Crosslinked polyethylene special material for rotational moulding

A technology of cross-linked polyethylene and special materials, applied in the field of cross-linked polyethylene special materials for rotational molding, can solve the problem of limiting the application range of LLDPE, poor processability of LLDPE, thermal creep, low temperature impact resistance and swelling resistance. and other problems, to achieve the effect of good rotomolding performance, good permeability and chemical resistance, and good fluidity

Inactive Publication Date: 2004-08-25
PETROCHINA CO LTD
View PDF0 Cites 31 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, LLDPE still has defects such as poor processability, thermal creep resistance, low temperatu

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Crosslinked polyethylene special material for rotational moulding
  • Crosslinked polyethylene special material for rotational moulding

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0018] formula:

[0019] LLDPE 7042 70 kg

[0020] LDPE 1F7A 30 kg

[0021] Dicumyl peroxide 4.5kg

[0022] Antioxidant 1010 500g

[0023] Preparation: Mix the raw materials prepared according to the formula evenly in a high-speed mixer, and then blend on a double-roll mill, and the blending temperature is 130-140°C. The next piece was crushed.

example 2

[0025] formula:

[0026] LLDPE 7042 90 kg

[0027] LDPE 1F7A 10 kg

[0028] 2,5 dimethyl-2,5 di-tert-butyl hexane 1 kg

[0029] Dilauryl Thiodipropionate 900g

[0030] Preparation: The method is the same as the preparation method of Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to a rotational moulding cross-linked polyethylene special-purpose material. It contains the following components: (by total weight of linear low-density polyethylene and low-density polyethylene) A. linear low-density polyethylene 70-90%; B. low-density polyethylene 10-30%; C. cross-linking agent 0.5-5%; and D. antioxidant 0.1-1%. Said invention also relates to a preparation method for using said special-purpose material. The special-purpose material composition can be molten and mixed in a mixer or twin screw extruder machine, blending temp. is 130-170 deg.C, the invented polyethylene special-purpose material can be obtained. The rotational moulding product prepared by said special-purpose material has good working property, high resistance to implact shock, good resistance to thermal creep and low-temp. toughness, etc.

Description

technical field [0001] The invention relates to a special cross-linked polyethylene material for rotational molding. Background technique [0002] Rotational molding is one of the methods of forming large and medium-sized products. This process originated in the United States in the 1940s. Due to various reasons, it has developed slowly and is limited to the processing of a few plastic products. In recent years, due to the development of plastics and their powdering, the gradual expansion of the application field of plastics, and the superiority of this process, it is developing rapidly. At present, the proportion of various types of rotationally molded polyethylene materials in foreign countries is roughly: 65% for linear low-density polyethylene (LLDPE), 20% for cross-linked polyethylene (XHDPE), 10% for high-density polyethylene (HDPE), and 10% for low-density polyethylene (LDPE). Polyethylene (LDPE) is 5%. In the late 1970s, linear low-density ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B29C48/40C08L23/06
CPCB29C48/40
Inventor 王洪梅陈光岩
Owner PETROCHINA CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap