A kind of 3D printing cobalt-chromium alloy for dental porcelain restoration and preparation method thereof

A 3D printing, cobalt-chromium alloy technology, applied in the direction of dentures, additive manufacturing, additive processing, etc., can solve the problems of low elongation, high strength and hardness, and poor mechanical properties of restorations, and achieve the benefits of metal porcelain Combination, low cost, effect of reducing surface active energy

Active Publication Date: 2021-09-07
CHENGDU KENINGDA MATERIALS
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing 3D printed cobalt-chromium alloy porcelain restorations have the following problems in clinical application: (1) problems such as porcelain chipping and porcelain peeling; (2) the restorations after annealing generally have low elongation, strength and hardness Excessive problem, that is, the 3D printed cobalt-chromium alloy used in the prior art for dental porcelain restoration has poor bonding performance and poor mechanical properties

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of 3D printing cobalt-chromium alloy for dental porcelain restoration and preparation method thereof
  • A kind of 3D printing cobalt-chromium alloy for dental porcelain restoration and preparation method thereof
  • A kind of 3D printing cobalt-chromium alloy for dental porcelain restoration and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] The invention provides a method for preparing a 3D printed cobalt-chromium alloy for dental porcelain restoration, comprising the following steps:

[0037] A 3D printing method is used to make a cobalt-chromium porcelain restoration on the substrate, and the cobalt-chromium porcelain restoration includes the following chemical composition in weight percentage: Cr 30-35%, W 4-9%, Mo 4-9%, Si 0.5-2.0%, Ta 5-10%, Nb 0.5-2.0%, the balance of Co and unavoidable impurities, the mass content of the impurities is less than 0.5%;

[0038] The cobalt-chromium porcelain restoration and the substrate are sequentially subjected to vacuum stress-relief annealing and support removal to obtain a cobalt-chromium alloy after stress-relief annealing;

[0039] In a protective atmosphere, the cobalt-chromium alloy after the stress relief annealing is sequentially subjected to solution treatment and aging treatment to obtain the 3D printed cobalt-chromium alloy for dental porcelain restorati...

Embodiment 1

[0062] In this example, the chemical composition of a 3D printed cobalt-chromium alloy for dental porcelain restoration and the weight percentages of each element are: Cr 30.0%, W 5.0%, Mo 5.0%, Si 1.0%, Ta 8.0%, Nb 1.5% , the balance is Co and impurities, and the weight percentage of impurities is less than 0.5%. Carry out heat treatment to cobalt-chromium alloy, specifically comprise the following steps:

[0063] (1) Use laser selective melting (SLM) technology to make cobalt-chromium ceramic alloys with the above chemical composition, then put the formed cobalt-chromium alloy together with the substrate into a vacuum furnace, and first raise the temperature to 600 at a rate of 20°C / min. ℃, keep warm for 45min; then rise to 1100℃ at a rate of 30℃ / min, keep warm for 60min; then cool to room temperature at a rate of 15℃ / min.

[0064] (2) Cutting the cobalt-chromium ceramic alloy annealed in step (1) from the substrate, and removing the support.

[0065] (3) Put the cobalt-ch...

Embodiment 2

[0069] In this example, the chemical composition of a 3D printed cobalt-chromium alloy for dental porcelain restoration and the weight percentages of each element are: Cr 32.0%, W 6.0%, Mo 7.0%, Si 1.5%, Ta 5.0%, Nb 0.5% , the balance is Co and impurities, and the weight percentage of impurities is less than 0.5%. Carry out heat treatment to cobalt-chromium alloy, specifically comprise the following steps:

[0070] (1) Use laser selective melting (SLM) technology to make cobalt-chromium ceramic alloys with the above chemical composition, then put the formed cobalt-chromium alloy together with the substrate into a vacuum furnace, and first raise the temperature to 550 at a rate of 25°C / min. ℃, keep warm for 50min; then raise the temperature to 1150℃ at a rate of 25℃ / min, keep warm for 70min; then cool to room temperature at a rate of 5℃ / min.

[0071] (2) Cutting the cobalt-chromium ceramic alloy annealed in step (1) from the substrate, and removing the support.

[0072] (3) P...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention provides a 3D printed cobalt-chromium alloy for dental porcelain restoration and a preparation method thereof, belonging to the field of dental porcelain restoration. The present invention adds Ta element, reduces thermal expansion coefficient, improves metal-ceramic bonding strength, reduces surface active energy, causes solid solution strengthening, improves strength; increases Cr element content, reduces Co element content, increases hcp phase content, is beneficial to metal-ceramic bonding, After the Co element is reduced, the combination of Cr-W, Cr-Mo, Cr-Si, W-Mo is improved, and the strength of the alloy is improved; the vacuum stress relief annealing is used to completely eliminate the residual stress, so that the cobalt-chromium restoration will not be used during service. The microstructure phase transformation will be caused by the residual stress, causing the formation of microcracks at the metal-ceramic bonding interface; solid solution and aging are used to adjust the phase composition of the cobalt-chromium alloy and the precipitation of the second phase, so that the alloy has good mechanical properties, and at the same time The hcp phase is further improved to improve the bonding strength of gold and porcelain.

Description

technical field [0001] The invention relates to the technical field of dental porcelain restoration, in particular to a 3D printed cobalt-chromium alloy for dental porcelain restoration and a preparation method thereof. Background technique [0002] 3D printing is a technology based on digital model files, using bondable materials such as powdered metal or plastic, to construct objects by layer-by-layer printing. It has rapid prototyping, short processing cycle, easy processing of personalized objects and Due to the characteristics of complex shape objects, it is especially suitable for the production of dental crowns and bridges in the field of dental porcelain restoration. In order to ensure the quality of 3D printing, 3D printing powder materials require: high purity, low oxygen content, good fluidity; high particle shape sphericity, fine particle size, and narrow distribution. For dental 3D printing alloy powder, it should also have good metal-ceramic bonding force, cor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/04C22C19/07B22F10/64B22F5/00B22F10/28B33Y10/00B33Y70/00B33Y40/20A61C13/083C22F1/02C22F1/10
CPCA61C13/083B22F3/24B22F5/00B22F2003/248B33Y10/00B33Y70/00B33Y40/20C22C1/0433C22C19/07C22F1/02C22F1/08C22F1/10
Inventor 李宁颜家振周亚男欧阳红川李锐张幖张玉鲜刘楠樊星云
Owner CHENGDU KENINGDA MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com