A kind of positive electrode slurry of aqueous lithium iron phosphate battery and preparation method thereof

A technology for lithium iron phosphate battery and positive electrode slurry, which is applied in battery electrodes, electrode manufacturing, active material electrodes, etc. Material stability, not easy to crack, excellent performance of pole piece adhesion

Active Publication Date: 2021-06-29
江西安驰新能源科技有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] In summary, the current positive electrode slurry of water-based lithium iron phosphate batteries still has the following problems: 1. Poor stability of the slurry; 2. The electrode sheet cracks and loses powder during coating; 3. The flexibility of the positive electrode sheet is poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of positive electrode slurry of aqueous lithium iron phosphate battery and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A positive electrode slurry for an aqueous lithium iron phosphate battery, comprising a positive electrode active material, a conductive agent and a binding agent, the binding agent comprising a binding agent A and a binding agent B, by weight, the positive electrode active material: viscose Bonding agent A: binder B: conductive agent = 93:1:3:3;

[0044] The positive electrode active material is lithium iron phosphate; the main chain of the binder A is polyethylene glycol, and the branched chain is acrylate; the binder B is a copolymer of acrylic acid and acrylonitrile. Tougheners were also added to Binder B. The toughening agent is polymethyl methacrylate.

[0045]A method for preparing lithium iron phosphate, comprising: respectively providing a lithium source solution, a ferrous source solution, and a phosphorus source solution, wherein the lithium source solution, the ferrous source solution, and the phosphorus source solution are respectively a lithium source com...

Embodiment 2

[0056] Referring to Example 1, different from Example 1, the lithium source for preparing aqueous lithium iron phosphate comes from a mixture of lithium carbonate and lithium hydroxide; the weight ratio of lithium carbonate and lithium hydroxide is 70:30. Tougheners were also added to Binder B. The toughening agent is polypropylene butyl ester.

Embodiment 3

[0058] Referring to Example 1, different from Example 1, the lithium source for preparing aqueous lithium iron phosphate comes from a mixture of lithium carbonate and lithium hydroxide; the weight ratio of lithium carbonate and lithium hydroxide is 80:40. Tougheners were also added to Binder B. The toughening agent is a mixture of polymethyl methacrylate and polypropylene butyl.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a positive electrode slurry for an aqueous lithium iron phosphate battery and a preparation method thereof, wherein the positive electrode slurry includes a positive electrode active material, a conductive agent and a binder, and the binder includes a binder A and a binder B, by weight ratio, positive electrode active material: binder A: binder B: conductive agent=90-95: 1-3: 2-5: 2-5; the positive electrode active material is lithium iron phosphate; The main chain of the binder A is polyethylene glycol, and the branched chain is acrylate; the binder B is a copolymer of acrylic acid and acrylonitrile. The invention can improve the stability of the slurry, improve the flexibility of the pole piece, and solve the problem of cracking and powder dropping of the pole piece.

Description

technical field [0001] The invention relates to the field of lithium iron phosphate batteries, in particular to a positive electrode slurry for an aqueous lithium iron phosphate battery and a preparation method thereof. Background technique [0002] Lithium iron phosphate battery refers to a lithium ion battery that uses lithium iron phosphate as the positive electrode material. In the large-scale production of the lithium iron phosphate battery industry, an organic solvent-based binder system is generally used, and polyvinylidene fluoride (PVDF) with a crystallinity of 50% is used as the binder, and the highly polar compound NMP ( N-methylpyrrolidone) as a dispersing solvent. It has the following disadvantages: [0003] (1) Although the organic solvent NMP has good dispersibility, it is volatile, flammable, explosive, and highly toxic; the volatilization of the organic solvent seriously pollutes the environment, makes the production site highly toxic, and seriously affect...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/58H01M4/62H01M4/136H01M4/04H01M10/0525
CPCH01M4/0404H01M4/136H01M4/5825H01M4/622H01M4/624H01M10/0525H01M2004/028Y02E60/10
Inventor 郭娜娜何涛斌毛振强汪正兵张小溪
Owner 江西安驰新能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com