Fibre-reinforced U-PVC foam material and its preparing process

A foamed material and fiber-reinforced technology, applied in the field of foamed materials and their preparation, can solve the problems of low strength, practical use restrictions, strong plastic texture, etc., and achieve the effect of expanding the scope of application

Inactive Publication Date: 2009-07-22
水浩 +1
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the inherent characteristics of U-PVC materials, such as large specificity (up to 1.47), too strong plastic texture, and weak shear force, many properties of wood cannot be achieved by this material.
In the past two years, U-PVC foaming materials and wood-plastic materials have been trial-produced, but these materials have defects such as too low strength and easy aging, and their actual use is greatly restricted and cannot replace wood.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A kind of preparation method of fiber-reinforced U-PVC hemp-plastic foamed floor, this method comprises: take 60 kilograms of PVC, 20 kilograms of flax fibers, 10 kilograms of calcium-zinc composite stabilizers, 5 kilograms of AC foaming agents, 5 kilograms of PE wax, in Fully mix in the mixing tank, then extrude at 100°C, cool the extrudate to shape, and then perform surface treatment to obtain the finished product.

Embodiment 2

[0033] A kind of preparation method of fiber-reinforced U-PVC hemp-plastic foamed floor: take 85 kilograms of PVC, 5 kilograms of flax, 2 kilograms of calcium-zinc composite stabilizer, 6 kilograms of AC foaming agent, ZB5302 kilograms, fully mix in the mixing tank, Then extrude at 200°C, cool the extruded product to shape, and then perform surface treatment to obtain the finished product.

Embodiment 3

[0035] A kind of preparation method of fiber-reinforced U-PVC hemp-plastic foamed floor: take 65 kilograms of PVC, 20 kilograms of flax, 5 kilograms of calcium-zinc composite stabilizer, 5 kilograms of AC foaming agent, 5 kilograms of stearic acid, in the mixing tank Mix thoroughly, then extrude at 140°C, cool the extruded product to shape, and then perform surface treatment to obtain the finished product.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a fiber-reinforced U-PVC foaming material and a preparation method thereof, which comprises 60-85% of PVC, 5-20% of flax, 2-10% of non-toxic composite stabilizer, 2-6% of foaming agent and lubricant 2-6%, fully mixed and reacted, then extruded at 100-200°C, cooled and shaped, and then surface treated to obtain the finished product. Compared with the prior art, the present invention has the advantages of light specific gravity, high strength, strong woody feeling, wear resistance, non-toxic and tasteless, non-oily, easy to clean, and aging resistance.

Description

technical field [0001] The invention relates to a foaming material and a preparation method thereof, in particular to a fiber-reinforced U-PVC foaming material and a preparation method thereof. Background technique [0002] Rigid-polyvinyl chloride (U-PVC) has made a major breakthrough in formula and technology after a generation of efforts, endowing the material with excellent performance and making it widely used in the field of building materials. However, due to the inherent characteristics of U-PVC materials, such as large specificity (up to 1.47), too strong plastic texture, and weak shear forces, many properties of wood cannot be achieved by this material. In the past two years, U-PVC foaming materials and wood-plastic materials have been trial-produced, but these materials have defects such as too low strength and easy aging, and their actual use is greatly restricted and cannot replace wood. Contents of the invention [0003] The object of the present invention i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08J5/04C08J9/00
CPCC08L33/08C08J2327/06C08K7/02C08J5/045C08L23/06C08L27/06C08L2666/04
Inventor 水浩张锡琪水清陈东博
Owner 水浩
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products