High-solid-content and low-viscosity polyaspartic acid ester primer-topcoat coating suitable for high-pressure airless spraying and preparation method thereof

An aspartic acid ester, high-pressure airless technology, applied in the field of coatings, can solve the problems of pinholes, fast reaction speed, short pot life, etc., and achieve the effect of long pot life, high salt spray resistance, and reduced winding

Active Publication Date: 2021-01-12
JIANGSU LANLING POLYMER MATERIAL CO LTD +1
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional polyaspartic ester coating, the main resin polyaspartic acid ester is secondary aminodiamine, the reaction speed is fast, the pot life is short, it is not suitable for conventional high-pressure airless spraying, only two-component suction pump can be used Graco spraying equipment with heating method is used; and due to the influence of factors such as moisture retention in the coating caused by high humidity in the coating manufacturing and construction environment, pinholes will appear after the coating film is dry. Phenomenon

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-solid-content and low-viscosity polyaspartic acid ester primer-topcoat coating suitable for high-pressure airless spraying and preparation method thereof
  • High-solid-content and low-viscosity polyaspartic acid ester primer-topcoat coating suitable for high-pressure airless spraying and preparation method thereof
  • High-solid-content and low-viscosity polyaspartic acid ester primer-topcoat coating suitable for high-pressure airless spraying and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0029] Example 1 According to the raw materials and proportions described in Table 2, add 8g of mixed solvent in the batching tank, add polyaspartic acid ester resin NH2850 10g, NH1520 8g, F520 6g, liquid polyester resin 670BA 14g, dispersant under stirring 0.4g, defoamer 0.3g, leveling agent 0.5g, dehydrating agent, low-speed stirring and dispersion for 5-10min, under the condition of stirring, add appropriate amount of TSC-2 titanate coupling agent to activate the polar group, about 30min. Then add 26g of pigment CR510 titanium dioxide, 12g of active anti-rust pigment APZ-99, 12.8g of superfine natural barium sulfate while stirring, stir at high speed for 20-30min, stand still for 30min, remove the moisture in the solvent and pigments and fillers; pump the materials into Sand mill with sand mill until the paint fineness is less than or equal to 45um, discharge the material, then add 1g of UV absorber and 1g of AD-802 matting agent, stir evenly, adjust the color, adjust the v...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-solid-content and low-viscosity polyaspartic acid ester primer-topcoat coating suitable for high-pressure airless spraying and a preparation method thereof. The high-solid-content low-viscosity polyaspartic acid ester primer-topcoat coating comprises the following components in percentage by mass: 30-40% of polyaspartic acid ester resin; 10%-20% of polyester resin;0.3%-1.5% of a dispersing agent; 0.3%-1.0% of a defoaming agent; 1%-3% of a dehydrating agent; 0.3%-0.8% of a leveling agent; 0.4%-1.5% of an anti-sagging agent; 1%-3.0% of an ultraviolet absorber; 34%-45% of pigment; 10%-25% of a filler; 6%-10% of a solvent; 20%-29% of curing agent. Conventional high-pressure airless spraying equipment can be adopted for construction, it is guaranteed that the mixed paint can be normally constructed after 30 min at the environment temperature of 30 DEG C, the surface of a paint film is leveled normally, the defects of pinholes, shrinkage cavities, bubbles andthe like are avoided, the weather resistance, gloss retention, color retention and weather resistance are excellent, the solid content is high, and the requirements of environment-friendly paint aremet; the one-time film forming thickness can reach 150-350mu m, the surface drying and hard drying time is fast, and the working life is long.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a high-solid-content, low-viscosity polyaspartate bottom-surface-in-one coating suitable for high-pressure airless spraying and a preparation method thereof. Background technique [0002] With the continuous and rapid development of my country's national economy and infrastructure, as well as the strengthening of environmental protection policies, the coatings used at this stage not only need to meet environmental protection requirements, but also need to have excellent weather resistance, good resistance to acid, alkali and salt corrosion It is not only durable and wear-resistant, but also has good construction and decoration. In this environment, many different types of environmentally friendly coatings are continuously introduced in the market. As an environmentally friendly coating, polyaspartic acid ester coating has high solid content, low VOC, high strength, high wear res...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/02C09D175/06C09D5/08C09D7/61C09D7/20
CPCC09D175/02C09D5/08C09D7/61C09D7/20C09D7/70C08L2205/02C08L75/06C08K7/24
Inventor 顾科毅陈建刚刘斌戎雪荣华忠梁马运立钟江兴唐松朱文凯吴端红
Owner JIANGSU LANLING POLYMER MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products