Aluminum ingot casting method based on waste aluminum materials

An aluminum and waste technology, applied in the field of aluminum ingot casting based on waste aluminum, can solve the problems of environmental damage, low recycling efficiency, complicated procedures, etc., and achieve the effect of improving quality

Inactive Publication Date: 2020-12-11
阿坝铝厂
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the content of aluminum in nature is relatively high, it is a non-renewable element after all, and the mining of aluminum in nature is not only complicated, but also causes damage and pollution to the environment
Relatively speaking, there is a large amount of scrap aluminum every year, which is another considerable amount of aluminum resources. However, the current recycling efficiency of scrap aluminum is not high, which undoubtedly causes a lot of waste of aluminum resources, which is not conducive to improving The recycling rate of aluminum resources and the reduction of the production cost of aluminum resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aluminum ingot casting method based on waste aluminum materials
  • Aluminum ingot casting method based on waste aluminum materials
  • Aluminum ingot casting method based on waste aluminum materials

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0047] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0048] refer to figure 1 , is a schematic diagram of the overall flow of the aluminum ingot casting method based on waste aluminum materials provided by the present invention. The aluminum ingot casting method based on scrap aluminum comprises the following steps:

[0049] Step S1, aluminum material recycling process, the aluminum material recycling process is used to perform preliminary impurity removal processing, aluminum-containing material screening and colle...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an aluminum ingot casting method based on the waste aluminum materials. The waste aluminum materials can be accurately and fully classified, and therefore aluminum elements in different chemical forms can be recycled in a centralized mode to the maximum extent; in addition, targeted chemical reaction treatment can be conducted according to the chemical forms of the aluminumelements, so that an aluminum base alloy melt is obtained, and finally the aluminum base alloy melt is cured and formed in a two-time discrete casting mode to obtain an aluminum ingot with a double-layer structure; therefore, the internal structure of the aluminum ingot is optimized, strain cracks of the aluminum ingot in the casting process are avoided, and the quality of the aluminum ingot is improved to the maximum extent.

Description

technical field [0001] The invention relates to the technical field of aluminum ingot production technology, in particular to an aluminum ingot casting method based on scrap aluminum materials. Background technique [0002] Aluminum alloy is widely used in different occasions due to its light weight and high mechanical strength. At present, aluminum ingots are mainly used as raw materials for the production of aluminum alloys. Although the content of aluminum element in nature is relatively high, it is a non-renewable element after all, and the mining of aluminum element in nature is not only complicated, but also causes damage and pollution to the environment. Relatively speaking, there is a large amount of scrap aluminum every year, which is another considerable amount of aluminum resources. However, the current recycling efficiency of scrap aluminum is not high, which undoubtedly causes a lot of waste of aluminum resources, which is not conducive to improving The recycl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22B7/00C22B21/00C25C3/06B22D7/00
CPCC22B7/003C22B21/0092C25C3/06B22D7/005Y02P10/20
Inventor 黄建明李刚李秀成
Owner 阿坝铝厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products