Composite filter membrane, preparation method thereof and industrial wastewater treatment method

A composite filtration, industrial wastewater technology, applied in water/sewage treatment, biological water/sewage treatment, water/sewage multi-stage treatment, etc. It can achieve the effect of excellent protein adsorption function, increase thermal stability performance, and improve dispersibility and stability.

Active Publication Date: 2020-12-04
浙江环之美环保科技有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the production scale of this preparation method is small, and the filtration performance and ad

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite filter membrane, preparation method thereof and industrial wastewater treatment method
  • Composite filter membrane, preparation method thereof and industrial wastewater treatment method
  • Composite filter membrane, preparation method thereof and industrial wastewater treatment method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0040] The invention provides a kind of preparation method of composite filter membrane, comprises the steps:

[0041] S1. Uniformly disperse cellulose nanocrystals in sodium periodate solution, react at 45-55°C for 1.5-2.5 hours, add ethanol, and perform dialysis to obtain oxidatively modified cellulose nanocrystals; Disperse the element nanocrystals in DMF to obtain the first dispersion liquid, disperse ethylenediaminetetraacetic acid dianhydride in DMF to obtain the second dispersion liquid, and slowly drop the second dispersion liquid at 70-80°C under the protection of nitrogen into the first dispersion liquid, stirred and reacted for 42 to 54 hours, centrifuged, washed, and freeze-dried to obtain cellulose nanocrystals modified by formylation and carboxylation;

[0042] S2. Mix the modified cellulose nanocrystals prepared in step S1 and the thermoplastic polymer in a predetermined ratio and uniformly melt and granulate to obtain a blended masterbatch; perform a two-compon...

Embodiment 1

[0055] Embodiment 1 of the present invention provides a kind of preparation method of composite filter membrane:

[0056] S1. Uniformly disperse 1g of cellulose nanocrystals (CNC) in 100ml of sodium periodate solution (sodium periodate content is 1g), ultrasonically disperse for 10min, react at 40°C for 2h, and add 20ml of ethanol to terminate the reaction. Then put the suspension into a dialysis bag with a molecular weight cut-off of 1000, and dialyze it with a large amount of deionized water for 2 days until the pH value of the suspension is neutral, and obtain aldehyde-modified cellulose nanocrystals;

[0057] Disperse the aldehyde-modified cellulose nanocrystals in 50mlDMF and ultrasonically disperse for 10min to obtain the first dispersion, disperse ethylenediaminetetraacetic dianhydride in 50mlDMF and ultrasonically disperse for 5min to obtain the second dispersion, wherein , the molar ratio of ethylenediaminetetraacetic dianhydride to the hydroxyl groups on the surface ...

Embodiment 2-3

[0079] The difference with Example 1 is: in step S1, cellulose nanocrystal (CNC) and sodium periodate (NaIO 4 ) The mass ratio setting is different, and other steps are all the same as in Example 1, and are not repeated here.

[0080] Table 1 is the parameter setting in embodiment 1-3 and comparative example 1

[0081] Example CNC and NaIO 4 mass ratio

Example 1 1：1 Example 2 1：0.5 Example 3 1：1.5

[0082] With the increase of the mass ratio of cellulose nanocrystals (CNC) to sodium periodate (NaIO4), the content of aldehyde groups in cellulose nanocrystals gradually increases, but the yield of aldylated cellulose nanocrystals will appear This is mainly due to the fact that sodium periodate oxidizes the hydroxyl groups on the cellulose nanocrystals to aldehyde groups, and at the same time, the strong oxidative properties will also cause the oxidative degradation of a part of the cellulose nanocrystals. High, the phenomenon that the yield...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Membrane pore sizeaaaaaaaaaa
Thicknessaaaaaaaaaa
Breaking strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a composite filter membrane, a preparation method thereof and an industrial wastewater treatment method. The preparation method comprises the following steps: firstly, carryingout carboxylation and formylation modification treatment on cellulose nanocrystals; then blending, melting and granulating the modified cellulose nanocrystals and a thermoplastic polymer to obtain blended master batches, and carrying out double-component melt spinning, drafting, reinforcing and splitting post-treatment on the blended master batches and polyvinylidene fluoride to obtain a compositenon-woven fabric base layer; then carrying out melt blending on polyvinylidene fluoride and the modified cellulose nanocrystals to obtain a blended material, preparing composite nanofibers by adopting a melt blending extrusion phase separation method, and dispersing the composite nanofibers into a solution to obtain a composite nanofiber suspension; and finally, immersing the composite non-wovenfabric base layer in the composite nanofiber suspension, and carrying out freeze drying to obtain the composite filter membrane with excellent filtering performance, pollutant adsorption performance and mechanical strength. By adopting an electrocoagulation microfiltration microbiological treatment combined process, the method has an efficient treatment effect on industrial wastewater.

Description

technical field [0001] The invention relates to the field of filter membrane preparation, and also to the technical field of industrial wastewater treatment, in particular to a composite filter membrane, a preparation method thereof, and an industrial wastewater treatment method. Background technique [0002] With the continuous acceleration of the industrialization process, the pollution of industrial wastewater is becoming more and more prominent. The presence of a large number of pollutants such as viruses and microorganisms and heavy metal ions in industrial wastewater can enter the human body through food chain enrichment and drinking, causing serious damage to human health. serious hazard. As people pay more and more attention to water resources, the filtration and separation of drinking water and industrial water has received more and more attention. Facing the increasingly serious shortage of water resources, traditional wastewater treatment membrane separation mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C02F9/14B01D71/82B01D69/12B01D67/00B01D61/14
CPCB01D61/147B01D67/0002B01D69/12B01D71/82C02F1/444C02F1/463C02F3/34C02F9/00
Inventor 杨雯雯李桂云
Owner 浙江环之美环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap