Production method of DMC composite material

A technology of composite materials and production methods, which is applied in the production field of DMC composite materials, can solve problems such as poor tensile strength, and achieve the effect of improved alkali resistance and high tensile strength

Pending Publication Date: 2021-12-07
句容市久诺复合材料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Most of the DMC materials that appear on the market are relatively stable in composition and relatively poor in tensile strength. The improvement has been only in the modification of the composition ratio, but the modification of the composition ratio cannot solve the fundamental problem at all.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of production method of DMC composite material in the present embodiment is:

[0020] Step 1: Add unsaturated polyester fiber and glass fiber at a mass ratio of 2:1 at normal temperature, wherein unsaturated polyester fiber: 90 parts, glass fiber: 45 parts, mix the two with, Stand by;

[0021] Step 2: Add and mix the cross-linking agent and thickener in a ratio of 1:1, cross-linking agent: 1.5 parts, thickener: 1.5 parts, and put the unsaturated polyester fiber and glass fiber in step 1 after mixing. in the mixture;

[0022] Step 3: put the filler into the mixture of step 2, filler: 6 parts, the filler is reclaimed twisted yarn, just stir well;

[0023] Step 4: Chopped roving is selected as the core material, and the mixture in step 3 is molded onto the surface of the core material by molding process.

Embodiment 2

[0025] A kind of production method of DMC composite material in the present embodiment is:

[0026] Step 1: Add unsaturated polyester fiber and glass fiber at a mass ratio of 2:1 at normal temperature, wherein unsaturated polyester fiber: 100 parts, glass fiber: 50 parts, mix the two with, Stand by;

[0027] Step 2: Add and mix the cross-linking agent and thickener in a ratio of 1:1, cross-linking agent: 2 parts, thickener: 2 parts, and put the unsaturated polyester fiber and glass fiber in step 1 after mixing. in the mixture;

[0028] Step 3: put the filler into the mixture of step 2, filler: 10 parts, the filler is recycled twisted yarn, just stir well;

[0029] Step 4: Chopped roving is selected as the core material, and the mixture in step 3 is molded onto the surface of the core material by molding process.

Embodiment 3

[0031] A kind of production method of DMC composite material in the present embodiment is:

[0032] Step 1: Add unsaturated polyester fiber and glass fiber at a mass ratio of 2:1 at normal temperature, wherein unsaturated polyester fiber: 60 parts, glass fiber: 30 parts, mix the two with, Stand by;

[0033] Step 2: Add and mix the cross-linking agent and thickener in a ratio of 1:1, cross-linking agent: 1 part, thickener: 1 part, and put the unsaturated polyester fiber and glass fiber in step 1 after mixing. in the mixture;

[0034] Step 3: put the filler into the mixture of step 2, filler: 5 parts, the filler is the recycled twisted yarn, just stir well;

[0035] Step 4: Chopped roving is selected as the core material, and the mixture in step 3 is molded onto the surface of the core material by molding process.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a production method of a DMC composite material, and belongs to the field of material preparation. The specific method comprises the following steps: 1) adding 60-100 parts by mass of unsaturated polyester fibers and 30-50 parts by mass of glass fibers in a mass ratio of 2: 1 at normal temperature, uniformly mixing the unsaturated polyester fibers and the glass fibers, and standing for later use; (2) adding and mixing a cross-linking agent and a thickening agent according to the ratio of 1: 1, and then putting the mixture into the mixture of the unsaturated polyester fibers and the glass fibers in the step (1); and (3) putting the filler into the mixture in the step (2), and uniformly stirring, and (4) selecting chopped twistless roving as a core material, and carrying out mold pressing on the mixture obtained in the step (3) to the surface of the core material by adopting a mold pressing process. According to the invention, the recycled twisted yarn is used as the filler, in addition, the chopped twistless roving is selected as the core material, and the glass fiber is compounded to form the material, so that the material has remarkable characteristics, the alkali resistance is qualitatively improved, and the tensile strength is higher.

Description

technical field [0001] The invention belongs to the field of material preparation, in particular to a production method of a DMC composite material. Background technique [0002] DMC, sometimes referred to as BMC, Chinese translation is referred to as bulk molding compound, the main components of BMC and DMC are the same, and they are called differently according to the industry or the area where they are used. The United Kingdom is the first country to adopt the abbreviation of DMC, and the abbreviation of BMC is more popular in the United States. DMC materials have a long history and have been used in a wide range of time. my country began to introduce British technology, and DMC is used more in China, especially in the electrical industry. [0003] Most of the DMC materials that appear on the market are relatively stable in composition and relatively poor in tensile strength. The improvement all the time is only the modification of the composition ratio, but the modific...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L67/06C08L33/02C08K7/14C08K5/5415C08J5/04
CPCC08J5/048C08J2367/06C08J2433/02C08K7/14C08K5/5415
Inventor 史月芳
Owner 句容市久诺复合材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap