Chitosan arginine gel dressing for repairing dental tubules
A saccharinine gel and dental tubule technology, applied in dentistry, dental preparations, dental prostheses, etc., can solve the problem of slow relief of dentin hypersensitivity pain, low dentinal tubule sealing effect, and poor periodontal reconstruction effect, etc. To reduce dentin hypersensitivity, improve uniform sealing and stable adhesion, and promote repair
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028] Embodiment 1-can be used for the chitosan arginine gel dressing of dental tubule restoration, according to the ratio of parts by weight, including 2 parts of bioactive glass, 0.1 part of functional mixture, 1 part of sorbitol, 2 parts of carbomer, 0.5 part of glycerin 3 parts, 3 parts of hydroxyethyl cellulose and 20 parts of water.
[0029] The preparation method of this chitosan arginine gel dressing comprises:
[0030] (1) Preparation of modified β-chitosan: After adding dopamine to 50°C hot water to completely dissolve it, adjust the pH to 8.0 with a concentration of 1mol / L sodium hydroxide solution, stir for 1 hour in a light-proof airtight container, and let stand 5h; add citric acid to adjust the pH to 6.5, add β-chitosan with 2.5 times the mass of dopamine, fully stir at a constant temperature of 35°C for 0.8h, and perform ultrasonic treatment for 30s to obtain modified β-chitosan;
[0031] (2) Preparation of functional mixture: add modified β-chitosan and argi...
Embodiment 2
[0033] Embodiment 2-the chitosan arginine gel dressing that can be used for dental tubule restoration, it differs from embodiment 1 in that it also includes 0.1 parts by weight of gamma polyglutamic acid.
[0034] The preparation method of this chitosan arginine gel dressing,
[0035] (1) Preparation of modified β-chitosan: After adding dopamine to 50°C hot water to completely dissolve it, adjust the pH to 8.0 with a concentration of 1mol / L sodium hydroxide solution, stir for 1 hour in a light-proof airtight container, and let stand 5h; add citric acid to adjust the pH to 6.5, add β-chitosan with 2.5 times the mass of dopamine, fully stir at a constant temperature of 35°C for 0.8h, and perform ultrasonic treatment for 30s to obtain modified β-chitosan;
[0036] (2) Preparation of functional mixture: add modified β-chitosan and arginine to 55% of the water according to the mass ratio of 1:6, and stir until completely dissolved to obtain the functional mixture;
[0037] (3) Mix...
Embodiment 3
[0039] Embodiment 3-can be used for the chitosan arginine gel dressing of dental tubule repair, according to the ratio of parts by weight, including 3 parts of bioactive glass, 0.4 part of functional mixture, 0.2 part of gamma polyglutamic acid, 5 parts of sorbitol , 3 parts of carbomer, 1 part of glycerin, 6 parts of hydroxyethyl cellulose and 25 parts of water.
[0040] The preparation method of this chitosan arginine gel dressing,
[0041] (1) Preparation of modified β-chitosan: After dopamine is completely dissolved in hot water at 60°C, adjust the pH to 8.5 with 1mol / L sodium hydroxide solution, stir in a light-proof airtight container for 2 hours, and let it stand 7h; add citric acid to adjust the pH to 6.8, add β-chitosan with 3.2 times the mass of dopamine, fully stir at a constant temperature of 40°C for 1.2h, and perform ultrasonic treatment for 60s to obtain modified β-chitosan;
[0042] (2) Preparation of functional mixture: add modified β-chitosan and arginine to...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap