Composite iron-titanium powder anti-rust paint
A technology of compounding iron-titanium powder and anti-rust paint, applied in the field of paint, can solve the problems of environmental pollution, high cost, toxicity, etc., and achieve the effects of no environmental pollution, good social and economic benefits
Inactive Publication Date: 2003-03-26
NAVAL UNIV OF ENG PLA
View PDF0 Cites 4 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Among them, red lead antirust paint has the best performance, but its cost is higher than other primers, and, no matter in use or in repair, red lead, that is, three lead tetroxide, has great toxicity, especially for removing old When using red lead antirust paint, it will cause great harm to people and seriously pollute the environment
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreExamples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0008] The production process is the same as the current production of 100kg phenolic red lead antirust paint, except that when adding red lead powder, add 10kg, or 40kg, or 60kg of composite iron-titanium powder.
Embodiment 2
[0010] It is the same as the production process of producing 100kg alkyd red lead antirust paint now, just add 10kg, or 40kg, or 60kg weight of composite iron-titanium powder instead when adding red lead powder.
Embodiment 3
[0012] The same as the current production process of producing 100kg epoxy red lead antirust paint, just add 10kg, or 40kg, or 60kg weight of composite iron-titanium powder instead when adding red lead powder.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
There is a kind of ferrotitanium compound powder antirust paint, it removes the red lead from the red lead antirust paint, the red lead is replaced by the ferrotitanium compound powder, its advantages are: it uses only 40% compound ferrotitanium powder to replace 50% red lead powder, its main technology includes reach or exceed red lead antirust paint, and the cost can be reduced about 1800 RMB / T. The product is innoxious and has no contamination to environment.
Description
technical field [0001] The invention relates to the technical field of paint. Specifically, it is a composite iron-titanium powder antirust paint. Background technique [0002] When traditional steel structures are treated with paint for anti-corrosion treatment, anti-rust paint is required as a primer. Among them, the most commonly used are red lead antirust paint, cloud iron antirust paint, zinc gray antirust paint, iron red antirust primer and so on. Among them, red lead antirust paint has the best performance, but its cost is higher than other primers, and, no matter in use or in repair, red lead, that is, three lead tetroxide, has great toxicity, especially for removing old When using red lead antirust paint, it will cause great harm to people and seriously pollute the environment. content of the invention [0003] The purpose of the present invention is to improve the components of the existing red lead antirust paint, r...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C09C1/36C09D5/08
Inventor 李家权金广泉
Owner NAVAL UNIV OF ENG PLA