Radiation wire drawing process for notebook computer aluminum shell
A notebook and aluminum casing technology, applied in the field of notebook aluminum casing processing technology, can solve the problem of single appearance and achieve the effects of beautifying the appearance and improving mechanical properties
Active Publication Date: 2020-12-11
昆山鼎国精密模具有限公司
View PDF8 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
In the prior art, the aluminum case of the notebook has a single appearance and only undergoes one wire drawing operation
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0017] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention.
[0018] In this embodiment, a kind of radial wire drawing process for notebook aluminum casing comprises the following steps:
[0019] S1. Selecting an aluminum plate to stamp and form the aluminum shell 4, and then polishing the surface of the aluminum shell 4;
[0020] S2. The polished aluminum shell 1 is fixedly placed on the lower mold 1 of the wire drawing machine through the jig 2, and the lower mold 1 rotates evenly under the drive of the first driving source, and the first driving source is a servo motor;
[0021] S3. When the lower die 1 evenly drives the aluminum shell 4 to rotate, the upper die 3 is driven by the second driving source and the wire drawing h...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention relates to the technical field of notebook aluminum shell machining processes, in particular to a radiation wire drawing process for a notebook computer aluminum shell. The radiation wire drawing process solves the defects in the prior art, and comprises the following steps of S1, selecting an aluminum plate, stamping the aluminum plate to manufacture an aluminum shell, and then polishing a surface layer of the aluminum shell; S2, fixedly placing the polished aluminum shell on a lower die of a wire drawing machine through a jig, and enabling the lower die to be driven by a firstdriving source to evenly rotate; S3, enabling an upper die to be driven by a second driving source to drive a wire drawing head to do parabolic motion to perform wire drawing treatment on a surface layer of the aluminum shell to form radial patterns; S4, after wire drawing is completed, enabling the base body surface to be cleaned and roughened through the high-speed sand flow impact effect; and S5, after sand blasting treatment, taking out the aluminum shell for anodic oxidation treatment, and obtaining a finished product. The lower die drives the aluminum shell to uniformly rotate, and is matched with the upper die to drive the wire drawing head to perform parabolic action, so that the radial patterns are formed on the surface of the aluminum shell, and the appearance of the notebook computer aluminum shell is beautified.
Description
technical field [0001] The invention relates to the technical field of notebook aluminum shell processing technology, in particular to a radial wire drawing process for the notebook aluminum shell. Background technique [0002] Surface brushing treatment is a surface treatment method that forms lines on the surface of the workpiece by grinding products to achieve a decorative effect. Because the brushed surface treatment can reflect the texture of metal materials, it has been loved by more and more users and has become more and more widely used. In the prior art, the aluminum casing of the notebook has a single appearance and only undergoes one wire drawing operation. Contents of the invention [0003] The object of the present invention is to solve the shortcomings in the prior art, and propose a radial drawing process for notebook aluminum casings. [0004] In order to achieve the above object, the present invention adopts the following technical solutions: [0005] A...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): B24B1/00B24C1/08
CPCB24B1/00B24C1/08
Inventor 凌磊
Owner 昆山鼎国精密模具有限公司