A technology of interlining and fabric, applied in the field of composite yarn for interlining

Inactive Publication Date: 2008-04-16
TOKAI THERMO +2
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These interlinings for clothing and gray fabrics for interlinings have excellent shape retention and can be reduced in weight compared with any of the above-mentioned wool interlinings, but they cannot fully satisfy the conditions required in recent years.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Textiles for lining cloth

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Use untwisted 100% polyester fiber yarn 333dtex / 10f (single filament fineness 33.3dtex) and 167dtex / 30f (single filament fineness 5.6dtex), 100% polyester textile yarn 40 / 1 (single filament fineness 1.3dtex) ) and other 3 kinds, and the twist processing with the twist coefficient of 10330 is carried out to make composite yarn for interlining. Said 333dtex / 10f is the core filament fiber again, and the filament is said 167dtex / 30f fiber filament and 40 / 1 textile filament.

[0040] Only 100% polyester textile yarn 40 / 2 is used for the warp yarn, and only the composite yarn for interlining is used for the weft yarn. Carry out plain weaving with a rapier type weft-inserting loom with a set density of 40 warps / 2.54cm and 40 wefts / 2.54cm to make natural color cloth. This unbleached cloth is subjected to scouring, pre-fixing, dyeing, and heat-setting to obtain interlining fabrics for clothing. The scouring process uses a scouring agent for continuous processing. In the preli...

Embodiment 2

[0042] Use untwisted 100% polyester fiber yarn 333dtex / 10f (single-filament fineness 33.3dtex), 167dtex / 30f false-twisted processed yarn (single-filament fineness 5.6dtex) and 167dtex / 48f false-twisted processed yarn (single-filament fineness 3.5dtex) and other three types, twisting processing with a twisting coefficient of 10330 to make composite yarns for interlinings. Furthermore, the 333dtex / 10f is a core fiber, and the above-mentioned 167dtex / 30f and 167dtex / 48f are thin filament fibers, respectively.

[0043] As the warp, 7% of the core-sheath composite fiber is composed of polyester (melting point of 200°C or higher) and polyethylene (melting point of 130°C) in the sheath, and 100% polyester is used for the remaining 93%. Ester spun silk 40 / 2. Only the composite yarn for interlining was used for the weft. Carry out plain weaving with a rapier type weft-inserting loom with a set density of 40 warps / 2.54cm and 40 wefts / 2.54cm to make natural color cloth. Subsequently, ...

Embodiment 3

[0045] All use untwisted 100% polyester fiber yarn 267dtex / 12f (single filament fineness 22.3dtex), 111dtex / 30f (single filament fineness 3.7dtex) and 111dtex / 48f (single filament fineness 2.3dtex), etc. Twisting processing with a twist coefficient of 8850 was performed to produce composite yarns for interlinings. Furthermore, the 267dtex / 12f is a core fiber, and the 111dtex / 30f and 111dtex / 48f are thin filament fibers respectively.

[0046] Only 100% polyester textile yarn 40 / 2 is used for the warp yarn, and only the composite yarn for interlining is used for the weft yarn. Carry out plain weaving with a rapier type weft-inserting loom with a set density of 40 warps / 2.54cm and 40 wefts / 2.54cm to make natural color cloth. Subsequently, the same processing as in Example 1 was carried out.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

PROBLEM TO BE SOLVED: To provide a cloth for an interlining exhibiting less reduction of forming property and form-maintaining property, and rigidity in consumption stage, having a good dimensional stability even by performing a cleaning with water and a smooth touch feeling on its surface, and a composite yarn for constituting the cloth. ŽSOLUTION: This composite yarn for the interlining is constituted by in a plurality of core yarn filaments and a fine filament yarn arranged around the core yarn filaments, and is processed by performing the yarn twisting of the core yarn filaments with the fine filament yarn by 4,500-20,000 twisting factor. The core yarn filaments consist of a thermoplastic synthetic fiber having 10-50 decitex single fiber fineness, and the fine filament yarn consists of fine filaments or a spun yarn consisting of a thermoplastic synthetic fiber having <10 decitex single fiber fineness. The fine filament yarn is preferably a spontaneous elongation yarn or a false-twisted yarn. The cloth for the interlining is obtained by performing an adjusting process on a raw fabric obtained by weaving or knitting the composite yarn for the interlining as a weft or warp yarn. In the adjusting process, a touch-processing by using a touch-adjusting agent is not performed. Ž

Description

technical field [0001] The present invention relates to a fabric for interlining mainly used for the front body and shoulders of heavy clothes such as suits, jackets, and coats, and a composite yarn for interlining as the warp or weft constituting the fabric for interlining. Background technique [0002] In general, fleece interlining is used for interlining fabrics such as the front part of heavy garments in order to impart formability and shape retention to the garment. It is required that the raw materials of the warp or weft constituting the fleece interlining have appropriate rigidity and resilience. Therefore, animal hair fiber blended yarn made by mixing rayon and wool with coarse and tense animal hair fibers (goat, camel, kraku sheep, yak, etc.) is used. The thickness of animal hair blended spinning yarn is 9-18 metric count (about 550 decitex (dtex)-1110dtex). In the step of finishing gray cloth made of animal hair blended spinning yarn, resin processing is perfor...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D03D15/00D04H3/00A41D27/02A41D27/06D02G3/04D02G3/28D02G3/36D02G3/38D03D1/00
Inventor 棚濑勉森元良自黑田本信
Owner TOKAI THERMO