Preparation method adhesive

An adhesive and preservative technology, applied in the direction of protein waste adhesives, etc., can solve the problems of easy mildew, viscosity drop, loss of bonding properties, etc. sexual effect

Inactive Publication Date: 2006-05-24
SHAANXI UNIV OF SCI & TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The viscosity of bone glue changes in a wide range with the change of temperature. As the temperature drops, the viscosity rises sharply. When the temperature is lower than 30°C, it basically loses its fluidity and becomes a gel state, thereby affecting the fluidity of the adhesive; In addition, the bone glue is easy to mildew, and the storage period is short. After the failure, the bone glue adhesive will delaminate, the viscosity will drop, and the bonding performance will be lost, making storage and transportation difficult.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0006] Example 1: first mix the bone glue and water in a mass ratio of 1:1, so that the bone glue is fully swollen to form a glue solution; when the water bath is at a constant temperature of 65°C, add 0.5 parts of 20% by mass concentration to every 100 parts of the glue solution NaOH, stir for 40 minutes; cool down to 50°C, slowly add 1.2 parts of epichlorohydrin dropwise to every 100 parts of the glue with NaOH added, and stir until the viscosity increases significantly; add 0.2 parts to every 100 parts of the glue Preservative sodium benzoate was added, and the pH value was adjusted to pH=8 with glacial acetic acid, and the reaction was continued for 25 minutes to obtain a yellow-brown viscous liquid.

Embodiment 2

[0007] Example 2: first mix the bone glue and water at a mass ratio of 1:1.3, so that the bone glue is fully swollen to form a glue; when the water bath is kept at a constant temperature of 58°C, add 1.5 parts of 20% of the mass percentage concentration to every 100 parts of the glue NaOH, stir for 36 minutes; cool down to 46°C, slowly add 1.1 parts of epichlorohydrin dropwise to every 100 parts of the above glue with NaOH added, stir until the viscosity increases significantly; add 0.1 parts to every 100 parts of the glue Preservative sodium benzoate was added, and the pH value was adjusted to pH=8 with glacial acetic acid, and the reaction was continued for 35 minutes to obtain a yellow-brown viscous liquid.

Embodiment 3

[0008] Example 3: first mix the bone glue with water at a mass ratio of 1:1.1, so that the bone glue is fully swollen to form a glue solution; when the temperature of the water bath is constant at 55°C, add 1.2 parts of 20% glucosinolate to every 100 parts of the glue solution NaOH, stir for 30 minutes; cool down to 40°C, slowly add 1.0 parts of epichlorohydrin dropwise to every 100 parts of the glue with NaOH added, stir until the viscosity increases significantly; add 0.1 parts to every 100 parts of the glue Preservative sodium benzoate was added, and the pH value was adjusted to pH=8 with glacial acetic acid, and the reaction was continued for 32 minutes to obtain a yellow-brown viscous liquid.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A preparation method of a high-stability adhesive. Firstly, the bone glue is mixed with water to fully swell the bone glue; when the temperature is constant in a water bath, NaOH is added to stir at a medium speed; Stir rapidly until the viscosity increases significantly; add preservative sodium benzoate, and adjust the pH value to pH=8 with glacial acetic acid, and continue the reaction to obtain a yellow-brown viscous liquid. The present invention decomposes bone glue under alkaline conditions, releases bone glue molecules by breaking peptide bonds, and then grafts and copolymerizes with epichlorohydrin to form a linear structure. On the one hand, the active groups in the bone glue solution are reduced, the tendency of the bone glue molecular chains to associate with each other to form a gel is reduced, and the pH value is adjusted to about 8 with glacial acetic acid to neutralize the unreacted alkali so that it does not continue Degrade bone glue molecules, keep the reaction system neutral and enhance its stability.

Description

technical field [0001] The invention belongs to fine chemical products, in particular to a preparation method of an adhesive. Background technique [0002] The viscosity of bone glue changes in a wide range with the change of temperature. As the temperature drops, the viscosity rises sharply. When the temperature is lower than 30°C, it basically loses its fluidity and becomes a gel state, thereby affecting the fluidity of the adhesive; In addition, the bone glue is prone to mildew, and the storage period is short. The bone glue adhesive after failure is delaminated, the viscosity drops, and the bonding performance is lost, so storage and transportation are difficult. Contents of the invention [0003] The purpose of the present invention is to overcome the shortcomings of the modified bone glue adhesive that is easy to mildew and the storage period is short, and provides a kind of advantage that not only retains the low freezing point of the original modified bone glue adh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J189/04
Inventor 李仲谨牛育华李文汉刘正安张君财杨振朱敏李晓钡李小燕杨艳丽李华锋
Owner SHAANXI UNIV OF SCI & TECH