Alkali-reducing processing promotor of polyester fiber fabric

An alkali weight reduction accelerator and polyester fiber technology, which can be used in fiber processing, textiles and papermaking, etc., can solve the problems of difficult control of polyester fiber alkali weight loss, poor uniformity, and large strength loss of polyester fiber fabrics. Promote uniform penetration, increase speed, and reduce weight to treat uniform effects

Inactive Publication Date: 2009-06-24
SUZHOU UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned common quaternary ammonium salt cationic surfactant has a very obvious promoting effect on the alkali weight reduction treatment of polyester fibers. The uniformity is poor, and the strength loss of polyester fiber fabric after weight reduction treatment is relatively large

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Alkali-reducing processing promotor of polyester fiber fabric
  • Alkali-reducing processing promotor of polyester fiber fabric
  • Alkali-reducing processing promotor of polyester fiber fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Alkali decrement accelerator formula is composed as follows by weight:

[0020] Polyoxyethylene-containing double quaternary ammonium salt cationic surfactant 30%

[0021] Nonionic Surfactant 8%

[0022] Water 62%

[0023] Preparation method: Dissolve the calculated amount of cationic surfactant and nonionic surfactant with a certain amount of water under heating conditions, then mix, stir evenly, and make up the remaining water.

[0024] The double quaternary ammonium salt cationic surfactant structure containing polyoxyethylene group used is:

[0025]

[0026] The structure of nonionic surfactants is:

[0027] CH 3 (CH 2 ) 11 O(CH 2 CH 2 O) 12 h

Embodiment 2

[0029] Alkali decrement accelerator formula is composed as follows by weight:

[0030] Polyoxyethylene-containing double quaternary ammonium salt cationic surfactant 35%

[0031] Nonionic Surfactant 5%

[0032] water 60%

[0033] Preparation method: Dissolve the calculated amount of cationic surfactant and nonionic surfactant with a certain amount of water under heating conditions, then mix, stir evenly, and make up the remaining water.

[0034] The double quaternary ammonium salt cationic surfactant structure containing polyoxyethylene group used is:

[0035]

[0036] The structure of nonionic surfactants is:

[0037] CH 3 (CH 2 ) 15 O(CH 2 CH 2 O) 15 h

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an accelerator for carrying out alkali weight reduction treatment on polyester fiber fabrics, which belongs to the technical field of textile dyeing and finishing. Its composition and mass percentage are: 20-40% of double quaternary ammonium salt cationic surfactant containing polyoxyethylene group, 2-10% of non-ionic surfactant, and the rest is water. Due to the use of double quaternary ammonium salt cationic surfactants containing polyoxyethylene groups, on the one hand, the speed of the hydrolysis reaction has been improved; The mildness of the active agent improves the uniformity of weight loss. At the same time, after compounding the double-linked quaternary ammonium salt cationic surfactant containing polyoxyethylene group and the fatty alcohol polyoxyethylene ether nonionic surfactant, a synergistic effect will be produced, which can better reduce the surface tension and promote the lye The uniform penetration can make the weight reduction treatment more uniform, and can improve the handle and surface properties of the treated fabric.

Description

technical field [0001] The invention relates to a textile finishing agent, in particular to an accelerator for carrying out alkali weight reduction treatment on polyester fiber fabrics, and belongs to the technical field of textile dyeing and finishing. Background technique [0002] In recent years, the synthetic fiber industry has developed rapidly, and polyester fiber (polyester) is widely used in various textiles as the synthetic fiber with the largest output. In terms of performance, untreated polyester fabrics have defects such as hard hand feeling and easy to produce aurora. In order to solve the above problems, polyester fabrics are often subjected to alkali reduction treatment in dyeing and finishing processing, which is generally called "simulation". Silk" finishing. Alkali reduction treatment is to put the polyester fiber fabric into a concentrated alkali solution to undergo a chemical reaction. The alkali hydrolyzes the ester bonds in the polyester fiber macromol...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/53D06M13/325D06M101/32
Inventor 王祥荣
Owner SUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com