Difunctional monomer double-imprinting-layer testosterone molecular imprinting magnetic nanosphere as well as preparation method and application thereof

A technology of bifunctional monomers and magnetic nanospheres, applied in separation methods, chemical instruments and methods, solid adsorbent liquid separation, etc., can solve the problem of low adsorption capacity of testosterone molecularly imprinted polymers, achieve good regeneration ability, basic Rich clusters and good structural stability

Active Publication Date: 2021-04-16
XI AN JIAOTONG UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the shortcomings of the above-mentioned prior art, the object of the present invention is to provide a bifunctional monomer double-imprinted layer testosterone molecularly imprinted magnetic nanosphere and its preparation method and application, so as to solve the problem of low adsorption capacity of testosterone molecularly imprinted polymers, Adsorption and removal of testosterone at the cellular level

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Difunctional monomer double-imprinting-layer testosterone molecular imprinting magnetic nanosphere as well as preparation method and application thereof
  • Difunctional monomer double-imprinting-layer testosterone molecular imprinting magnetic nanosphere as well as preparation method and application thereof
  • Difunctional monomer double-imprinting-layer testosterone molecular imprinting magnetic nanosphere as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The preparation method of the bifunctional monomer double imprinted layer testosterone molecularly imprinted magnetic nanosphere comprises the following steps:

[0033] Step 1. Put 100mg of magnetic nanoparticles modified by amphiphilic functional groups, 15mg of testosterone, and 30mL of alcohol-water mixture (1:9) in a reaction vessel to react for 30 minutes to form a carrier-template complex; then add 3mL of ammonia water, 100 μL of 3-aminopropyltriethoxysilane, 100 μL of phenyltrimethoxysilane and 2 mL of ethyl orthosilicate were reacted for 6 hours. After the reaction, the reaction product was washed with ultrapure water until it was neutral, and then heated at 30°C, 0.05 Dry at MPa for 3h;

[0034]Step 2: Elute the dried solid polymer in step 1 with a mixture of absolute ethanol and acetic acid at a volume ratio of 90:10, and wash the eluted solid polymer with ultrapure water until neutral. Then, the obtained product was dried at 30° C. and 0.05 MPa for 3 h to ob...

Embodiment 2

[0046] The preparation method of the bifunctional monomer double imprinted layer testosterone molecularly imprinted magnetic nanosphere comprises the following steps:

[0047] Step 1. Put 200mg of magnetic nanoparticles modified by amphiphilic functional groups, 25mg of testosterone, and 40mL of alcohol-water mixture (1:9) in a reaction vessel to react for 40min to form a carrier-template complex; then add 3.5mL of ammonia water , 150 μL of 3-aminopropyltriethoxysilane, 150 μL of phenyltrimethoxysilane and 2.5 mL of ethyl orthosilicate were reacted for 7 hours. After the reaction, the reaction product was washed with ultrapure water to neutrality, and then heated at 30 ° C , Dry at 0.05MPa for 3h;

[0048] Step 2: Elute the dried solid polymer in step 1 with a mixture of absolute ethanol and acetic acid with a volume ratio of 91:9, and wash the eluted solid polymer with ultrapure water until neutral. Then, the obtained product was dried at 30° C. and 0.05 MPa for 3 hours to o...

Embodiment 3

[0059] The preparation method of the bifunctional monomer double imprinted layer testosterone molecularly imprinted magnetic nanosphere comprises the following steps:

[0060] Step 1. Put 300mg of magnetic nanoparticles modified by amphiphilic functional groups, 35mg of testosterone, and 60mL of alcohol-water mixture (2:8) in a reaction vessel for 60 minutes to form a carrier-template complex; then add 4mL of ammonia water, 200 μL of 3-aminopropyltriethoxysilane, 200 μL of phenyltrimethoxysilane and 3 mL of ethyl orthosilicate were reacted for 8 hours. After the reaction, the reaction product was washed with ultrapure water to neutrality, and then heated at 30 ° C, 0.05 Dry at MPa for 3h;

[0061] Step 2: Elute the dried solid polymer in step 1 with a mixture of absolute ethanol and acetic acid with a volume ratio of 92:8, and wash the eluted solid polymer with ultrapure water until neutral. Then, the obtained product was dried at 30° C. and 0.05 MPa for 3 hours to obtain the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
adsorption capacityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a difunctional monomer testosterone molecularly imprinted magnetic nanosphere with double imprinted layers as well as a preparation method and application of the magnetic nanosphere, and belongs to the technical field of nano-material preparation and nano-medicine. Magnetic nanospheres modified by amphiphilic functional groups are used as carriers, testosterone is used as template molecules, 3aminopropyltriethoxysilane and phenyltrimethoxysilane are used as bifunctional monomers, and the bifunctional monomer double-imprinting-layer testosterone molecularly imprinted magnetic nanospheres are prepared by adopting a method of combining a two-step fixed template and surface imprinting. The difunctional monomer double-imprinting-layer testosterone molecularly imprinted magnetic nanospheres prepared by the method disclosed by the invention are uniform in particle size, good in structural stability, high in selectivity, rich in functional monomer groups and good in biological safety; and the method is a new method for preparing the testosterone molecularly imprinted polymer with high adsorption capacity and high selectivity, the testosterone in cells is removed through full adsorption, the efficiency of castration treatment of the prostate cancer can be remarkably improved, and a new thought is provided for endocrine treatment of the prostate cancer.

Description

technical field [0001] The invention belongs to the technical field of nanomaterial preparation and nanomedicine, and relates to a bifunctional monomer double imprinted layer testosterone molecularly imprinted magnetic nanosphere and a preparation method and application thereof. Background technique [0002] Prostate cancer is one of the common malignant tumors of the male urinary system. The incidence of prostate cancer in my country has shown an obvious and continuous growth trend. Prostate cancer is becoming a malignant tumor of the urinary system that seriously affects the health of men in my country. The prostate is an androgen-dependent organ, and its growth and metastasis are closely dependent on androgen. After the androgen is secreted, it enters the cell, binds to the androgen receptor, and then enters the nucleus to initiate gene expression, thereby promoting the proliferation and metastasis of prostate cancer. The mechanism of action of the clinically applied meth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G77/26C08J9/26B01J20/26B01J20/28B01J20/30B01D15/00C08L83/08
Inventor 唐骁爽宋慧佳张海频豆晓杰张博文范瑞韬高瑞霞
Owner XI AN JIAOTONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap