Coated steel sheet with excellent heat dissipation
A technology for coating steel plates and steel plates, which is applied in coating, hot-dip plating process, and coating of superimposed layers, etc. It can solve the problems of increased noise and large heat dissipation, and achieves excellent heat dissipation and electromagnetic wave shielding Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0170] (embodiment 1: the impact of plating seed on heat dissipation)
[0171] A coated steel sheet having a cold-rolled steel sheet (thickness: 0.6mm) having the chemical composition shown in Table 1 as a base material was used as a coating substrate, and on the surface of the substrate, one side (coating A coating film was formed on the other side (inner surface) without any treatment, and a coated steel sheet was produced, and the heat dissipation of the coated steel sheet and the heat radiation property of the inner surface were evaluated.
[0172] Table 1
[0173]
[0174] [plating species]
[0175] Two types of hot-dip galvanized steel sheet (symbol "GI") and alloyed hot-dip galvanized steel sheet (symbol "GA") were used.
[0176] Hot-dip galvanized steel sheet (GI)
[0177] Al concentration of coating: 0.40%
[0178] Plating adhesion: 60g / m on both the painted surface and the inner surface 2
[0179] Coating surface roughness: center l...
Embodiment 2
[0210] (Example 2: Effect of coating film thickness on heat dissipation)
[0211] The alloyed hot-dip galvanized steel sheet (GA) used in Example 1 was used as a coating substrate, and on the surface of the substrate, a coating film was formed on one side (coating surface) by the same method as in Example 1, The other side (inner side) is not subjected to any treatment, and the coated steel plate is manufactured. The heat dissipation of the coated steel sheet and the heat radiation of the front and back surfaces were evaluated. The evaluation method of heat dissipation and heat radiation is the same as in the case of Example 1.
[0212] Table 4 gives the results. In Table 4, paint 3 and paint 5 in the column of "inner layer coating film" correspond to paint 3 and paint 5 shown in Table 2.
[0213] test
[0214] As shown in Table 4, when the total thickness of the coating film (No. 17) is about 10 μm or more when the coating film (No. In the case of 11 to 15), if ...
Embodiment 3
[0215] (Example 3: Relationship between antirust treatment on the inner surface and electrical conductivity, heat dissipation and corrosion resistance)
[0216] Using the hot-dip galvanized steel sheet (GI) and the alloyed hot-dip galvanized steel sheet (GA) used in Example 1 as the coating base material, the coating primer was formed on the painted surface by the same method as in the case of Example 1. Treatment layer, inner layer coating film (use coating 3 of Table 2, thickness 5 μm) and outer layer coating film.
[0217] The inner surface was prepared separately as shown in the "inner surface" column of Table 5 described later. That is, it can be roughly divided into the following three types:
[0218] ・Plating surface (as plated) (No.18, 19)
[0219] ·Inorganic coating or inorganic-organic composite coating (No.22~47)
[0220] Coating film (A primer treatment was applied by the same method as in Example 1, and an inner layer coating film with a thickness of 5 μm was for...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap