Carbon deposit cleaning agent and its application in reproduction of deactivation catalyst

A technology for deactivating catalysts and cleaning agents, which is used in catalyst regeneration/reactivation, physical/chemical process catalysts, chemical instruments and methods, etc., to achieve the effect of reducing carbon deposits and reducing toxicity

Active Publication Date: 2006-05-10
CHINA PETROLEUM & CHEM CORP +1
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the reason for the deactivation of the catalyst deactivated by carbon deposition is obviously different from that of the titanium-containing heterogeneous catalyst u

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] In the flask of 1000ml, add carbon deposit cleaning agent (its specific composition and its content are shown in Table 1) to the hydrodesulfurization MoNiP / Al of 100ml deactivated residual oil after an industrial operation 2 o 3 Catalyst (numbering is A, carbon deposition content is 11.45wt%) is processed respectively, and the catalyst after processing continues to process with dehydrated alcohol, measures the content change of amorphous and graphite-like shape carbon deposition with thermogravimeter then, its result sees Table 1.

[0033]

[0034] As can be seen from Table 1, compared with the deactivated catalyst that only ethanol and benzene or kerosene and gasoline are processed, with the catalyst that the carbon deposit cleaning agent solution of the present invention is processed, the amount of carbon deposits all significantly reduces, especially without The relative content of stereotyped carbon deposits has been significantly reduced.

[0035] It can ...

Embodiment 2

[0042] In the flask of 1000ml, add carbon deposit cleaning agent (its concrete composition and its content are shown in Table 3) to the 100ml Mo / HZSM-5 methane aromatization catalyst (numbering is B, and carbon deposit content is 10.84wt% after an industrial operation) ) were processed respectively, and the treated catalyst continued to be processed with absolute ethanol, and then the content changes of amorphous and graphite-like carbon deposits were measured with a thermogravimeter, and the results are shown in Table 3.

[0043]

Carbon cleaning agent

solvent

deal with

condition

residual product

carbon content,

wt%

Thermogravimetry Results: Occupancy

The content of residual carbon deposits,

wt%

amorphous

graphite-like

-

287ml ethanol

287ml benzene

Soak for 16h, straight

Distillation 2h

10.21

86

14

40ml ethylene ...

Embodiment 3

[0052] 100ml hydrotreating MoNiP / Al after an industrial operation 2 o 3 Deactivated catalyst (coded as C, carbon deposit content is 10.21wt%) can be regenerated in the following way:

[0053] First, the catalyst is loaded into the regeneration unit, and the N 2 The device is replaced, and then the oxygen content is adjusted to 2.0v%, and the catalyst is regenerated by burning charcoal step by step. The main control conditions at each stage are: 120°C, constant temperature for 3h; 200°C constant temperature for 2h; 300°C constant temperature for 1.5h; 500°C constant temperature for 3h.

[0054] The 15ml catalyst that regenerates like this is packed in microreactor, carry out activity evaluation according to following condition:

[0055] Raw oil: 950μg / g pyridine / kerosene; volumetric space velocity: 2.0h -1 ;Temperature: 360°C: Reaction pressure: 4.0MPa; Hydrogen flow rate: 100ml / min. Samples were taken for analysis after 12 hours of stabilization. The nitrogen content in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a carbon build-up cleaning agent and its use in the regeneration process of devitalized catalyst, the carbon build-up cleaning agent comprises the following components: butyl acetate 5-95 v%, diethyleneglycol monobutyl ether 5-95 v%, isopropanol 0-90 v%, and toluene 0-90 v%. The carbon build-up cleaning agent can be used for catalysts with appreciable heat release during regeneration, especially for devitalized hydrogenation catalyst and methane aromatization catalyst requiring oxidation burning-out for carbon build-up cleaning.

Description

technical field [0001] The invention relates to a carbon deposit cleaning agent and its application in the regeneration process of deactivated catalysts, especially suitable for the regeneration of deactivated hydrogenation catalysts. Background technique [0002] Catalysts used in refining and chemical processes will gradually lose their activity during long-term operation. The reason is largely due to the deposition of carbon deposits on the surface of the catalyst. These coke-deactivated catalysts are regenerated by oxidizing and burning off the coke, and the activity can be partially or completely restored, and they can still be used in industrial production. Some catalysts can even be regenerated multiple times to achieve the purpose of saving energy and increasing benefits. [0003] When the carbon deposition deactivation catalyst is regenerated by burning carbon, the carbon deposition will react with oxygen and be removed, and a large amount of heat will be generated...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01J38/52B01J38/02
Inventor 张喜文凌凤香孙万富赵荣林
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap