A preparation method of a long-life, low-cost soldering iron tip

A low-cost, soldering iron tip technology, applied in the field of ferrous metal alloys, can solve problems that plague the development of soldering iron tips, high production costs of soldering iron tips, and influence on the quality of soldering iron tips

Active Publication Date: 2021-07-06
SIRUI ADVANCED COPPER ALLOY CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the method of producing long-life soldering iron tips at home and abroad is to process the copper rod into a copper substrate, and then go through the processes of iron plating, nickel plating, and chrome plating (working surface) in turn to prepare the finished soldering iron tip. It has good mechanical strength and tin corrosion resistance. Nickel plating and chromium plating can be used as an additional protective layer, which can make the iron coating more compact and prevent the infiltration of tin on the surface. The quality of the soldering iron tip has a direct impact
The production cost of soldering iron tip is high, and the quality is unstable, which has become a problem that plagues the development of the soldering iron tip industry

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A preparation method of a long-life, low-cost soldering iron tip
  • A preparation method of a long-life, low-cost soldering iron tip
  • A preparation method of a long-life, low-cost soldering iron tip

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A method for preparing a long-life, low-cost soldering iron tip: comprising the following steps:

[0026] S1: Ingredients: prepare the raw material CuFe master alloy, the mass ratio of Cu and Fe in the CuFe master alloy is 1:1, the size of the electrolytic copper plate is 0.2m*0.1m*0.05m, and the size of the CuFe master alloy is 0.1m*0.1 m*0.02m, control the mass percentage of Fe element in the raw material at 50%, too large metal volume is not conducive to controlling the content of Fe in the ingredients, and too small metal volume is easy to oxidize the metal;

[0027] S2: Vacuum smelting: Put the raw materials prepared in S1 into a vacuum induction furnace, and vacuumize the vacuum induction furnace. When the vacuum degree in the vacuum induction furnace reaches р=4Pa, start heating and adjust the vacuum The power of the induction furnace is 20KW, continue heating for 10 minutes, then increase the power of the vacuum induction furnace to 40KW, continue heating for 10...

Embodiment 2

[0033] A method for preparing a long-life, low-cost soldering iron tip: comprising the following steps:

[0034] S1: Ingredients: Prepare the raw material electrolytic copper plate and CuFe master alloy. The mass ratio of Cu and Fe in the CuFe master alloy is 1:1. During the batching, the mass percentage of Fe element in the raw material is controlled at 40%, and the electrolytic copper plate The size is 0.2m*0.1m*0.05m, and the CuFe master alloy size is 0.1m*0.1m*0.02m. Too large a metal volume is not conducive to controlling the content of Fe in the ingredients, and too small a metal volume is easy to oxidize the metal;

[0035]S2: Vacuum smelting: Put the raw materials prepared in S1 into a vacuum induction furnace, and vacuumize the vacuum induction furnace. When the vacuum degree in the vacuum induction furnace reaches р=3Pa, start heating and adjust the vacuum The power of the induction furnace is 25KW, continue heating for 8 minutes, then increase the power of the vacuu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a long-life and low-cost soldering iron tip, including S1: batching, S2: vacuum melting, S3: casting, S4: hot forging, turning the outer circle, S5: drawing and intermediate annealing, S6: Machining, the soldering iron tip prepared by the present invention is prepared by the CuFe alloy material, has long service life, strong corrosion resistance, low production cost, and can control the heat conduction of the soldering iron tip by adjusting the ratio of copper and iron content Efficiency, more widely used occasions.

Description

technical field [0001] The invention relates to the technical field of ferrous metal alloys, in particular to a method for preparing a long-life and low-cost soldering iron tip. Background technique [0002] With the rapid development of the modern electronic industry, soldering technology has also been developed rapidly. In recent years, soldering technology mostly uses lead-free solder with high working temperature, and the soldering process requires that the soldering iron tip can be continuous and long-term. time to work. Therefore, higher requirements are put forward for the high temperature resistance, oxidation resistance and corrosion resistance of the soldering iron tip material. At present, the method of producing long-life soldering iron tips at home and abroad is to process the copper rod into a copper substrate, and then go through the processes of iron plating, nickel plating, and chrome plating (working surface) in turn to prepare the finished soldering iron ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23P15/00B23K3/02
CPCB23K3/02B23P15/00
Inventor 周斌苟锁郭创立孙君鹏王群刘向东王沛梁建斌张青队
Owner SIRUI ADVANCED COPPER ALLOY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com