A method for preparing cadmium telluride or cadmium zinc telluride polycrystalline material

A technology of cadmium zinc telluride and cadmium telluride, which is applied in the growth of polycrystalline materials, chemical instruments and methods, single crystal growth, etc., can solve the problems of quartz crucible container explosion, material oxidation and scrapping, equipment damage and economics, etc., to prevent volatilization Loss, reduction of equipment cost, and reduction of transient response

Active Publication Date: 2020-12-22
中科宏芯(常州)传感科技有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the preparation process of cadmium telluride and cadmium zinc telluride materials, the successful synthesis of polycrystalline materials of cadmium telluride and cadmium zinc telluride by simple substance of tellurium, simple substance of cadmium and simple substance of zinc is the key technology. Usually, the method of vacuum sintering and sealing of quartz crucible is adopted. After the synthesis is completed The quartz crucible needs to be broken open to take out the crystal ingot inside, and a quartz crucible needs to be lost every time it is synthesized, and the cost is high; When it is large, the explosion of the quartz crucible container often occurs, resulting in material oxidation and scrapping and equipment damage, resulting in great economic losses

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing cadmium telluride or cadmium zinc telluride polycrystalline material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Example 1: Prepare 100 kg of CdTe crystal material.

[0033] Preparation process:

[0034] 1) The first crucible 1, the second crucible 2, and the first cover 3 are made of quartz; the first crucible 1 has an annular groove 11 along the outer peripheral wall, the inner diameter of the lower part of the first crucible 1 is 300 mm, the inner diameter of the upper part is 322 mm, and the wall thickness 5mm, length 800mm; the width of annular groove 11 is 18mm, the wall thickness is 2.5mm, and the depth is 15mm; the upper part of the second crucible 2 is cylindrical, and the lower part is funnel-shaped. 4 The total length is 100 mm, the wall thickness is 3 mm, and the inner diameter of the tail end of the thin tube 4 is 8 mm; the top of the first cover 3 is closed, the bottom is open and the side wall can be inserted into the annular groove 11, the inner diameter of the first cover 3 is 336 mm, the wall thickness is 2.5 mm, The length is 30 mm; the first crucible 1, the se...

Embodiment 2

[0045] Embodiment 2: prepare 6kg Cd 0.96 Zn 0.04 Te crystal material.

[0046] Preparation process:

[0047] 1) The first crucible 1, the second crucible 2, and the first cover 3 are made of quartz; the first crucible 1 has an annular groove 11 along the outer peripheral wall, the inner diameter of the lower part of the first crucible 1 is 90 mm, the inner diameter of the upper part is 112 mm, and the wall thickness 3mm, length 800mm; the width of the annular groove 11 is 18mm, the wall thickness is 2.5mm, and the depth is 15mm; the upper part of the second crucible 2 is cylindrical, and the lower part is funnel-shaped. The total length of the tube 4 is 100 mm, the wall thickness is 2.5 mm, and the internal diameter of the tail end of the thin tube 4 is 1 mm; the top of the first cover 3 is closed, the bottom is open and the side wall can be inserted into the annular groove 11, the internal diameter of the first cover 3 is 336 mm, and the wall thickness is 2.5 mm. mm, lengt...

Embodiment 3

[0058] Embodiment 3: prepare 6kg Cd 0.9 Zn 0.1 Te crystal material.

[0059] Preparation process:

[0060] 1) The first crucible 1, the second crucible 2, and the first cover 3 are made of quartz; the first crucible 1 has an annular groove 11 along the outer peripheral wall, the inner diameter of the lower part of the first crucible 1 is 90 mm, the inner diameter of the upper part is 112 mm, and the wall thickness 3mm, 800mm in length, the width of the annular groove 11 is 18mm, the wall thickness is 2.5mm, and the depth is 15mm. The upper part of the second crucible 2 is cylindrical, and the lower part is funnel-shaped. The outer diameter of the cylindrical tube is 110 mm, the length is 150 mm, the total length of the funnel and the thin tube 4 is 100 mm, the wall thickness is 2.5 mm, and the inner diameter of the tail end of the thin tube 4 is 2 mm; The top of the cover 3 is closed, the bottom is open, and the side wall can be inserted into the annular groove 11. The inne...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of cadmium telluride or cadmium zinc telluride polycrystalline material, which is characterized in that it comprises the following preparation process: 1) a first crucible, a second crucible capable of being loaded into the first crucible, and a first crucible are covered The first cover of a crucible is cleaned and dried; wherein, the first crucible has an annular groove along the peripheral wall; the top of the first cover is closed, the bottom is open, and the side wall can be inserted into the annular groove; the bottom of the second crucible is provided with holes ; 2) Weighing elemental tellurium and elemental cadmium according to the matching ratio to form cadmium telluride; or weighing elemental tellurium, elemental cadmium, and elemental zinc according to the matching ratio to form cadmium telluride. The preparation method of the present invention adopts the liquid seal technology to prevent the volatilization loss of cadmium vapor, and the first crucible can be used repeatedly, thereby reducing the cost; by reducing the instantaneous reaction amount of tellurium and cadmium, the intensity of the combined reaction of tellurium and cadmium is reduced , reducing the withstand voltage requirements for synthesis equipment and reducing equipment costs.

Description

technical field [0001] The invention belongs to the field of preparation of crystal materials, in particular to a method for synthesizing cadmium telluride (CdTe) or cadmium zinc telluride (CdTe) 1- x Zn x Te) new method for polycrystalline materials. Background technique [0002] CdTe and CdZnTe crystals are the preferred substrate materials for making HgCdTe infrared focal plane detectors, and ideal semiconductor materials for making nuclear radiation detectors. In addition, CdTe and CdZnTe crystals are used in the preparation of Thin-film solar cells, infrared windows, light modulators, etc. also have broad applications. [0003] In the preparation process of cadmium telluride and cadmium zinc telluride materials, the successful synthesis of polycrystalline materials of cadmium telluride and cadmium zinc telluride by simple substance of tellurium, simple substance of cadmium and simple substance of zinc is the key technology. Usually, the method of vacuum sintering and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C30B28/06C30B29/48
CPCC30B28/06C30B29/48
Inventor 孙士文
Owner 中科宏芯(常州)传感科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com