Recycled coarse aggregate water absorption testing method and system

A technique of regenerated coarse aggregate and testing method, which is applied in the field of measurement of regenerated coarse aggregate, and can solve the problems of high water absorption rate, uncertain time of water absorption rate, different time length and degree of wiping, etc.

Active Publication Date: 2021-04-23
北京新桥技术发展有限公司 +2
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] After the regenerated coarse aggregate is taken out of the water, it takes at least 5 minutes to wipe the regenerated coarse aggregate to the surface-dry state with water-absorbing materials. The degree of wiping is different; and the recycled coarse aggregate is still absorbing water continuously during the wiping process, so the specific time for the calculated water absorption rate at this time will not be determined, and the shorter the soaking time of the recycled coarse aggregate in water , the more limited the method of using the above method to test the water absorption rate is, the water absorption rate may even be higher when soaked for 5 minutes than when soaked for 10 minutes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Recycled coarse aggregate water absorption testing method and system
  • Recycled coarse aggregate water absorption testing method and system
  • Recycled coarse aggregate water absorption testing method and system

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0041]In order to make the technical problems solved by the present invention, the technical solutions adopted and the technical effects achieved clearer, the technical solutions of the present invention will be further described below in conjunction with the accompanying drawings and through specific implementation methods. It should be understood that the specific embodiments described here are only used to explain the present invention, but not to limit the present invention. In addition, it should be noted that, for the convenience of description, only the parts related to the present invention are shown in the drawings but not all of them.

[0042] Such as Figure 1 to Figure 3 As shown, the present embodiment provides a regenerated coarse aggregate water absorption test system, including a basket 1, a balance 2, a water tank 3, a controller and an intelligent terminal, wherein the mesh basket 1 is used to hold the regenerated coarse aggregate; The upper end of the net b...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of recycled coarse aggregate measurement, and discloses a recycled coarse aggregate water absorption testing method and system, and the method comprises the following steps: measuring the mass m1 of dried recycled coarse aggregate; putting the mesh basket containing the recycled coarse aggregate into water at a preset temperature to enable the recycled coarse aggregate to stand in the water for 1440 minutes, and respectively collecting the water mass MT and M1 of the recycled coarse aggregate when the water absorption duration is T and 1440 minutes; taking out the recycled coarse aggregate, wiping to a saturated surface dry state, and measuring the mass m2 of the recycled coarse aggregate in the saturated surface dry state; and calculating the water absorption rate WT of the regenerated coarse aggregate when the water absorption duration is T, wherein WT=(MT+m2-m1-M1) / m1*100%. By setting T, the water absorption rate of the recycled coarse aggregate at any moment within 0-1440 min can be obtained, the early water absorption rate of the recycled coarse aggregate is tested, especially the water absorption rate of the recycled coarse aggregate in the first 10 min, and the influence of the recycled coarse aggregate on the slump of cement concrete can be conveniently estimated.

Description

technical field [0001] The invention relates to the technical field of measuring recycled coarse aggregates, in particular to a method and system for testing the water absorption of recycled coarse aggregates. Background technique [0002] The traditional method of testing the water absorption of primary coarse aggregate is to soak the primary coarse aggregate in water for 24 hours, then take out the primary coarse aggregate, wipe it with water-absorbing material until it is saturated and dry, weigh it, and calculate the water absorption after drying. However, due to the large mortar content in the recycled coarse aggregate, the fast water absorption rate, and the large water absorption capacity, the recycled coarse aggregate is close to saturation within 5-10 minutes of putting the recycled coarse aggregate in water. When the original coarse aggregate water absorption test method is used to test the water absorption of the recycled coarse aggregate, the water absorption tes...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N5/02
CPCG01N5/025
Inventor 于蕾刘兆磊吕思忠郭建民吴斌王晓明王凯刘星亮
Owner 北京新桥技术发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com