example 1, a kind of anti-HIC pipeline steel based on tissue regulation is prepared, which specifically includes the following components in mass percentage:
[0065] C: 0.1%, Mn: 0.80%, Nb: 0.05%, Cr: 1.5%, Mo: 0.6%, V: 0.06%, B: 0.05%, N: 0.015%, Zr: 0.15%, the balance is Fe and impurity elements.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention provides a steel for anti-HIC pipelines based on tissue regulation and a preparation method thereof. The steel for anti-HIC pipelines based on tissue regulation has strong anti-HIC ability, and the HIC sensitivity indexes are all 0. B, N, V, Zr and other trace elements, designed (V, B) N and (Nb, B) x N is a highly stable high-temperature second phase, which can effectively refine the grains in the process of controlled rolling and controlled cooling, and reduce the grain size to about 1 μm. By regulating the uniform distribution of Mo elements, high HIC resistance and high Comprehensive performance of strength.
Description
technical field [0001] The invention belongs to the field of steel preparation, and in particular relates to a steel for anti-HIC pipelines based on tissue regulation and a preparation method thereof. Background technique [0002] Pipeline network construction is a strategic requirement. Natural gas pipeline transportation has the characteristics of high efficiency, economy and safety, and is the main form of long-distance gas transportation. With the gradual changes in the international energy structure, the proportion of natural gas in energy will increase dramatically in the next few decades. The development of natural gas pipelines tends to be large-diameter, high-pressure and thick-walled. The service conditions of pipelines are becoming more and more stringent, such as the increase of transmission pressure, complex transmission medium, and many pipelines need to pass through densely populated areas or deserts, swamps and severe cold regions, etc., which put forward h...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More