Material non-adhesive to biological substance, curable composition, and artificial organ and medical instrument using same

a biological substance and non-adhesive technology, applied in the field of material non-adhesive to biological substances, curable compositions, artificial organs and medical instruments, to achieve the effects of preventing or suppressing the adhesion of cells or blood components, excellent non-adhesive properties, and improving biocompatibility

Inactive Publication Date: 2019-08-15
FUJIFILM CORP
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

The present invention provides a material that does not stick to living organisms. This material can be used to make things like medical instruments and artificial organs that are more compatible with the human body. The patent text also describes a curable composition that can be used to make this material. Overall, the invention makes it possible to create products that are safer and more effective for use in the body.

Problems solved by technology

It is expected that the artificial organs or medical instruments can be used longer than the related art by making the biological substance difficult to adhere to such members or instruments.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Material non-adhesive to biological substance, curable composition, and artificial organ and medical instrument using same
  • Material non-adhesive to biological substance, curable composition, and artificial organ and medical instrument using same
  • Material non-adhesive to biological substance, curable composition, and artificial organ and medical instrument using same

Examples

Experimental program
Comparison scheme
Effect test

example 2

[0212](Preparation of Photocurable Composition)

[0213]The compound ex1 (4.5 g), 2-hydroxyethyl methacrylate (manufactured by Wako Pure Chemical Industries, Ltd., 4.5 g), triethylene glycol dimethacrylate (manufactured by Wako Pure Chemical Industries, Ltd., 0.8 g), IRGACURE 2959 (trade name, manufactured by BASF Corporation, 0.2 g), and methanol (3.3 g) were mixed with each other, thereby preparing a photocurable composition.

[0214]A glass substrate having a size of 24 mm2 was coated with the obtained photocurable composition at 2000 rpm for 20 seconds using a spin coater, and then the coated surface of the glass substrate was irradiated with black light for 5 minutes, thereby preparing a glass substrate on which a photocurable coating film was formed.

[0215]A CoCr piece having a size of 0.5×1 cm was immersed in the obtained photocurable composition, taken out, and then irradiated with black light for 5 minutes, thereby preparing a CoCr piece on which a coating film of a photocured pro...

reference example 3

[0216]A CoCr substrate washed with acetone was washed with plasma and immersed in a 0.1 mass % methanol solution of 2-bromo-N-(3,4-dihydroxyphenethyl)propanamide synthesized according to J. Am. Chem. Soc., 205, 127, pp. 15843 to 15847 for 20 hours.

[0217]Next, the compound ex1 (7.2 g), water (24 g), methanol (19 g), 2-bromoisobutyrate (manufactured by Wako Pure Chemical Industries, Ltd., 0.016 g), and N,N,N′,N″,N″-pentamethyldiethylene triamine (manufactured by Wako Pure Chemical Industries, Ltd., 0.346 g) were mixed with each other, and bubbled with nitrogen for 20 minutes while the mixture was stirred. Thereafter, the CoCr substrate was immersed in a mixed solution, copper bromide (I) was added thereto (manufactured by Wako Pure Chemical Industries, Ltd., 0.044 g), and then atom transfer radical polymerization (ATRP) was performed for 3 hours. Next, the obtained CoCr substrate was dried at 50° C., thereby obtaining a CoCr substrate on which a surface polymer graft film was formed. ...

example 4 and reference example 4

[0223]A coating film of a polymer was formed using each of ex2, ex4, ex6, ex8, and ex9 in place of ex1 used in Reference Example 1. The cell adhesion test and the platelet adhesion test were performed in the same manners as those in Reference Example 1. As the result, it was confirmed excellent non-adhesive properties to a biological substance were shown in both tests (0 time, [A]).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
wavelengthaaaaaaaaaa
wavelengthsaaaaaaaaaa
Login to View More

Abstract

A material non-adhesive to a biological substance containing: a polymer compound (A) which includes a repeating unit derived from a sulfobetaine monomer represented by Formula (I) or (II).In the formulae, R1 represents a methyl group, an ethyl group, an n-propyl group, or an isopropyl group, a plurality of R1's may be the same as or different from each other.R2 represents a hydrogen atom or a methyl group.n represents an integer of 2 to 4.L represents a linear or branched alkylene group having 3 or 4 carbon atoms.

Description

CROSS-REFERENCE TO RELATED APPLICATIONS[0001]This is a Rule 53(b) Divisional Application of application Ser. No. 15 / 581,703 filed Apr. 28, 2017 which is a Continuation of PCT International Application No. PCT / JP2015 / 077131 filed on Sep. 25, 2015, which claims priority under 35 U.S.C. § 119 (a) to Japanese Patent Application No. 2014-220307 filed on Oct. 29, 2014, to Japanese Patent Application No. 2015-021539 filed on Feb. 5, 2015, and to Japanese Patent Application No. 2015-149458 filed on Jul. 29, 2015. Each of the above applications is hereby expressly incorporated by reference, in its entirety, into the present application.BACKGROUND OF THE INVENTION1. Field of the Invention[0002]The present invention relates to a material non-adhesive to a biological substance, a curable composition, and an artificial organ and a medical instrument using the same.2. Description of the Related Art[0003]It is desired that artificial internal organs or medical instruments are prepared using materi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityApplications(United States)
IPC IPC(8): C08F220/60A61L31/10A61L29/00A61L31/00C08F228/02C08F220/28C08F220/18A61L27/00A61L27/34C08F20/60A61L33/00
CPCC08F220/60A61L31/10A61L29/00A61L31/00C08F228/02C08F220/28C08F220/18A61L27/00A61L27/34C08F20/60A61L33/00C08F2220/1825C08F2220/606C08F2220/603C08F220/603C08F220/1804C08F220/20C08F220/606
InventorFUKAGAWA, KIYOTAKA
OwnerFUJIFILM CORP