A kind of screen printing fluorescent shoe upper and its preparation process

A preparation process and a technology for shoe uppers, which are applied in the directions of shoe uppers, footwear, and shoe-making machinery, etc., can solve the problems of not being able to provide lighting functions and having no luminous effect.

Active Publication Date: 2022-05-06
福建省华昂体育用品有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But these beautiful designs and decorations do not have a luminous effect, especially in the dark and cannot provide a lighting function, which makes the shoes have a lot of room for improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of screen printing fluorescent shoe upper and its preparation process
  • A kind of screen printing fluorescent shoe upper and its preparation process
  • A kind of screen printing fluorescent shoe upper and its preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A silk screen fluorescent shoe upper, the fluorescent shoe upper is composed of a shoe upper and a fluorescent material, the material of the shoe upper is textile canvas and PU leather material, the main components of the fluorescent material are: vinyl resin and fluorescent powder, the characteristics of vinyl resin There are: yellow-brown viscous liquid, acid value 8-12MGKOH / G, viscosity 300-500MPAS / 25℃, gel time 6-22MIN / 25℃, thermal stability ≥ 24H / 80℃, heat distortion temperature 150-160 ℃, the phosphor adopts SRAI204:EU(2+).

[0035] Vinyl resin contains solid particles, the content of solid particles is 58-66%, the ratio of vinyl resin to phosphor is 1:1, solid particles are divided into small particles and medium particles, and the size of solid particles is 0.1-2mm .

[0036] Table 1: Specifications and stirring time of solid particles with different contents in Example 1

[0037]

Embodiment 2

[0039] A silk screen fluorescent shoe upper, the fluorescent shoe upper is composed of a shoe upper and a fluorescent material, the material of the shoe upper is textile canvas and PU leather material, the main components of the fluorescent material are: vinyl resin and fluorescent powder, the characteristics of vinyl resin There are: yellow-brown viscous liquid, acid value 8-12MGKOH / G, viscosity 300-500MPAS / 25℃, gel time 6-22MIN / 25℃, thermal stability ≥24H / 80℃, heat distortion temperature 150-160 ℃, the phosphor adopts SRAI204:EU(2+).

[0040]Vinyl resin contains solid particles, the content of solid particles is 58-66%, the ratio of vinyl resin to phosphor is 1:1, solid particles are divided into small particles and medium particles, and the size of solid particles is 0.1-2mm .

[0041] Table 2: Specifications and stirring time of solid particles with different contents in Example 2

[0042]

Embodiment 3

[0044] A silk screen fluorescent shoe upper, the fluorescent shoe upper is composed of a shoe upper and a fluorescent material, the material of the shoe upper is textile canvas and PU leather material, the main components of the fluorescent material are: vinyl resin and fluorescent powder, the characteristics of vinyl resin There are: yellow-brown viscous liquid, acid value 8-12MGKOH / G, viscosity 300-500MPAS / 25℃, gel time 6-22MIN / 25℃, thermal stability ≥ 24H / 80℃, heat distortion temperature 150-160 ℃, the phosphor adopts SRAI204:EU(2+).

[0045] Vinyl resin contains solid particles, the content of solid particles is 58-66%, the ratio of vinyl resin to phosphor is 1:1, solid particles are divided into small particles and medium particles, and the size of solid particles is 0.1-2mm .

[0046] Table 3: Specifications and stirring time of solid particles with different contents in Example 3

[0047]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
heat deflection temperatureaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a screen-printed fluorescent vamp and a preparation process thereof. The fluorescent vamp is composed of a vamp and a fluorescent material. The material of the vamp is textile canvas and PU leather. The main components of the fluorescent material are: Vinyl resin and fluorescent powder, the characteristics of the vinyl resin are: yellow-brown viscous liquid, acid value 8-12MGKOH / G, viscosity 300-500MPAS / 25°C, gel time 6-22MIN / 25°C, heat Stability ≥ 24H / 80℃, heat distortion temperature 150‑160℃. The screen-printed fluorescent shoe upper uses a special fluorescent liquid as a silk-screened material. By mixing vinyl resin with fluorescent powder, the vinyl resin contains solid particles. The content of solid particles is 58-66%, and the size of solid particles is 0.1-2mm. , not only makes the fluorescent upper more grainy, but also makes the vinyl resin and fluorescent powder more fully mixed.

Description

technical field [0001] The invention relates to the technical field of screen-printed fluorescent vamps, in particular to a screen-printed fluorescent vamp and a preparation process thereof. Background technique [0002] Since ancient times, people have learned to wrap their feet with some things, not only to protect their feet from being scratched by sharp stones, but also to keep warm from the cold; from the simplest animal skins and leaves to straw sandals, cloth shoes and then When it comes to leather shoes, it can be said that the development history of shoes is the evolution history of human civilization. In terms of industry competition, although China has made great progress in the production of footwear, it is still inferior to some developed countries. Because the functions of shoes are limited, they can only improve and develop from some novel functions and appearances. [0003] The appearance of existing shoes is constantly changing, and the material is also con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A43B23/02A43D8/22A43D95/10A43D95/08
CPCA43B23/0235A43D8/22A43D95/10A43D95/08
Inventor 杜丕皇方业永林拥护刘建国
Owner 福建省华昂体育用品有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap