Bamboo arc sheet spreading method

A bamboo chip and arc-shaped technology, which is applied in the field of raw material bamboo processing technology, can solve the problems of raw material waste, high cost, and reduce production cost, and achieve the effects of not being easy to spring back, improving processing productivity, and increasing the degree of softening

Inactive Publication Date: 2007-05-23
NANJING FORESTRY UNIV
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to solve the defects of large waste of raw materials and high cost in the current production of bamboo flooring, and provide a method for flattening bamboo slices, which allows arc-shaped bamboo slices with a width of 30 to 100 mm to pass through the bamboo. After the sheet flattening method is processed, the equal thickness processing can reduce the consumption of bamboo resources and greatly reduce the production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] The arc-shaped bamboo slices with an arc length of 30 millimeters are cut into equal width bamboo slices with parallel sides. Place in a plane hot press (model zy3-130) with a lateral press mechanism, press plate temperature at 180 degrees, keep the pressure at 0-0.2Mpa for 3 minutes and then press gradually until the bamboo slices are flattened. Continue to keep the pressure at 0.5Mpa for 5 minutes after the bamboo sheet is flattened. While the bamboo slices are gradually flattened, the width of the bamboo slices increases with the expansion of the arc length of the bamboo slices. At this time, the lateral pressing mechanism (model zy3-130-c) moves in the width direction to meet the Expand the arc length (width of the bamboo slices) and ensure the lateral pressure on the bamboo slices (0-0.2Mpa), so that the arc-shaped bamboo slices are flattened under the simultaneous action of lateral pressure and vertical pressure, reducing or reaching the bamboo slices. The inner ...

Embodiment 2

[0015] The arc-shaped bamboo slices with an arc length of 100 mm are sawed into bamboo slices with parallel sides of equal width. Place in a plane hot press (model zy3-130) with a lateral press mechanism, press plate temperature at 220 degrees, keep the pressure at 0-0.2Mpa for 3 minutes and then gradually pressurize until the bamboo slices are flattened. After the bamboo slices are flattened, continue to hold the pressure for 5 minutes under a pressure of 2.0Mpa. While the bamboo slices are gradually flattened, the width of the bamboo slices increases with the expansion of the arc length of the bamboo slices. At this time, the lateral pressing mechanism (model zy3-130-c) moves in the width direction to meet the Expand the arc length (width of the bamboo slices) and ensure the lateral pressure on the bamboo slices (0-0.2Mpa), so that the arc-shaped bamboo slices are flattened under the simultaneous action of lateral pressure and vertical pressure, reducing or reaching the bamb...

Embodiment 3

[0017] After carbonization, the arc-shaped bamboo slices with an arc length of 55 mm are sawn into bamboo slices with parallel sides of equal width. Place it in a plane hot press (model zy3-130) with a lateral press mechanism, press plate temperature at 200 degrees, keep the pressure at 0-0.2Mpa for 3 minutes and then press gradually until the bamboo slices are flattened. After the bamboo slices are flattened, continue to hold the pressure for 5 minutes under a pressure of 1.25Mpa. While the bamboo slices are gradually flattened, the width of the bamboo slices increases with the expansion of the arc length of the bamboo slices. At this time, the lateral pressing mechanism (model zy3-130-c) moves in the width direction to meet the Expand the arc length (width of the bamboo slices) and ensure the lateral pressure on the bamboo slices (0-0.2Mpa), so that the arc-shaped bamboo slices are flattened under the simultaneous action of lateral pressure and vertical pressure, reducing or...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for flattening the arc bamboo plate, wherein it cuts arc bamboo plate into arc plate with parallel edges to be put in thermal compressor with adjustable side compressor; compressing and flattening the bamboo plate; the side compressor moves along width; keeping pressure at 0.5-2.0MPa for 5min, shaping it. The invention can soften the bamboo plate, and it can flexibly adjust the width and pressure on bamboo plate; and it can improve the efficiency.

Description

technical field [0001] The invention relates to a method for flattening original bamboo arc-shaped bamboo slices. The invention belongs to the technical field of processing technology of raw material bamboo. Background technique [0002] Because bamboo is a round, hollow stem plant. Therefore, for many years, in the industrial application process of bamboo, in order to obtain flat bamboo chips with a certain width and thickness, bamboo is divided into bamboo strips or bamboo strips, and then processed into bamboo chips of equal thickness for application. And bamboo chip must be planed off the natural circular arc part of bamboo in carrying out equal thickness processing process, just can make the plane bamboo chip of equal thickness, has caused a large amount of waste of bamboo material raw material like this, and bamboo material output rate is low. Contents of the invention [0003] The purpose of the present invention is to solve the defects of large waste of raw mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27M1/02
Inventor 黄河浪赵明卢晓宁薛丽丹
Owner NANJING FORESTRY UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com