Ru china shining glaze and its preparation method

A technology of luminous glaze and Ru porcelain, applied in the field of glazes painted on the surface of ceramics, can solve the problems of inability to adapt to the level of artistic appreciation, monotonous glaze color, etc., and achieve the effect of increasing the decorative effect

Inactive Publication Date: 2009-04-15
孟玉松
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Since the successful restoration of Ru porcelain in 1988, it has been mainly producing antique products. Although it has an elegant and solemn style, its glaze color is relatively monotonous, which cannot meet the needs of today's cultural and artistic development situation and people's more perfect art appreciation level.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ru china shining glaze and its preparation method
  • Ru china shining glaze and its preparation method
  • Ru china shining glaze and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] The Ru porcelain luminescent glaze of the present invention and its preparation process will be further described below in conjunction with the examples.

[0022] The luminescent glaze of Ru porcelain in the present invention is composed of basic glaze and luminescent powder, wherein the basic glaze is composed of the following components by weight percentage: 12%-36% of white feldspar, 10%-20% of quartz, and 0-14% of calcite , borax 0-25%, boric acid 0-35%, zircon 0-10%, potassium nitrate 0-8%, zinc oxide 0-8%, fluorite 0-5%, sodium carbonate 0-7%, carbonic acid Strontium 0-20%, barium carbonate 0-15%, dolomite 0-5%.

[0023] Listed in the following table 1 is the formula and five examples of the basic glaze of the Ru porcelain luminous glaze of the present invention.

[0024] Table 1 Ru porcelain luminous glaze base material formula (weight %)

[0025]

[0026] The components and proportions of the luminescent color base of the luminescent powder in the luminesce...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention is one kind of luminous glaze for Ru kiln porcelain and its preparation process. The luminous glaze consists of luminous powder in 25-30 wt% and base glaze material in 70-75 wt%. The base glaze material consists of white feldspar, quartz, calcite, borax, boric acid, zirconia, potassium nitrate, zinc oxide, fluorite, sodium carbonate, strontium carbonate, barium carbonate and dolomite in certain weight proportion. The luminous glaze is used in decorating Ru kiln porcelain to make it possess certain effect of glowing with different colors. It has no toxicity, harmful matter and no radiation and is suitable for decorating Ru kiln porcelain products.

Description

technical field [0001] The invention relates to a glaze painted on the surface of ceramics, in particular to a luminous glaze painted on Ru porcelain products and a preparation method thereof. Background technique [0002] Ru porcelain has been mainly producing antique products since its research and restoration in 1988. Although it has an elegant and solemn style, its glaze color is relatively monotonous, which cannot meet the needs of today's cultural and artistic development and people's more perfect art appreciation level. Contents of the invention [0003] In order to overcome the lack of monotonous color of the existing Ru porcelain glaze, which affects its decorative effect, the purpose of the present invention is to provide a Ru porcelain luminous glaze and a preparation method thereof, which can maintain the elegant and solemn artistic appearance of Ru porcelain. On the premise of the characteristics, the Ru porcelain is decorated more magnificently. According to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/86C03C8/22C03C8/14
Inventor 孟玉松
Owner 孟玉松