Sorbent of zeolite with carrying silver, preparation method and application

A silver-loaded zeolite and adsorbent technology, which is applied in chemical instruments and methods, other chemical processes, separation/purification of carboxylic acid compounds, etc., can solve the problem of uneven distribution of coarse pore size, corrosion of refining equipment, and reduced use efficiency of adsorbents and other problems, to achieve the effect of high industrialization implementation prospect and simple preparation method

Active Publication Date: 2006-07-05
SHANGHAI HUAYI ENERGY CHEM +1
View PDF22 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] U.S. Patents US 3,927,078, US 4,046,807, US 4,115,444, US 4,252,741, US 4,374,070, US 4,430,273, US 4,559,183, US 5,003,104, US 5,292,948, and European patents EP 8396, EP 87,869 and EP 8396, EP 87,869. In the process, iodide participates in the reaction as a co-catalyst, so the product inevitably contains trace amounts of inorganic iodine, organic iodide and molecular iodine impurities. 05-301839 (BP Company) and patent publication level 05-125011 (BP Company) disclosed in the presence of rhodium / methyl iodide catalyst, methanol and (or) acetic acid and (or) acetic anhydride prepared by carbonylation of methyl acetate method, the existing problem is, always contain a small amount of iodide impurity in acetic acid or acetic anhydride after distillation
[0007] 2. Crude acetic anhydride, or the iodide concentration in the crude acetic anhydride / crude acetic acid mixture is too high, which will cause corrosion to the refining device, which is mentioned by Daicel
Due to the uneven distribution of the amorphous binder among the zeolite powder crystal grains in the adsorbent particles, the coarse pore size distribution between the zeolite crystal grains is uneven. Diffusion to the zeolite crystal grains also reduces the use efficiency of the adsorbent and affects the strength of the adsorbent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Put 80 grams of acid-resistant base zeolite into a 50mL autoclave, and add 40ml of 0.5mol / L ion-exchange silver-carrying Ag + Solution (AgNO 3 solution), heated to 140°C, and the constant temperature time was 6 hours. After the ion exchange silver loading was completed, the adsorbent was taken out, washed with distilled water, and dried in an oven at 80°C. EDX analysis was performed on the ion-exchange silver-loaded adsorbent, and the results obtained are shown in Table 1:

[0030] the element

Embodiment 2

[0032] Put the acid-resistant zeolite adsorbent into the ion exchange column, the solid volume of the exchange column is 20mL, and the solution concentration is 0.1mol / L Ag + Solution (AgNO 3 Solution), continue to flow through the exchange column, the duration is 24 hours, the temperature is 80 ℃, and the flow velocity is 4 m / s. The EDX method is used to analyze the composition of the ion-exchange silver-loaded sorbent. The results obtained are shown in Table 2:

[0033] the element

Embodiment 3～11

[0035] Take by weighing the ion-exchange silver-loaded adsorbent 16g (about 20mL) that embodiment 2 obtains, carry out the test of removing trace inorganic iodide in the acetic anhydride product under the conditions listed in table 3 respectively in the ion-exchange column, after the test, B The analysis results of inorganic iodide content and silver content in the acid anhydride product are listed in Table 3, to prove that the ion-exchange silver-loaded adsorbent has a good effect on removing trace amounts of inorganic iodide in the acetic anhydride product.

[0036]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a silver-bearing zeolite adsorbent, its preparation method and application. The invented silver-bearing zeolite adsorbent is a silver-bearing acid-resistant zeolite, its silver weight content is 7-15%. The described silver-bearing zeolite adsorbent can be used for removing trace iodide from acetic anhydride product. Besides, said invention also provides the concrete structure of said zeolite.

Description

technical field [0001] The invention relates to a silver-loaded zeolite adsorbent and the application of its preparation method, in particular to the application of removing trace iodide in acetic anhydride products. technical background [0002] Acetic anhydride is widely used in industry as an acetylating agent. In the United States, 95% of the production of acetic anhydride in Japan is used to produce cellulose acetate, triacetate cellulose containing 61.5-62% acetyl is used to manufacture high-strength, non-flammable photosensitive films, and diacetate containing 50-57% acetyl Cellulose is used to make cigarette filters and plastics. Acetic anhydride is also widely used in medicine, dyestuff, pesticide and fragrance industry. [0003] U.S. Patents US 3,927,078, US 4,046,807, US 4,115,444, US 4,252,741, US 4,374,070, US 4,430,273, US 4,559,183, US 5,003,104, US 5,292,948 and European patents EP 8396, EP 87,869, EP 8396, 87,869 In the process, iodide participates in the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/18C07C51/47C07C53/08
Inventor 陈墨庆周皓岚龙英才崔伟
Owner SHANGHAI HUAYI ENERGY CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com