A kind of preparation method of aluminum alloy material for flux-free gas shielded brazing

An aluminum alloy material, gas shielding technology, applied in welding/cutting medium/material, welding equipment, metal rolling, etc., can solve the problems of heat dissipation performance parameter influence, connection strength influence, etc., to improve milling efficiency and finished products. Quality, effect of accelerated foil rolling rate

Active Publication Date: 2022-07-19
镇江龙源铝业有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, when welding workpieces such as aluminum coils and plates made of aluminum alloy, the welding method of gas shielded brazing is often used, and a large amount of heat will be generated during the brazing process. High requirements, aluminum alloy materials that do not meet the corresponding heat dissipation performance parameters not only affect the connection strength after brazing but also affect the quality of the formed product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of aluminum alloy material for flux-free gas shielded brazing

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] The present invention will now be described in further detail with reference to the accompanying drawings. These drawings are all simplified schematic diagrams, and only illustrate the basic structure of the present invention in a schematic manner, so they only show the structures related to the present invention.

[0032] like figure 1 Shown is a preparation method of an aluminum alloy material for flux-free gas shielded brazing provided by the present application, comprising the following steps:

[0033] 1) Ingredients: prepare the raw materials for making gas shielded brazing materials according to the preset mass ratio, and record the corresponding mass ratio of each component selected in this batching;

[0034] 2) Casting: cast the prepared raw materials into castings;

[0035] 3) Milling surface: Rough milling and fine milling are performed on the surface of the casting to remove the burrs and particles attached to the surface of the casting:

[0036] 4) Hot ro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a preparation method of an aluminum alloy material for flux-free gas shielded brazing, which is characterized by comprising the following steps: 1) batching; 2) casting; 3) milling; 4) hot rolling; 5) Cold rolling; 6) One intermediate annealing; 7) Cold finishing rolling; 8) Two intermediate annealing; 9) Foil rolling; 10) Slitting; 11) Packaging; The rolling process of rolling ensures that the size of the product meets the requirements, and at the same time further improves its heat dissipation performance, so that the connection performance of the weldment can be effectively achieved in the process of gas shielded brazing, thereby ensuring the quality of brazing, thereby further improving the quality of the finished product; Transfer it into the stereo scanning workshop, generate a stereo actual model for each casting, and compare it with the preset stereo preset model inside the center console, so as to determine the subsequent milling process according to different comparison results, and further improve the milling process. Surface accuracy and milling efficiency.

Description

technical field [0001] The invention relates to the technical field of aluminum products, in particular to a preparation method of an aluminum alloy material for flux-free gas shielded brazing. Background technique [0002] Gas shielded brazing is the use of inert gas as a protective atmosphere to melt the low melting point metal at a certain temperature, and then connect the contacting metals with a high melting point during cooling and solidification, which is called gas shielded brazing. In the prior art, the welding method of gas shielded brazing is often used for the welding of aluminum coils and plates made of aluminum alloys, and a large amount of heat is generated during the brazing process. High requirements, aluminum alloy materials that do not meet the corresponding heat dissipation performance parameters not only affect the connection strength after brazing, but also affect the quality of products after forming. SUMMARY OF THE INVENTION [0003] In order to ov...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B21B1/22B23K35/28B23P15/00
CPCB23K35/286B23P15/00
Inventor 薛卫龙张龙陆健王学峰董福伟
Owner 镇江龙源铝业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap