Wall brick and processing method thereof

A technology for wall bricks and blanks, applied in the field of decorative materials and their processing, can solve problems such as insufficient decorative effect of wall bricks, and achieve the effect of strong decorative effect.

Inactive Publication Date: 2009-06-10
成都宏翁装饰材料有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a wall tile with a strong decorative effect and a processing method thereof, so as to solve the problem of insufficient decorative effect of the existing wall tiles during use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The wall brick of the present invention selects porous or non-porous volcanic stone as the body material, and the pore diameter of the porous volcanic stone is ≤ 1 mm (porous type is preferred). Cut the volcanic stone body into a green body according to the required size, and then use the following steps to make wall tiles with three-dimensional crystal effect:

[0020] (1) Applying a fineness of 350 mesh on the volcanic rock body, containing 28% of nafeldspar, 30% of quartz sand, 30% of frit, 2% of alumina, 4% of black talc, and 6% of kaolin, to form A biscuit body covered with a white base layer;

[0021] (2) The above-mentioned biscuit is heated in a roller kiln at a low temperature of 300-500°C for 10-35 minutes, at a medium temperature of 500-800°C for 10-35 minutes, and at a high temperature of 800-1200°C for 15-35 minutes, and then heated for 10 minutes. -15 minutes to cool down to 40-60°C;

[0022] (3) out of the oven to form a white green body covered with th...

Embodiment 2

[0029] The wall tile of the present invention comprises a bad body and a glaze body covering the surface of the green body. The upper surface of the glaze body is glass, and irregular cracks covering the entire glaze body appear on the glass at the junction with the glaze body.

[0030] The wall brick of the present invention selects porous volcanic rock with an aperture≤1mm as the body material to make the body, and then adopts the following process steps to make the wall brick with crystals of the present invention:

[0031] (1) The fineness of the volcanic stone body is 400 mesh, containing 28% of nafeldspar, 30% of quartz sand, 30% of frit, 2% of alumina, 4% of black talc, and 6% of kaolin to form A biscuit body covered with a white base layer;

[0032] (2) The above-mentioned biscuit is heated in a roller kiln at a low temperature of 300-500°C for 10-35 minutes, at a medium temperature of 500-800°C for 10-35 minutes, and at a high temperature of 800-1200°C for 15-35 minut...

Embodiment 3

[0041] The wall tile of the present invention comprises a bad body and a glaze body covering the surface of the green body. The upper surface of the glaze body is glass, and irregular crystals covering the entire glaze body appear on the glass at the junction with the glaze body.

[0042] The technology of processing wall brick of the present invention:

[0043] The wall brick of the present invention selects porous or non-porous volcanic stone as the body material, and the pore diameter of the porous volcanic stone is ≤ 1 mm (porous type is preferred). Cut the volcanic stone body into a green body according to the required size, and then use the following steps to make wall tiles with three-dimensional crystal effect:

[0044](1) Apply a mixture with a fineness of 300 meshes, 28% nafeldspar, 30% quartz sand, 30% frit, 2% alumina, 4% black talc and 6% kaolin on the volcanic rock body to form A biscuit body covered with a white base layer;

[0045] (2) The above-mentioned bis...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
pore sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a wall brick, comprising a blank, a glaze covered on the surface of the blank, wherein the upper surface of the glaze is glass which is provided with an irregular crystalline spread the entire glaze on the position connected with the glaze, and the invention also discloses a processing method of the wall brick of the invention. The processing method of the invention is producing a completed product as setting a white bottom layer- heating- arranging glass- heating or the like, wherein the glass is heated thereby changing the liner coefficient of dilatation and cooled down suddenly with the natural thickness, therefore forms the irregular crystalline spread the entire glaze on the position connected with the glaze and forms a decorative effect as a crystal, a frost flower, a diamond and a water droplet or the like, and the formed irregular crystalline can produce a multi-color effect with high stereo perception via the actions of reflection and refraction by natural light and artificial light source. The invention has the great decorative effect and can be used widely in high-grade decoration places.

Description

technical field [0001] The invention relates to a decorative material and a processing method thereof, in particular to a wall tile and a processing method thereof. Background technique [0002] At present, the existing ceramic wall tiles are made of body and glaze together. The production process generally goes through: raw material formula - added to ball mill for grinding - slurry to mixing tank - high pressure pump to drying tower - brick pressing Forming - firing. [0003] The existing ceramic wall tiles generally use opaque raw glaze. The shrinkage rate of the raw material used in the raw glaze and the raw material used in the green body is not much different after firing, so there is generally no crystal effect. The basic requirements of ceramic wall tiles; frit glaze is made of various commonly used glaze raw materials and then melted at a high temperature of about 1500 ℃. When in use, you only need to grind the raw glaze or fritted glaze into a glaze slurry, and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): E04F13/15C04B41/86C04B37/04
Inventor 邓学林
Owner 成都宏翁装饰材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap